Manufacturing method of winter shirt fabric

A fabric and shirt technology, applied in the field of winter shirt fabric preparation, can solve the problems of destroying the wearer's temperament and demeanor, bloated appearance, etc., and achieve the effects of good thermal insulation performance, good drapability, and good antibacterial performance

Active Publication Date: 2016-09-28
徐州荣盛纺织整理有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Shirts can be worn alone or inside to match suits, jackets, etc. Because shirts are relatively thin, it is necessary to add clothes inside the shirt or suit to keep warm when the temperature is low, but it will appear bloated in appearance. A kind of down shirt, in which a layer of down-filled liner is sewn inside the shirt to reduce the number of pieces of clothing and at the same time achieve the effect of keeping warm. However, down shirts still look thick to young people no

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of winter shirt fabric
  • Manufacturing method of winter shirt fabric

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] A method for preparing winter shirt fabrics is carried out according to the following steps:

[0031] A. After dispersing the kapok fiber, it is placed in the prepared environmental protection treatment solution and immersed for 2.5 hours, then washed with water and dried at 45°C;

[0032] B. Blend the treated kapok fiber and polyester fiber to obtain a polyester blended yarn;

[0033] C. Weaving the blended yarn to obtain a blended blank, which is then printed, post-set and dried to obtain a winter shirt fabric.

[0034] The environmental protection treatment liquid of kapok fiber includes the following components by weight percentage:

[0035] Food grade glycerin 4%

[0036] Olive oil 2%

[0037] Vegetable dye 5%

[0038] Paper mulberry juice 0.7%

[0039] Guar gum 10%

[0040] Safflower Seed Extract 2%

[0041] The balance of deionized water.

[0042] The polyester fiber is dyed with vegetable dyes in the fiber preparation stage.

[0043] The weight percentages of po...

Example Embodiment

[0044] Example 2

[0045] A method for preparing winter shirt fabrics is carried out according to the following steps:

[0046] A. After dispersing the kapok fiber, place it in the prepared environmental protection treatment solution and immerse it for 2h, then wash it with water and dry it at 50℃;

[0047] B. Blend the treated kapok fiber and polyester fiber to obtain a polyester blended yarn;

[0048] C. Weaving the blended yarn to obtain a blended blank, which is then printed, post-set and dried to obtain a winter shirt fabric.

[0049] The environmental protection treatment liquid of kapok fiber includes the following components by weight percentage:

[0050] Food grade glycerin 3%

[0051] Olive oil 3%

[0052] Vegetable dye 2%

[0053] Paper mulberry juice 0.8%

[0054] Guar Gum 8%

[0055] Safflower Seed Extract 1%

[0056] The balance of deionized water.

[0057] The polyester fiber is dyed with vegetable dyes in the fiber preparation stage.

[0058] The weight percentages of polyester f...

Example Embodiment

[0059] Example 3

[0060] A method for preparing winter shirt fabrics is carried out according to the following steps:

[0061] A. After dispersing the kapok fiber, place it in the prepared environmental protection treatment solution and immerse it for 3 hours, then wash it with water and dry it at 40°C;

[0062] B. Blend the treated kapok fiber and polyester fiber to obtain a polyester blended yarn;

[0063] C. Weaving the blended yarn to obtain a blended blank, which is then printed, post-set and dried to obtain a winter shirt fabric.

[0064] The environmental protection treatment liquid of kapok fiber includes the following components by weight percentage:

[0065] Food grade glycerin 5%

[0066] Olive oil 1%

[0067] Vegetable dye 2%

[0068] Paper mulberry juice 0.6%

[0069] Guar gum 12%

[0070] Water Saffron Seed Extract 1.5%

[0071] The balance of deionized water.

[0072] The polyester fiber is dyed with vegetable dyes in the fiber preparation stage.

[0073] The weight percentages o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a manufacturing method of winter shirt fabric. Polyester fiber and kapok fiber are blended to achieve excellent heat-preserving and antibacterial effect and excellent drapability, the kapok fiber is processed in an environment-friendly mode, so that the kapok fiber is high in heat-preserving property, no chemical agents are needed except a food-grade glycerol and the method is a novel environment-friendly fiber preparing method.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a preparation method for winter shirt fabrics. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort of polyester fibers and increase the added value...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P1/34D06P1/651D06P1/46D06P1/48D06P1/44D06P3/60D02G3/04
CPCD02G3/04D06P1/34D06P1/44D06P1/46D06P1/48D06P1/65118D06P3/60D10B2201/01D10B2331/04
Inventor 包新姐
Owner 徐州荣盛纺织整理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka