Anti-aging agent NBC coated with nanomaterial and preparation method of anti-aging agent NBC
A nanomaterial and anti-aging agent technology, applied in the field of anti-aging agent NBC and its preparation, can solve problems such as low product utilization rate, and achieve the effects of reducing dosage, convenient use and cost reduction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Anti-aging agent NBC is made from the following raw materials by weight: 53 parts of anti-aging agent NBC, 38 parts of calcium terephthalate, sulfur-containing silane coupling agent bis-[3-(triethoxysilicon)-propyl]-tetra 1 part of sulfide.
[0022] Preparation steps: first, add 38 parts of calcium terephthalate into the reactor; add 53 parts of anti-aging agent NBC to the reactor after crushing and grinding, mix and stir with calcium terephthalate, and control the temperature at 50 degrees; anti-aging After mixing and stirring NBC and calcium terephthalate for 1 hour, add 1 part of sulfur-containing silane coupling agent bis-[3-(triethoxysilyl)-propyl]-tetrasulfide, mix and stir, and finally form The anti-aging agent NBC is fully coated with nanomaterials, and the total reaction time is 2:20.
[0023] The anti-aging agent NBC obtained in this example can completely coat nanomaterials, which ensures the application effect of this product in rubber.
Embodiment 2
[0025] Anti-aging agent NBC is made from the following raw materials by weight: 60 parts of anti-aging agent NBC, 46 parts of calcium terephthalate, and 2 parts of alkyl silane coupling agent tetraethyl silicate.
[0026] Preparation steps: first, add 46 parts of calcium terephthalate into the reactor; add 60 parts of anti-aging agent NBC to the reactor after crushing and grinding, mix and stir with calcium terephthalate, and control the temperature at 60 degrees; anti-aging Agent NBC and calcium terephthalate were mixed and stirred for 1 hour, 2 parts of alkyl silane coupling agent tetraethyl silicate were added, mixed and stirred, and finally a product of anti-aging agent NBC fully coated with nanomaterials was formed, and the total reaction time was 1 40 minutes.
[0027] The anti-aging agent NBC obtained in this example can completely coat nanomaterials, which ensures the application effect of this product in rubber.
Embodiment 3
[0029] Anti-aging agent NBC is prepared from the following raw materials by weight: 55 parts of anti-aging agent NBC, 43 parts of calcium terephthalate, and 2 parts of alkylsilane coupling agent 1,2-bis(triethoxysilyl)ethane.
[0030] Preparation steps: first, add 43 parts of calcium terephthalate into the reactor; add 55 parts of anti-aging agent NBC into the reactor after crushing and grinding, mix and stir with calcium terephthalate, and control the temperature at 58 degrees; After mixing and stirring NBC and calcium terephthalate for 1 hour, add 2 parts of alkylsilane coupling agent 1,2-bis(triethoxysilyl)ethane, mix and stir, and finally form an all-inclusive antioxidant NBC For products coated with nanomaterials, the total reaction time is 1:45.
[0031] The anti-aging agent NBC obtained in this example can completely coat nanomaterials, which ensures the application effect of this product in rubber.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap