Abstract

The invention application is a divisional application of a Chinese patent application 201510029118.1. The invention provides a spinning method for white coconut shell charcoal tencel combed cotton yarns. The method comprises: a, fore-spinning process requirements including bale plucking speed being 800+-80 r / min, kirschner beater speed being 380+-40 r / min, beater speed of a lapper being 550+-50 r / min, doffer speed of coconut shell carbon fibers being 18+-2 m / min, distance between a cylinder and a doffer being 0.019+-0.001 inch, doffer speed of tencel fibers being 21+-2 m / min, distance between a cylinder and a doffer being 0.019+-0.001 inch; fixed quantity being 21-24 g / 5m, draft multiple range of drafting tension being 6-8 times; process requirements of rough yarns including rough yarn design fixed quantity being 4.8+-4 g / 10m, roving twist factor being set at 88, total draft multiple being 8.28+-1 times, first break draft multiple being 1.35+-0.3 times, flyer speed being 900+-10 r / min, roller gauge being 10 mm x 28 mm x 41 mm; b, in spun yarn process requirements, twist multiplier being 368; c, in spooling process requirements, speed being 1000+-0 m / min.

Description

[0001] This application is a divisional application of a Chinese invention application with the application number "201510029118.1" and the application date of "January 20, 2015" entitled "White Coconut Shell Charcoal Tencel Combed Cotton Shirt Fabric and Its Weaving Method". technical field [0002] The invention belongs to the technical field of textiles, and in particular relates to a spinning method of white coconut shell charcoal tencel combed cotton yarn. Background technique [0003] In the prior art, the white coconut shell carbon fiber has super adsorption and moisture absorption functions, and has the functions of releasing negative oxygen ions beneficial to the human body and emitting far infrared rays. However, white coconut shell carbon fiber and tencel fiber have many problems such as low yarn strength and spinning wrapping roller during spinning. And there will be the problem of color fading of colored yarn or mutual staining between yarns of different colors....

AI Technical Summary

Problems solved by technology

However, the white coconut shell carbon fiber and tencel fiber have many problems such as low yarn strength and spinning around the skin roller during spinning.

Moreover, there will be problems of color fading of colored yarn or mutual staining between yarns of different colors

When the white coconut shell carbon fiber is weaved, when the existing technology is used, the above-mentioned functions of itself will be lost, and its original meaning will be lost.