A kind of y2si2o7 whisker and preparation method thereof

The technology of whisker and yttrium silicate is applied in the field of Y2Si2O7 whisker and its preparation, and achieves the effects of improving diffusion rate, easy control, and facilitating the elimination of impurities

Active Publication Date: 2018-04-17
SHAANXI UNIV OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, Y 2 Si 2 o 7 Preparation of whiskers is rarely reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of y2si2o7 whisker and preparation method thereof
  • A kind of y2si2o7 whisker and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] a Y 2 Si 2 o 7 The preparation method of whisker, comprises the following steps:

[0030] (1) Weigh analytically pure Y(NO) 3 ·6H 2 O in a beaker, in a fume hood as Y(NO) 3 ·6H 2 The molar ratio of O:TEOS=1:1 measures certain TEOS, stirs 30min to obtain the mixed solution of the two, then adds a certain amount of dehydrated alcohol, is mixed with the solution that concentration is 0.5mol / L, heats and stirs evenly, obtains Transparent yttrium silicate precursor mixture.

[0031] (2) Place the obtained yttrium silicate precursor mixture in a polytetrafluoroethylene-lined hydrothermal kettle, control the filling ratio to 30%, then put the reaction kettle into an oven, control the temperature at 100°C, and react for 12 hours . A wet gel of yttrium silicate was obtained.

[0032] (3) The obtained yttrium silicate wet gel was dried at 100°C, and then heat-treated in a muffle furnace at 350°C for 60 minutes to obtain yttrium silicate dry gel powder.

[0033] (4) Mix ...

Embodiment 2

[0036] a Y 2 Si 2 o 7 The preparation method of whisker, comprises the following steps:

[0037] (1) Weigh analytically pure Y(NO) 3 ·6H 2 O in a beaker, in a fume hood as Y(NO) 3 ·6H 2 The molar ratio of O:TEOS=1:1 measures certain TEOS, stirs 60min to obtain the mixed solution of the two, then adds a certain amount of dehydrated alcohol, is mixed with the solution that concentration is 0.75mol / L, heats and stirs evenly, obtains Transparent yttrium silicate precursor mixture.

[0038] (2) Place the obtained yttrium silicate precursor mixture in a polytetrafluoroethylene-lined hydrothermal kettle, control the filling ratio to 50%, then put the reaction kettle into an oven, control the temperature at 110°C, and react for 24h . A wet gel of yttrium silicate was obtained.

[0039] (3) The obtained yttrium silicate wet gel was dried at 80°C, and then heat-treated in a muffle furnace at 500°C for 30 minutes to obtain yttrium silicate dry gel powder.

[0040] (4) Mix the o...

Embodiment 3

[0043] a Y 2 Si 2 o 7 The preparation method of whisker, comprises the following steps:

[0044] (1) Weigh analytically pure Y(NO) 3 ·6H 2 O in a beaker, in a fume hood as Y(NO) 3 ·6H 2 O: TEOS = 1: 1 molar ratio Take a certain amount of TEOS, stir for 50 minutes to get a mixture of the two, then add a certain amount of absolute ethanol to prepare a solution with a concentration of 1mol / L, heat and stir evenly to obtain a transparent yttrium silicate precursor mixture.

[0045] (2) Place the obtained yttrium silicate precursor mixture in a polytetrafluoroethylene-lined hydrothermal kettle, control the filling ratio to 60%, then put the reaction kettle into an oven, control the temperature at 120°C, and react for 24h . A wet gel of yttrium silicate was obtained.

[0046] (3) The obtained yttrium silicate wet gel was dried at 90°C, and then heat-treated in a muffle furnace at 400°C for 50 minutes to obtain yttrium silicate dry gel powder.

[0047] (4) Mix the obtained ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of Y2Si2O7 crystal whiskers, and belongs to the technical field of ceramic material preparation.The preparation method comprises the following steps that 1, Y(NO)3.6H2O and TEOS are taken and then stirred to be uniform, absolute ethyl alcohol is added, the materials are stirred to be uniform under the heating condition, and transparent yttrium silicate precursor mixed liquid is prepared; 2, the transparent yttrium silicate precursor mixed liquid reacts for 12-24 h at the temperature of 80 DEG C-120 DEG C, and wet yttrium silicate gel is prepared; 3, the wet yttrium silicate gel is dried and then subjected to heat treatment at the temperature of 300 DEG C-500 DEG C, and dry yttrium silicate gel powder is prepared; 4, the dry yttrium silicate gel powder and mixed complex salts are mixed to be uniform according to the ratio of 1:(1-3) and then subjected to heat treatment, wherein the mixed complex salts are formed by mixing sodium molybdate with sodium sulfate according to the mass ratio of 1:1; 5, products obtained through treatment in the step 4 are sequentially subjected to washing and acid pickling and then dried, and the Y2Si2O7 crystal whiskers are prepared.The method is simple in preparation technology and short in reaction period; the Y2Si2O7 crystal whiskers prepared through the method are controllable in morphology, uniform in crystal whisker size distribution and appropriate in length-diameter ratio.

Description

technical field [0001] The invention belongs to the technical field of preparation of ceramic materials, in particular to a Y 2 Si 2 o 7 Whiskers and methods for their preparation. Background technique [0002] Y 2 Si 2 o 7 Also known as yttrium disilicate, belongs to monoclinic p2 1 / m space group structure, formed in space by [YO 6 ] The vertices of the octahedron are connected into a two-dimensional network structure, and the layers of the network structure and the interlayer gaps are separated by [Si 2 o 7 ] 6- Double tetrahedral filling [Julien Parmentier, Philippe Bodart R. Phase transformations in Gel-derived and mixed-powder-derived yttrium disilicate, Y 2 Si 2 o 7 by X-ray diffraction and 29SiMAS NMR [J]. Journal of Solid State Chemistry, 2000, 149: 16220.]. Y 2 Si 2 o 7 Crystalline phases include α-Y 2 Si 2 o 7 , β-Y 2 Si 2 o 7 , γ-Y 2 Si 2 o 7 and δ-Y 2 Si 2 o 7 (stable above 1535°C) and other crystal forms (sorted from low-temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B29/34C30B29/62C30B25/00
CPCC30B25/005C30B29/34C30B29/62
Inventor 黄剑锋周磊雍翔曹丽云欧阳海波陈意声李翠艳李春光
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com