Resin mold-filling method for manufacturing inverted-U-shaped stringer wallboards

A long stringer and resin technology, which is applied in the field of composite material manufacturing, can solve the problems of easy dry spot at the end of the stringer, fiber folds on the surface of parts, difficult resin flow control, etc., so as to improve the surface quality and internal quality, and reduce the dry spot. , the effect of improving the surface quality

Active Publication Date: 2016-10-26
SHENYANG AIRCRAFT CORP
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing VARI technology is in the manufacture of such as figure 1 and figure 2 For the "Ω"-shaped long stringer panel part shown (the part is 1400mm long and 400mm wide, and there are three "Ω"-shaped long stringers at equal intervals on one side of the skin of the part), there is not only the problem of difficult resin flow control, but also There are fiber folds on the surface of the parts, and the ends of the stringers are prone to defects such as dry spots and pores

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin mold-filling method for manufacturing inverted-U-shaped stringer wallboards
  • Resin mold-filling method for manufacturing inverted-U-shaped stringer wallboards
  • Resin mold-filling method for manufacturing inverted-U-shaped stringer wallboards

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] A resin filling method for manufacturing "Ω" type long truss panels, the method is as follows:

[0018] 1. Preparation of the prefabricated body, the fiber cloth is cut according to the requirements of the fiber angle and size in the digital model, and then the skin and the stringer are laid on the forming mold and the "Ω"-shaped stringer core respectively; Position and combine; after the combination is completed, clamp and fix the "Ω"-shaped stringer with the skin prefabricated body; sew the "Ω"-shaped stringer to the skin;

[0019] 2. After the suture is completed, follow the figure 2 According to the resin flow channel design idea in the article, the guide tubes are placed on both sides of the parallel "Ω"-shaped stringers, and then packaged. figure 2 The direction of the solid arrow in the center is the direction of resin flow. The flow of resin is mainly divided into three stages. Stage 1 is when the resin enters the fiber prefabricated body; stage 2 is when th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a resin mold-filling method for manufacturing inverted-U-shaped stringer wallboards by using a VARI technology. The method comprises the following steps: (a) preparing a fiber prefabricated body; cutting fiber cloth according to requirements on fiber angle and size in a digifax, then paving skin and stringers on a forming mold and an inverted-U-shaped stringer core mold, and stitching inverted-U-shaped stringers on the skin after finishing paving, positioning and combining; (b) placing flow guide tubes on two sides parallel to the length direction of the inverted-U-shaped stringers and enabling the resin flowing direction to be vertical to the length direction of the inverted-U-shaped stringers; (c) packaging a vacuum bag; (d) connecting equipment and the flow guide pipes after finishing packaging, and waiting for resin mold-filling. Through the method, a part resin mold-filling flowing channel is innovatively designed; the control problem of flowing of the resin is skillfully solved, so that the internal quality of the parts is ensured; the rate of finished products is increased.

Description

technical field [0001] The invention relates to a VARI (vacuum-assisted resin infiltration) manufacturing technology of "Ω"-shaped long truss wall plate parts, specifically relates to the design of resin filling flow channel and mold filling process control for parts manufacturing, and belongs to the field of composite material manufacturing. Background technique [0002] VARI technology is an important part of liquid forming technology in the field of composite material manufacturing. Compared with traditional prepreg / autoclave technology, it can realize the integral molding of large composite components without using autoclave. Its equipment Small investment and low cost. Compared with the fully closed mold of RTM technology, its mold cost is low. The resin used in VARI technology has the advantages of low viscosity, medium and low temperature mold filling, etc. Therefore, its process cost is also low. In view of the above advantages, at present, this technology is widel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/44B29C70/52
CPCB29C70/446B29C70/542
Inventor 康亮梁禄忠马秘辉张旺孟庆杰周开锋
Owner SHENYANG AIRCRAFT CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products