Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Abrasion-resistant clutch friction plate for automobile

A clutch and anti-wear technology, applied in clutches, friction linings, friction clutches, etc., can solve the problems of abrasive particles not easily discharged and abrasive wear, etc., and achieve the effect of reducing wear and prolonging service life

Inactive Publication Date: 2016-11-09
NANTONG WANDA FRICTION MATERIAL
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the clutch plate is closely combined with the flywheel and the pressure plate, the abrasive particles are not easy to discharge, and act as abrasives on the joint surface, thus causing abrasive wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Abrasion-resistant clutch friction plate for automobile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The application will be further described in detail below with reference to the drawings and embodiments. It can be understood that the specific embodiments described here are only used to explain the related invention, but not to limit the invention. In addition, it should be noted that, for ease of description, only the parts related to the invention are shown in the drawings.

[0010] It should be noted that the embodiments in the application and the features in the embodiments can be combined with each other if there is no conflict. Hereinafter, the present application will be described in detail with reference to the drawings and in conjunction with embodiments.

[0011] This embodiment provides an anti-wear automobile clutch friction plate, which includes the following materials in parts by mass: compounding agent: 0.4-1.2, sulfur: 6-8, starch 8-12, adhesive: 18-25, filler : 64-87.

[0012] The friction plate provided in the embodiment of the present invention can eff...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an abrasion-resistant clutch friction plate for an automobile. The abrasion-resistant clutch friction plate comprises, by mass, 0.4-1.2 parts of compounding agents, 6-8 parts of sulphur, 8-12 parts of starch, 18-25 parts of adhesives, and 64-87 parts of filling agents. According to the technical scheme provided by the embodiment of the invention, certain materials are added into the friction plate, abrasive material abrasion caused by tight combination between a friction plate and a flywheel as well as between the friction plate and a compression plate in the using process of a clutch can be effectively reduced, adhesion abrasion caused by high temperature due to vehicle overloading can also be effectively reduced, the abrasion of the friction plate and a mating plate is reduced, and the service life of the clutch is prolonged.

Description

Technical field [0001] The present disclosure generally relates to the field of automobile friction linings, and more particularly to anti-wear type automobile clutch friction linings. Background technique [0002] The friction linings used in dry automobile clutches will be worn during use and will produce wear under various conditions. Among them, the forms of wear are divided into three categories, namely, abrasive wear caused by the mechanical action of the friction surface, The molecular force forms surface adhesion nodes, and the adhesion wear caused by shearing of the adhesion nodes through mechanical action, and the surface corrosion and wear caused by the chemical action of the medium. [0003] During use, the friction plate will contact the flywheel or pressure plate to cause abrasive wear. When the surface of the friction plate is subjected to a normal load, the micro-protrusions on the surface will be plastically deformed and adhered. Under the action of small amplitud...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F16D13/64F16D69/02C09K3/14
CPCF16D13/64C09K3/14F16D69/02F16D2200/0082
Inventor 花月群彭鹏张杨张月锋
Owner NANTONG WANDA FRICTION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com