Mirror finishing technology for shell of beard clipper

A mirror processing and shaver technology, applied in the field of polishing, can solve the problems of difficult mirror polishing of the shaver shell, small metal loss, and low error rate, and achieve various shell styles and mirror effects, small metal loss, and low error rate. low rate effect

Active Publication Date: 2016-07-20
GUANGDONG ROMAN TECH CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a shaver shell mirror surface processing technology with short time, low metal loss and low error rate for the traditional polishing process, which is difficult to realize the mirror surface polishing of the shaver shell, so as to solve the problem of the existing shaver assembly mirror Issues of insecurity and low usability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A process for processing the mirror surface of a razor shell. The following operations are performed on the metal layer to be processed: (1) Cleaning: soak the metal layer to be processed in an alkaline solution for ultrasonic cleaning for 5 minutes, and then clean it with water; (2) water Sandblasting and polishing: use quartz sand polishing liquid to perform water sandblasting and polishing on the metal layer to be processed for 45 seconds, and then wash it with water. The quartz sand polishing liquid includes quartz sand, and the particle size of the quartz sand is 3000 mesh; ( 3) Grinding and fine polishing: use a fine polishing liquid to perform polishing pad grinding and fine polishing on the metal layer to be processed for 5 minutes. The fine polishing liquid includes abrasive components, and the abrasive components are white corundum and cubic silicon nitride micropowder. The particle size of the abrasive component was 9000 mesh.

[0038] Wherein, the quartz san...

Embodiment 2

[0052] A process for processing the mirror surface of a razor shell. The following operations are performed on the metal layer to be processed: (1) cleaning: soak the metal layer to be processed in an alkaline solution for ultrasonic cleaning, and then clean it with water; (2) water spray Sand polishing: use quartz sand polishing liquid to perform water sandblasting and polishing on the metal layer to be processed, and then clean it with water. The quartz sand polishing liquid includes quartz sand, and the particle size of the quartz sand is 1000 mesh. The polishing time for polishing is 45s, the sandblasting pressure is 0.2Mpa, and the angle between the jet stream and the metal layer to be processed is 35°; (3) Grinding and fine polishing: use fine polishing liquid to perform polishing pad grinding on the metal layer to be processed Fine polishing, the fine polishing liquid includes abrasive components, the abrasive components are white corundum, the particle size of the abras...

Embodiment 3

[0064] A process for processing the mirror surface of a razor shell. The following operations are performed on the metal layer to be processed: (1) cleaning: soak the metal layer to be processed in an alkaline solution for ultrasonic cleaning, and then clean it with water; (2) water spray Sand polishing: use quartz sand polishing liquid to perform water sandblasting and polishing on the metal layer to be processed, and then clean it with water. The quartz sand polishing liquid includes quartz sand, and the particle size of the quartz sand is 5000 mesh. The polishing time is 30s, the sandblasting pressure is 0.1Mpa, and the angle between the jet stream and the metal layer to be processed is 15°; (3) Grinding and fine polishing: use fine polishing liquid to perform polishing pad grinding on the metal layer to be processed Fine polishing, the fine polishing liquid includes abrasive components, the abrasive components are cubic silicon nitride micropowders, the particle size of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of polishing, in particular to a mirror finishing technology for a shell of a beard clipper. The mirror finishing technology comprises following steps of (1) cleaning, wherein a metal layer to be machined is soaked into an alkaline solution to be subject to ultrasonic cleaning for 10 min to 30 min, and then is cleaned through clean water; (2), water sandblasting polishing, wherein quartz sand polishing liquid is used for carrying out water sandblasting polishing treatment on the metal layer to be machined, and then cleanwater is used for cleaning the metal layer, the quartz sand polishing liquid comprises quartz sand, and the granularity of the quartz sand ranges from 1000 meshes to 5000 meshes; and (3), grinding and finishing polish, wherein finishing polish liquid is used for carrying out polishing pad grinding and finishing polish on the metal layer to be machined, and the finishing polish liquid comprises abrasive ingredients. The mirror finishing technology is short in time, small in metal loss and low in error rate; and time of the whole working procedure is controlled within one hour, through secondary physical polishing, the metal layer to be machined reaches the mirror finishing effect, and the roughness is below 0.8 micrometer.

Description

technical field [0001] The invention relates to the technical field of polishing, in particular to a process for processing the mirror surface of a shaver shell. Background technique [0002] In the prior art, it is very necessary for the shaver to be used with a mirror as a grooming tool. There are also some manufacturers in the market producing shaver shells equipped with mirrors, but the mirror is a fragile item, and the shaver As a tool that needs to be moved frequently, it is very easy to fall and cause the mirror to break, which is easy to hurt the human body, and the razor after the mirror is broken will not continue to be used due to safety hazards, which greatly reduces the life of the product. cycle. [0003] Therefore, there is an urgent need for a polishing process to achieve the mirror effect of the metal layer on the shaver shell, and to solve the safety and practical problems of traditional razors equipped with mirrors. The steps of the traditional polishing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24C1/08B24C11/00B24B1/00B24B37/00C09G1/02C23F3/00C25F3/16
CPCB24B1/00B24B37/00B24C1/083B24C1/086B24C11/00C09G1/02C23F3/00C25F3/16
Inventor 严佑春
Owner GUANGDONG ROMAN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com