High-temperature-resisting steel perfusion glue

A technology of high temperature resistance and high temperature, which is applied in the field of steel glue filling, can solve the problems of not being able to meet and improve people's quality of life, not being able to meet the needs of reinforcement in high temperature fields, and not being able to meet people's living needs, etc., to solve the difficulty of reinforcement, improve rigidity, The effect of good toughness

Inactive Publication Date: 2016-12-14
CARBON COMPOSITESTIANJIN CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, ordinary steel potting glue cannot meet the needs of reinforcement in high temperature fields
[0005] Conventional steel glue cannot be reinforced at high temperature, which limits the scope of use of steel glue, so it cannot meet people's living needs, nor can it meet and improve people's quality of life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The invention provides a technical solution: a high-temperature-resistant steel-filling glue, which belongs to the two-component epoxy structural reinforcement glue, and includes the following weight components:

[0025] A component:

[0026] Epoxy resin 128 75 parts,

[0027] Active diluent 10 parts,

[0028] 0.5 part of silane coupling agent,

[0029] B component:

[0030] Modified aromatic amine curing agent 90 parts.

[0031] A preparation method for high temperature resistant steel glue, comprising the following steps:

[0032] S1. Preparation of reactive diluent mixture for high-temperature potting glue: Stir the epoxy resin, reactive diluent and coupling agent according to the above weight components through a stirring device, and mix evenly. The stirring device is a planetary mixer or a turbine mixer;

[0033] S2. Prepare the curing agent for high-temperature steel potting glue: cure the modified aromatic amine curing agent, and keep it for 7 days;

[00...

Embodiment 2

[0037] The invention provides a technical solution: a high-temperature-resistant steel-filling glue, which belongs to the two-component epoxy structural reinforcement glue, and includes the following weight components:

[0038] A component:

[0039] Epoxy 128 82 parts,

[0040] Active diluent 13 parts,

[0041] 1 part of silane coupling agent,

[0042] B component:

[0043] Modified aromatic amine curing agent 95 parts.

[0044] A preparation method for high temperature resistant steel glue, comprising the following steps:

[0045] S1. Preparation of reactive diluent mixture for high-temperature potting glue: Stir the epoxy resin, reactive diluent and coupling agent according to the above weight components through a stirring device, and mix evenly. The stirring device is a planetary mixer or a turbine mixer;

[0046] S2. Prepare the curing agent for high-temperature steel potting glue: cure the modified aromatic amine curing agent, and keep it for 8 days;

[0047] S3. ...

Embodiment 3

[0050] The invention provides a technical solution: a high-temperature-resistant steel-filling glue, which belongs to the two-component epoxy structural reinforcement glue, and includes the following weight components:

[0051] A component:

[0052] Epoxy resin 128 85 parts,

[0053] Active diluent 15 parts,

[0054] 1.5 parts of silane coupling agent,

[0055] B component:

[0056] Modified aromatic amine curing agent 100 parts.

[0057] A preparation method for high temperature resistant steel glue, comprising the following steps:

[0058] S1. Preparation of reactive diluent mixture for high-temperature potting glue: Stir the epoxy resin, reactive diluent and coupling agent according to the above weight components through a stirring device, and mix evenly. The stirring device is a planetary mixer or a turbine mixer;

[0059] S2. Prepare the curing agent for high-temperature steel potting glue: cure the modified aromatic amine curing agent, and keep it for 9 days;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-temperature-resisting steel perfusion glue. The high-temperature-resisting steel perfusion glue belongs to double-component epoxy structural strengthening glue and comprises a component A and a component B. The component A comprises, by weight, 75-85 parts of epoxy resin 128, 10-15 parts of reactive diluents and 0.5-1.5 parts of silane coupling agent. The component B comprises, by weight, 90-100 parts of modified aromatic amine curing agent. By the adoption of the modified aromatic amine curing agent, the rigidity of cured epoxy resin is improved, the thermal stability of conventional steel perfusion glue is improved, long-term usage at 80-200 DEG C can be achieved, heat resistance is improved greatly, the application range of steel perfusion glue is widened, and the high-temperature-resisting steel perfusion glue keeps the properties of conventional steel perfusion glue including low viscosity, high mobility and good wettability and has unique advantages for building reinforcement in a high-temperature environment.

Description

technical field [0001] The invention relates to the technical field of steel-filling glue, in particular to a high-temperature-resistant steel-filling glue. Background technique [0002] Structural reinforcement is currently an effective measure for reinforcing bridges, roads, housing buildings, reservoir dams and other buildings. Structural reinforcement glue is an important part of the field of structural reinforcement. Common structural reinforcement glues include planting reinforcement glue, steel glue, steel filling glue, crack glue, etc. Among them, steel glue is mainly used for concrete components, masonry components outsourcing steel plate reinforcement, and grouting repair of internal defects of concrete. However, in the reinforcement of high-temperature fields such as thermal power generation and high-temperature pipelines, conventional steel-filling adhesives will cause bonding performance and mechanical properties to decrease significantly in a long-term high-te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J163/00C08G59/50
CPCC08G59/5033C09J163/00
Inventor 单书燕
Owner CARBON COMPOSITESTIANJIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com