Novel wire insulating material

A technology of insulating materials and wires, applied in the direction of insulators, insulated conductors, insulated cables, etc., can solve the problems of poor moisture-proof performance, short service life, low wire strength, etc., and achieve good moisture-proof performance, long service life and excellent flame retardancy Effect

Inactive Publication Date: 2016-11-09
HEFEI PULFI WIRE TECH CO LTD
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by this invention is to provide a new type of wire insulation material to solve the defects of low strength, large loss, poor moisture resistance, easy aging and short service life of wires in the prior art during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A novel wire insulating material is characterized in that: the weight ratio of the novel wire insulating material is: 40 parts of nano ceramics, 19 parts of polyurethane, 40 parts of chlorinated polyethylene rubber, 18.5 parts of silicon carbide, 2 parts of barium sulfate powder, 1.8 parts of sodium silicate, 5 parts of rubber, 11 parts of xylenol, 4 parts of iron oxide powder, 1.7 parts of sulfur, 13 parts of polyester oxalate, 12 parts of diglycidyl cyclohexanedicarboxylate, 12 parts of meerschaum 4.5 parts, 4.5 parts of asphalt, 8 parts of adhesive, and 8 parts of plasticizer.

[0021] In the present invention, the adhesive is a mixture of epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane coupling agent.

[0022] In the present invention, the parts by weight of each component of the adhesive are 8 parts of epoxy resin, 2 parts of phenolic resin, 2 parts of acrylic acid, 3 parts of polyvinyl acetate and 1 part of silane coupling agent.

[0023] ...

Embodiment 2

[0028] A novel wire insulating material is characterized in that: the weight ratio of the novel wire insulating material is: 50 parts of nano ceramics, 10 parts of polyurethane, 20 parts of chlorinated polyethylene rubber, 15 parts of silicon carbide, 8 parts of barium sulfate powder, 3 parts of sodium silicate, 2 parts of rubber, 8 parts of xylenol, 6 parts of iron oxide powder, 1.5 parts of sulfur, 17 parts of polyester oxalate, 16 parts of diglycidyl cyclohexanedicarboxylate, 4 parts of sepiolite 2 parts, 2 parts of asphalt, 4 parts of adhesive, 6 parts of plasticizer.

[0029] In the present invention, the adhesive is a mixture of epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane coupling agent.

[0030] In the present invention, the parts by weight of each component of the adhesive are 10.5 parts of epoxy resin, 3.5 parts of phenolic resin, 3 parts of acrylic acid, 4.5 parts of polyvinyl acetate and 2 parts of silane coupling agent.

[0031] In the ...

Embodiment 3

[0036] A novel wire insulating material is characterized in that: the weight ratio of the novel wire insulating material is: 45 parts of nano ceramics, 14.5 parts of polyurethane, 30 parts of chlorinated polyethylene rubber, 22 parts of silicon carbide, 5 parts of barium sulfate powder, 4.2 parts of sodium silicate, 3.5 parts of rubber, 9.5 parts of xylenol, 2 parts of iron oxide powder, 1.9 parts of sulfur, 9 parts of polyester oxalate, 14 parts of diglycidyl cyclohexanedicarboxylate, 8 parts of sepiolite 7 parts, 7 parts of asphalt, 6 parts of adhesive, and 10 parts of plasticizer.

[0037] In the present invention, the adhesive is a mixture of epoxy resin, phenolic resin, acrylic acid, polyvinyl acetate and silane coupling agent.

[0038] In the present invention, the parts by weight of each component of the adhesive are 13 parts of epoxy resin, 5 parts of phenolic resin, 4 parts of acrylic acid, 6 parts of polyvinyl acetate and 3 parts of silane coupling agent.

[0039] I...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel wire insulating material and relates to the technical field of electric engineering. The insulating material contains, by weight, 40-50 parts of nano-ceramics, 10-19 parts of polyurethane, 20-40 parts of chlorinated polyethylene rubber, 15-22 parts of silicon carbide, 2-8 parts of barium sulfate powder, 1.8-4.2 parts of sodium silicate, 2-5 parts of rubber, 8-11 parts of xylenol, 2-6 parts of iron oxide powder, 1.5-1.9 parts of sulphur, 9-17 parts of oxalic polyester, 12-16 parts of diglycidyl cyclohexanedicarboxylate, 4-12 parts of meerschaum, 2-7 parts of asphalt, 4-8 parts of an adhesive and 6-10 parts of a plasticizer. According to the novel wire insulating material, nano-ceramics is used as the main raw materials, and the other raw materials function together and cooperate with each other. Thus, the insulating material has good insulating properties, high strength, high temperature resistance, low high-frequecny loss, good humidity resistance, excellent flame retardancy and ageing resistance and long service life, and is appropriate to be used as a wire.

Description

technical field [0001] The invention relates to the technical field of electrical engineering, in particular to a novel wire insulation material. Background technique [0002] According to the national standard GB2900.5, the definition of insulating material is: "the material used to make the device electrically insulated". That is, a material that prevents the passage of electric current. Its resistivity is very high, usually in the range of 10^9 to 10^22Ω m. As in an electric motor, the insulation around the conductors isolates the turns from each other and from the grounded stator core to ensure safe operation of the motor. [0003] At present, the power industry is in a period of rapid development, and electrical products have been popularized in various industries. The insulation requirements of electrical products are very high. Although there are many types of surface insulation materials on the market, the performance is relatively single, and their uses are highl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L75/04C08L63/00C08L61/06C08L31/04C08K13/02C08K3/34C08K3/30C08K3/22C08K3/06H01B3/44H01B7/295H01B7/282
CPCC08L23/286C08K2201/005C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/202C08L2205/035H01B3/443H01B7/282H01B7/295
Inventor 刘勇
Owner HEFEI PULFI WIRE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap