A kind of resin concrete and using method thereof

A resin concrete and epoxy resin technology, which is applied in the field of civil engineering, can solve the problems of operator's physical injury and easy volatilization, and achieve the effects of good permeability resistance, poor water permeability resistance and good repair effect.

Active Publication Date: 2019-06-14
广州毛勒桥梁附件有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] When the existing epoxy resin is used in resin concrete, liquid solvents are required, which are volatile and cause harm to the operator's body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of resin concrete and using method thereof
  • A kind of resin concrete and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A resin concrete comprises the following components according to the weight ratio: epoxy resin: 1, curing agent: 0.35, stones: 3.7 and quartz fine sand: 3.7.

[0027] Among them, the epoxy resin is: E-44 epoxy resin 6101. The curing agent is epoxy curing agent 5010B or T31. The stones are quartz stone aggregates with a particle size of 5-10mm. The fine sand is quartz fine sand material.

[0028] The using method of above-mentioned resin concrete comprises the following steps:

[0029] S1: Set up a mixer within 3m of the work construction area, put epoxy resin, fine sand, and stone raw materials into the mixer drum to stir according to the weight ratio, and mix evenly to obtain a mixture; the temperature of the mixture is 20-35°C.

[0030] S2: Mix the curing agent into the above mixture according to the weight ratio and stir evenly, and the stirring time is ≤2min to obtain the resin concrete.

[0031] S3: Pour the resin concrete into the gap or mold that needs to be ...

Embodiment 2

[0033] A resin concrete comprises the following components according to the weight ratio: epoxy resin: 0.9, curing agent: 0.45, stones: 3.7 and quartz fine sand: 3.7.

[0034] Among them, the epoxy resin is: E-44 epoxy resin 6101. The curing agent is epoxy curing agent 5010B or T31. The stones are quartz stone aggregates with a particle size of 5-10mm. The fine sand is quartz fine sand material.

[0035] The using method of above-mentioned resin concrete comprises the following steps:

[0036] S1: Set up a mixer within 3m of the work construction area, put epoxy resin, fine sand, and stone raw materials into the mixer drum to stir according to the weight ratio, and mix evenly to obtain a mixture; the temperature of the mixture is lower than 20°C; the preheating time is 20min, The temperature is 50°.

[0037] S2: Mix the curing agent into the above mixture according to the weight ratio and stir evenly, and the stirring time is ≤2min to obtain the resin concrete.

[0038] S...

Embodiment 3

[0040] A resin concrete comprises the following components according to the weight ratio: epoxy resin: 1.2, curing agent: 0.25, stones: 3.7 and quartz fine sand: 3.7.

[0041] Among them, the epoxy resin is: E-44 epoxy resin 6101. The curing agent is epoxy curing agent 5010B or T31. The stones are quartz stone aggregates with a particle size of 5-10mm. The fine sand is quartz fine sand material.

[0042] The using method of above-mentioned resin concrete comprises the following steps:

[0043] S1: Set up a mixer within 3m of the work construction area, put epoxy resin, fine sand, and stone raw materials into the mixer drum and stir according to the weight ratio, and mix evenly to obtain a mixture; the temperature of the mixture is higher than 35°C. The amount of curing agent needs to be less than that at room temperature.

[0044] S2: Mix the curing agent into the above mixture according to the weight ratio and stir evenly, and the stirring time is ≤2min to obtain the resi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a resin concrete, which comprises, by weight, 0.8-1.2 parts of an epoxy resin, 0.2-0.45 part of a curing agent, 3.5-4.0 parts of stone, and 3.5-4.0 parts of fine sand. According to the present invention, the resin concrete has advantages of high efficiency, good repair effect, excellent physical mechanical property, excellent tensile resistance, excellent compression resistance, excellent impact resistance, simple construction and short construction operation time, wherein the traffic can be opened after 3 h.

Description

technical field [0001] The invention relates to the technical field of civil engineering, in particular to a modified resin concrete and an application method thereof. Background technique [0002] In the form of increasing traffic volume on expressways, the operating pressure on roads and bridges continues to increase, and when repairs are required, the closure of roads has a greater impact. [0003] The structural characteristics of epoxy resin endow it with excellent product performance. As an adhesive, it has excellent bonding performance to various metals, non-metals, thermoplastics, and thermosetting plastics, and has high bonding strength, especially suitable for structural bonding. , The structure synthesized by sand and stone materials also has excellent physical and mechanical properties, and has excellent tensile, compressive and impact resistance properties. These advantages apply to building structures in harsh environments. [0004] When existing epoxy resins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/14
CPCC04B26/14C04B14/02C04B14/06
Inventor 郑文凡曾志龄黄森强
Owner 广州毛勒桥梁附件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com