Cable support frame

A cable support frame and support part technology, applied in the support frame field, can solve the problems to be improved, and achieve the effects of good insulation and wear resistance, uniform organization, and improved strength

Inactive Publication Date: 2016-06-22
唐岁寒
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its strength, wear resistance, insulation and corrosion resistance all need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cable support frame

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A cable support frame, the cable support frame is composed of a foot support (1) and a support part (2), and the two parts are integrally formed, it is characterized in that the manufacturing cable support frame includes the following steps:

[0036] The content of each element component of the cable support frame is: Ni10%, C10%, Nb5%, V2%, Si0.8%, Ba0.4%, Ce0.1%, B0.05%, Cd0.04%, and the balance is W

[0037] The powder composed of the above elements is ball milled, and then pressed to obtain a blank;

[0038] The blank is placed in a sintering furnace, and the first sintering is carried out at a sintering temperature of 1550°C, a heating rate of 35°C / min, and a holding time of 2 hours, and then cooled with the furnace to obtain a pre-sintered blank;

[0039] Homogenize the pre-sintered billet at 900°C for a holding time of 6 hours, then cool down to 700°C for a holding time of 3 hours and cool with the furnace;

[0040] Afterwards, the billet is placed in a sinteri...

Embodiment 2

[0045] A cable support frame, the cable support frame is composed of a foot support (1) and a support part (2), and the two parts are integrally formed, it is characterized in that the manufacturing cable support frame includes the following steps:

[0046] The content of each element component of the cable support frame is: Ni11%, C15%, Nb6%, V3%, Si0.9%, Ba0.5%, Ce0.2%, B0.06%, Cd0.05%, and the balance is W

[0047] The powder composed of the above elements is ball milled, and then pressed to obtain a blank;

[0048] The billet is placed in a sintering furnace, and the first sintering is carried out at a sintering temperature of 1560°C, a heating rate of 35°C / min, and a holding time of 3 hours, and then cooled with the furnace to obtain a pre-sintered billet;

[0049] Homogenize the pre-sintered billet at 910°C for 6 hours, then cool down to 700°C for 3 hours and cool with the furnace;

[0050] Afterwards, the billet is placed in a sintering furnace, and the second sinteri...

Embodiment 3

[0055] A cable support frame, the cable support frame is composed of a foot support (1) and a support part (2), and the two parts are integrally formed, it is characterized in that the manufacturing cable support frame includes the following steps:

[0056] The content of each element component of the cable support frame is: Ni10.5%, C13%, Nb5.5%, V2.5%, Si0.85%, Ba0.45%, Ce0.15%, B0.055%, Cd0. 045%, the balance is W

[0057] The powder composed of the above elements is ball milled, and then pressed to obtain a blank;

[0058] The billet is placed in a sintering furnace, and the first sintering is carried out at a sintering temperature of 1555°C, a heating rate of 35°C / min, and a holding time of 2.5 hours, and then cooled with the furnace to obtain a pre-sintered billet;

[0059] Homogenize the pre-sintered billet at 905°C for a holding time of 6 hours, then cool down to 700°C for a holding time of 3 hours and cool with the furnace;

[0060] Afterwards, the billet is placed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cable support frame. The cable support frame is composed of a foot bracket (1) and a support part (2), wherein the two parts are integrally formed. The cable support frame disclosed by the invention adopts a tungsten-based material, and the tungsten-based material ensures the strength requirement of the support frame; and a multi-stage sintering process is adopted, thus the strength of the material is enhanced, and the structure of the tungsten-based material can be uniform.

Description

technical field [0001] The invention relates to a cable support frame and belongs to the technical field of support frames. Background technique [0002] Cables are commonly used tools in engineering operations. When cables are not needed, they are usually placed on cable racks for collection. A traditional cable rack includes two brackets and a cross bar installed between the two brackets, and the cables are placed on the cross bar. And its strength, wear resistance, insulation, corrosion resistance all need to be improved. Contents of the invention [0003] A cable support frame, the cable support frame is composed of a foot support (1) and a support part (2), and the two parts are integrally formed, it is characterized in that the manufacturing cable support frame includes the following steps: [0004] The content of each element component of the cable support frame is: Ni10-11%, C10-15%, Nb5-6%, V2-3%, Si0.8-0.9%, Ba0.4-0.5%, Ce0.1-0.2% , B0.05-0.06%, Cd0.04-0.05%, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C27/04C22C1/05C23C8/36C23C24/10B22F3/10B22F3/24B22F5/00C09D1/06B65D61/00
CPCC22C27/04B22F3/1017B22F3/24B22F5/00B22F2998/10B65D61/00C09D1/06C22C1/05C23C8/36C23C24/103B22F1/0003B22F3/02B22F2003/241
Inventor 唐岁寒
Owner 唐岁寒