Mouth rehabilitation material and preparation method thereof

A technology of dental restoration and cerium oxide, which is applied in the field of dental treatment, can solve the problems of limited clinical application range, small visual difference, and incompatibility of mechanical properties and processing properties of ceramic materials, and achieve clinical beauty, good mechanical properties and processing properties. Performance and the effect of small linear expansion coefficient

Inactive Publication Date: 2017-01-04
枣庄市立医院
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although cast ceramics, glass-infiltrated alumina ceramics, dense polycrystalline alumina ceramics, and zirconia ceramics have been released and used clinically, the mechanical properties and processing properties of the obtained ceramic materials ar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mouth rehabilitation material and preparation method thereof
  • Mouth rehabilitation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An oral restorative material, in terms of mass percentage, comprises the following components: 0.6% of cerium oxide, 0.8% of yttrium oxide, 1% of borax, 2% of sodium stannate, 3% of silicon dioxide, 15% of aluminum oxide, and the balance is Zirconia. The oral restorative material is powder, and its particle size is 40nm.

[0029] The preparation method of above-mentioned a kind of oral restorative material, comprises the steps:

[0030] (1) Dissolve zirconium oxychloride (the molar amount is obtained by converting the formula quantity of zirconia, the mass volume ratio of zirconium oxychloride to ethanol is 1g: 40-50mL) in ethanol, and then add cerium oxide at 60°C , alumina and yttrium oxide;

[0031] (2) Cool to 25°C, add sodium bicarbonate or potassium bicarbonate solution with a mass fraction of 2%, then add acrylate (the amount added is 0.7% of the mass of zirconium oxychloride), ultrasonically wash, and put it into an autoclave The reaction was carried out in (...

Embodiment 2

[0034] A dental restorative material, in terms of mass percentage, comprising the following components: cerium oxide 2%, yttrium oxide 3%, borax 4%, sodium stannate 4%, silicon dioxide 5%, aluminum oxide 24%, and the balance is Zirconia. The oral restorative material is powder, and its particle size is 50nm.

[0035] The preparation method of above-mentioned a kind of oral restorative material, comprises the steps:

[0036] (1) Dissolve zirconium oxychloride (the molar amount is converted from the formula quantity of zirconia, and the mass volume ratio of zirconium oxychloride to ethanol is 1g: 40-50mL) in ethanol, and then add cerium oxide at 80°C , alumina and yttrium oxide;

[0037] (2) Cool to 25°C, add sodium bicarbonate or potassium bicarbonate solution with a mass fraction of 5%, then add acrylate (the amount added is 0.9% of the mass of zirconium oxychloride), ultrasonically wash, and put it into an autoclave The reaction was carried out in (the reaction temperature...

Embodiment 3

[0040] An oral restorative material, in terms of mass percentage, comprising the following components: preferably, comprising the following components: 1% cerium oxide, 1.2% yttrium oxide, 2% borax, 2.5% sodium stannate, 3.5% silicon dioxide, Aluminum oxide 17%, the balance is zirconia. The oral restorative material is powder, and its particle size is 40nm.

[0041] The preparation method of above-mentioned a kind of oral restorative material, comprises the steps:

[0042] (1) Dissolve zirconium oxychloride (the molar amount is obtained by converting the formula quantity of zirconia, the mass volume ratio of zirconium oxychloride to ethanol is 1g: 40-50mL) in ethanol, and then add cerium oxide at 60°C , alumina and yttrium oxide;

[0043] (2) Cool to 25°C, add sodium bicarbonate or potassium bicarbonate solution with a mass fraction of 2%, then add acrylate (the amount added is 0.7% of the mass of zirconium oxychloride), ultrasonically wash, and put it into an autoclave The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a mouth rehabilitation material and a preparation method thereof. The mouth rehabilitation material is prepared from, by mass, 0.6%-2% of cerium oxide, 0.8-3% of yttrium oxide, 1%-4% of borax, 2%-4% of sodium stannate, 3%-5% of silicon dioxide, 15%-24% of aluminum oxide and the balance zirconium oxide. The mouth rehabilitation material is directly subjected to injection molding to obtain a ceramic tooth part, the tensile strength is high, the linear expansion coefficient is small, the Rockwell hardness is high, the yield strength is high, the advantages of being high in hardness, strength and toughness and the like are achieved, that is, good mechanical performance and processability are achieved, and meanwhile more excellent corrosion resistance is achieved. In addition, the ceramic tooth part obtained through direct injection molding of the mouth rehabilitation material and the tooth body of the human body are equivalent in refractive index, the ceramic tooth part is closer to the teeth of the human body, and clinical use is more attractive.

Description

technical field [0001] The present invention relates to an oral restorative material. The invention belongs to the technical field of dental treatment. Background technique [0002] Oral restoration is mainly aimed at the treatment of tooth defects and tooth loss, such as inlays, full crowns, dentures, etc., and also includes the use of artificial restorations for the treatment of periodontal disease and maxillofacial tissue defects. It is an important part of stomatology. an important branch. [0003] The number of patients with tooth loss caused by dental caries, periodontitis and tooth damage in my country is as high as one-fifth to one-third of the total population. Therefore, it is undoubtedly very important to accelerate the development of oral restorative materials and products, relieve the pain of millions of patients, and reduce the burden of medical expenses, and it is also the call of social development. [0004] Because of its good biocompatibility, ceramic ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K6/027A61K6/02
CPCA61K6/802A61K6/818A61K6/822A61K6/824A61K6/831
Inventor 侯超杜波战延军董艳丽
Owner 枣庄市立医院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com