Making method of graphene-containing breast-conditioning health care bra

A production method and graphene technology, applied in bras, bras, phototherapy, etc., can solve the problems of not being easy to dry, increase the burden on the human body, and the weight of sponges, and achieve easy cleaning and drying, avoid fat outflow, and short preparation cycle Effect

Inactive Publication Date: 2016-10-12
广州美乔新材料科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Sponge is made of polyurethane or polyvinyl alcohol foam, which has the following disadvantages: first, the sponge is relatively heavy, which increases the total amount of the sponge and increases the load on the human body; second, the air permeability is poor, so that the skin cannot breathe normally
In addition, although the use of steel rings can make the bra appear stiff and concentrated, the wearing comfort and softness of the bra are greatly reduced.
[0004] The disadvantages of the existing traditional bra technology are: uncomfortable, airtight, easy to hide dirt, difficult to dry, easy to mold in humid weather, steel rings are easy to compress the breasts, resulting in poor blood circulation, or because of comfort but can not lift breasts , or only the chest function has no health care function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Making method of graphene-containing breast-conditioning health care bra
  • Making method of graphene-containing breast-conditioning health care bra
  • Making method of graphene-containing breast-conditioning health care bra

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment one: a kind of manufacturing method of the breast conditioning health-care bra containing graphene comprises the following steps:

[0024] a. add 2.5 parts by weight graphene and 92.5 parts by weight hot-melt silica gel in the warm water of 5 parts by weight at 50 degrees and mix evenly to make graphene glue;

[0025] b. Evenly print the graphene glue mixed in a on the Sanmingye fabric according to the template, repeat the printing 5 times, each time at an interval of 5 minutes, and leave it at room temperature for 4 hours to dry before use;

[0026] c. Bond the dried material in b with the superelastic nonwoven fabric with adhesive glue;

[0027] d. Place the bonded material in c at a temperature below 190°C for cold-pressing and pressing, and repeat the cold-pressing and pressing process for 2 times, each time for 2 minutes;

[0028] e. Trim the material processed by the die in d to make a cup;

[0029] f. Sew the cups made in e together with traditional ...

Embodiment 2

[0031] Embodiment two: a kind of manufacturing method of the breast conditioning health-care bra containing graphene comprises the following steps:

[0032] a. add 2.5 parts by weight graphene and 92.5 parts by weight hot-melt silica gel in the warm water of 5 parts by weight at 50 degrees and mix evenly to make graphene glue;

[0033] b. Evenly print the graphene glue mixed in a on the Sanmingye fabric according to the template, repeat the printing 8 times, each interval is 5 minutes, and leave it at room temperature for 4 hours to dry before use;

[0034] c. Bond the dried material in b with the superelastic nonwoven fabric with adhesive glue;

[0035] d. Place the bonded material in c at a temperature below 190°C for cold-pressing and pressing, and repeat the cold-pressing and pressing process for 2 times, each time for 2 minutes;

[0036] e. Trim the material processed by the die in d to make a cup;

[0037] f. Sew the cups made in e together with traditional parts such ...

Embodiment 3

[0040] Embodiment three: a kind of manufacturing method of the breast conditioning health-care bra containing graphene comprises the following steps:

[0041] a. add 2.5 parts by weight graphene and 85 parts by weight hot-melt silica gel in the warm water of 10 parts by weight at 50 degrees and mix evenly to make graphene glue;

[0042] b. Evenly print the graphene glue mixed in a on the Sanmingye fabric according to the template, repeat the printing 10 times, with an interval of 5 minutes each time, and leave it at room temperature for 4 hours to dry before use;

[0043] c. Bond the dried material in b with the superelastic nonwoven fabric with adhesive glue;

[0044] d. Position the laminated material in c below 190°C for cold pressing and compression molding, and repeat the cold pressing and compression molding treatment for 3 times, each time for 2 minutes;

[0045] e. Trim the material processed by the die in d to make a cup;

[0046] f. Sew the cups made in e together wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A making method of a graphene-containing breast-conditioning health care bra comprises the following steps: uniformly mixing warm water, graphene and hot-melt silica gel to prepare a graphene glue; uniformly printing a sandwich fabric with the mixed graphene glue for multiple times according to a template, air-drying, and fitting with a non-woven fabric sticky glue; carrying out positioning cold pressing and mold pressing of the fitted material at the temperature of 190 DEG C or less; then trimming into cups; seaming the cups combined with surface cups, back wings, flanks, shoulder straps, hook buckles, decorations and other traditional components, wherein the flanks adopt arc-shaped side plastic bones, the graphene-containing breast-conditioning health care bra is obtained through machine sewing. The graphene-containing breast-conditioning health care bra manufactured by applying the graphene high technology composite raw material provides a safest and comprehensive care for female breasts.

Description

technical field [0001] The invention relates to a preparation method of underwear, in particular to a preparation method of a graphene-containing breast conditioning health care bra. Background technique [0002] With the continuous development of society, women have higher and higher requirements for the use of bras. Traditionally, the main function of bras is to provide external support for breasts, adjust breast size, increase comfort and mobility, and maintain female breasts. Plump, fully displaying the role of female-specific body curves. [0003] In order to make women's breasts look more plump after wearing bras, the fabrics of traditional ordinary bras are made of flat sewing cups or foam sponge mold cups and stiff steel rings. Sponge is made of polyurethane or polyvinyl alcohol foam, which has the following disadvantages: first, the sponge is relatively heavy, which increases the total amount of the sponge and increases the load on the human body; second, the air p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41C3/00A41C3/12A41C5/00A61N5/06
CPCA41B2400/20A41B2400/32A41B2400/322A41B2400/34A41C3/0064A41C3/0085A41C3/12A41C5/005A61N5/0625A61N2005/0632A61N2005/0645A61N2005/066
Inventor 曾新民吴景乔
Owner 广州美乔新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com