Environment-friendly chemical fiber board and preparation method thereof

A kind of chemical fiber board, an environment-friendly technology, applied in the field of construction, can solve the problems of large amount of clothes being eliminated and affecting the quality of the environment, and achieve the effect of alleviating adverse effects, alleviating the lack of forest resources, and alleviating the contradictions of destroying the natural environment

Inactive Publication Date: 2016-07-20
脱德明
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, with the improvement of social living standards, people's clothing is changed frequently, and a large amount of clothing is eliminated, forming a large amount of clothing garbage. Since there is no ideal clothing garbage recycling technology at present, it exists in the environment and becomes an environmental impact. one of the factors of quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An environment-friendly chemical fiber board, which is composed of the following ingredients in parts by weight: 24 parts of waste chemical fiber clothing, 41 parts of calcium carbonate, 95 parts of PVC resin, 0.2 parts of polyethylene wax, 6 parts of stabilizer, 1 part of AC foaming agent, water 0.4 parts of talc, 2 parts of silicon dioxide, 0.3 parts of polyvinyl acetate emulsion, and 0.1 part of oxidized starch.

[0019] The preparation method of described environment-friendly chemical fiber board comprises the following steps:

[0020] ⑴Remove other sundries from waste chemical fiber clothing raw materials and process them into an area of ​​0.09cm 2 debris;

[0021] (2) Take waste chemical fiber clothing fragments, calcium carbonate, PVC resin, polyethylene wax, stabilizer, AC foaming agent, hydrotalcite, silicon dioxide, polyvinyl acetate emulsion, and oxidized starch by weight and add them to the mixer and stir until they are evenly mixed ;

[0022] (3) Place t...

Embodiment 2

[0024] An environment-friendly chemical fiber board, which is composed of the following ingredients in parts by weight: 33 parts of waste chemical fiber clothing, 65 parts of calcium carbonate, 52 parts of PVC resin, 0.5 parts of polyethylene wax, 9 parts of stabilizer, 1.2 parts of AC foaming agent, water 1.2 parts of talc, 4 parts of silicon dioxide, 0.6 parts of polyvinyl acetate emulsion, and 0.3 parts of oxidized starch.

[0025] The preparation method of the environment-friendly chemical fiber board in this implementation is the same as that in Example 1.

Embodiment 3

[0027] An environment-friendly chemical fiber board, which is composed of the following ingredients in parts by weight: 28 parts of waste chemical fiber clothing, 55 parts of calcium carbonate, 76 parts of PVC resin, 0.35 parts of polyethylene wax, 7.5 parts of stabilizer, 1.1 parts of AC foaming agent, water 0.8 parts of talc, 3 parts of silicon dioxide, 0.45 parts of polyvinyl acetate emulsion, and 0.2 parts of oxidized starch.

[0028] The preparation method of the environment-friendly chemical fiber board in this implementation is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly chemical fiber board, which is composed of the following components in parts by weight: 24 to 33 parts of waste and old chemical fiber clothes, 41 to 65 parts of calcium carbonate, 52 to 95 parts of PVC resin, 0.2 to 0.5 part of polyethylene wax, 6 to 9 parts of stabilizer, 1 to 1.2 parts of AC foaming agent, 0.4 to 1.2 parts of hydrotalcite, 2 to 4 parts of silicon dioxide, 0.3 to 0.6 part of polyvinyl acetate emulsion, and 0.1 to 0.3 part of oxidized starch. The chemical fiber board is used for architectural decoration and finishing. The provided chemical fiber board can relieve the burden on wood resources and also reduce the pollution caused by waste clothes to the environment.

Description

technical field [0001] The invention belongs to the technical field of construction, and in particular relates to an environment-friendly chemical fiber board and a preparation method thereof. Background technique [0002] Existing organic boards used for interior decoration of buildings include wood profile boards, multi-layer plywood, glued blockboards, and pressurized fiberboards. Although the aforementioned boards are structurally different, the raw materials all come from trees. Due to the lack of forest resources and the gradual strengthening of social environmental protection awareness, there is a sharp contradiction between the increasing demand and the sharply reduced raw materials. In addition, with the improvement of social living standards, people's clothing is changed frequently, and a large amount of clothing is eliminated, forming a large amount of clothing garbage. Since there is no ideal clothing garbage recycling technology at present, it exists in the env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L3/10C08L101/00C08K13/02C08K3/26C08K3/36C08J9/10
Inventor 脱德明
Owner 脱德明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com