High-strength low-resistivity high-voltage transmission power cable

A low-resistivity, high-voltage power transmission technology, applied to power cables with shielding layers/conductive layers, insulated cables, cables, etc., can solve problems such as difficult to find breakpoints, solve the problem of long-term large-scale power outages, and improve hardness , The effect of resistivity reduction

Inactive Publication Date: 2016-07-13
谢春梅
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Second, once there is an open circuit problem in the power cable, it is very difficult to find the open circuit point, which will lead to long-term and large-scale power outages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength low-resistivity high-voltage transmission power cable
  • High-strength low-resistivity high-voltage transmission power cable
  • High-strength low-resistivity high-voltage transmission power cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1: High-strength low-resistivity high-voltage transmission power cable, including 3 conductors, a conductor shielding layer, an insulating layer, and a protective layer; the conductor shielding layer is arranged on the outside of the conductor, and the insulating layer is arranged on the outside of the conductor shielding layer. The conductor is arranged in the protective layer; it also includes a cylindrical fixing device, and the cylindrical fixing device is located in the protective layer; the side of the cylindrical fixing device is provided with three arc-shaped grooves at equal intervals; the three conductors They are respectively located in the arc-shaped groove; the cavity formed between the conductor, the cylindrical fixing device and the protective layer is filled with an insulating filler; it also includes a remote breakpoint detection unit and 6 terminal breakpoint detection units; the said The 6 terminal breakpoint detection units are equidistantl...

Embodiment 2

[0060] On the basis of Embodiment 1, the first switch, the second switch, and the third switch all use controllable thyristors.

[0061] Wherein, the conductor is made of aluminum alloy material, and the weight ratio of the aluminum alloy material is as follows: aluminum: 1000 parts; neodymium: 0.6 parts; boron: 4 parts; iron: 1 part; copper: 1.5 parts; : 1.5 parts; magnesium: 2.5 parts; zinc: 0.5 parts; lanthanum: 0.01 parts;

[0062] The first step: After preparing the aluminum alloy raw materials according to the above weight parts, firstly, the melting temperature is 730°C, after stirring, refining, and slag removal, the continuous casting machine is used to continuously cast aluminum alloy ingots of Φ120 mm, and then through Rapidly drop to 430°C in 6-8 seconds;

[0063] Step 2: Use an extruder to hot-extrude at 430°C to make a Φ30mm aluminum alloy rod;

[0064] Step 3: keep warm in an inert gas for 1 hour, then cool down to 300°C;

[0065] The fourth step: using a wir...

Embodiment 3

[0067] Others are exactly the same as in Example 1, wherein the conductor is made of an aluminum alloy material, and the weight ratio of the aluminum alloy material is as follows:

[0068] Aluminum: 1000 parts; Neodymium: 0.7 parts; Boron: 5 parts; Iron: 1 part; Copper: 1.5 parts; Silicon: 1.5 parts; Magnesium: 2.5 parts; Zinc: 0.5 parts; Lanthanum: 0.01 parts;

[0069] The first step: After preparing the aluminum alloy raw materials according to the above weight parts, firstly, the melting temperature is 730°C, after stirring, refining, and slag removal, the continuous casting machine is used to continuously cast aluminum alloy ingots of Φ120 mm, and then through Rapidly drop to 430°C in 6-8 seconds;

[0070] Step 2: Use an extruder to hot-extrude at 430°C to make a Φ30mm aluminum alloy rod;

[0071] Step 3: keep warm in an inert gas for 1 hour, then cool down to 300°C;

[0072] The fourth step: using a wire drawing machine to draw 6-8 times to prepare a Φ4mm aluminum alloy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength low-resistivity high-voltage transmission power cable, which comprises three conductors, conductor shielding layers, an insulated layer, a protection layer, a cylindrical fixing device, a remote breakpoint detection unit and N terminal breakpoint detection units, wherein the conductor shielding layers are arranged outside the conductors; the insulated layers are arranged outside the conductor shielding layers; the three conductors are arranged in the protection layer; the cylindrical fixing device is located in the protection layer; the side surface of the cylindrical fixing device is provided with three arc-shaped grooves at equal intervals; the three conductors are respectively located in the arc-shaped grooves; the cavity formed between the conductors, the cylindrical fixing device and the protection layer is filled with an insulated filler; and the N terminal breakpoint detection units are arranged on the high-strength low-resistivity high-voltage transmission power cable line at equal intervals. The problem of short circuit caused by friction does not happen, the breakpoint can be quickly judged once the broken circuit problem happens to the power cable, and the wire core has high strength and low resistivity.

Description

[0001] This application is a divisional application of a patent application with an application date of 2014-10-15, an application number of 201410544511.X, and an invention name of a high-strength low-resistivity high-voltage transmission power cable. technical field [0002] The invention relates to the technical field of high-voltage power transmission, in particular to a high-strength low-resistivity high-voltage power transmission power cable. Background technique [0003] With the rapid development of the national economy, the amount and scope of use of power cables as the main artery of the national economy are increasing. Power cables are cables used to transmit and distribute electrical energy. It is often used in urban underground power grids, outgoing lines of power stations, internal power supply of industrial and mining enterprises, and underwater transmission lines across rivers and seas. In power lines, the proportion of power cables is gradually increasing. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B7/32H01B7/18H01B9/02H01B1/02G01R31/08
CPCH01B7/1805G01R31/083H01B1/023H01B7/32H01B9/02
Inventor 谢春梅
Owner 谢春梅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com