Nickel-chromium flat wire for electrical heating elements

An electric heating element, nickel-chromium technology, applied in the direction of metal material coating process, etc., can solve the problem of unsatisfactory surface finish, and achieve excellent abrasion resistance and good surface finish.

Inactive Publication Date: 2017-01-04
CHANGSHU MEILI ALLOY MATERIAL CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing nickel-chromium flat wires are used for electric heating elements. The abrasion resistance, oxidation resistance, corrosion resi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The nickel-chromium flat wire for electric heating elements includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0026] 1) Put 1-2 parts by weight of urotropine, 2.4 parts by weight of aminotrimethylene phosphonic acid, 2.5 parts by weight of hexyldecanol, and 0.7 parts by weight of lauryltrimethylammonium chloride into 40 parts by weight of deionized water in turn, and stir Uniform;

[0027] 2) Add 5.6 parts by weight of polyvinyl alcohol, 8.5 parts by weight of ethyl acrylate, 1.3 parts by weight of pancreatin plus bleach T, and 0.7 parts by weight of hexamethylenetetramine, and continue to stir until fully mixed evenly to obtain a coating treatment liquid;

[0028] 3) Put the nickel-chromium alloy main body into the coating treatment solution for immersion, take it out and dry it.

Embodiment 2

[0030] The nickel-chromium flat wire for electric heating elements includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0031] 1) 1 part by weight of urotropine, 2.4 parts by weight of aminotrimethylene phosphonic acid, 2.5 parts by weight of hexyldecanol, and 0.7 parts by weight of lauryltrimethylammonium chloride are dropped into 40 parts by weight of deionized water in turn, and stirred evenly;

[0032] 2) Add 5.6 parts by weight of polyvinyl alcohol, 8.5 parts by weight of ethyl acrylate, 1.3 parts by weight of pancreatin plus bleach T, and 0.7 parts by weight of hexamethylenetetramine, and continue to stir until fully mixed evenly to obtain a coating treatment liquid;

[0033] 3) Put the nickel-chromium alloy main body into the coating treatment solution for immersion, take it out and dry it.

Embodiment 3

[0035] The nickel-chromium flat wire for electric heating elements includes a nickel-chromium alloy main body, and the nickel-chromium alloy main body is subjected to coating treatment, and the coating treatment includes the following steps:

[0036] 1) Put 2 parts by weight of urotropine, 2.4 parts by weight of aminotrimethylene phosphonic acid, 2.5 parts by weight of hexyldecanol, and 0.7 parts by weight of lauryltrimethylammonium chloride into 40 parts by weight of deionized water in turn, and stir evenly;

[0037] 2) Add 5.6 parts by weight of polyvinyl alcohol, 8.5 parts by weight of ethyl acrylate, 1.3 parts by weight of pancreatin plus bleach T, and 0.7 parts by weight of hexamethylenetetramine, and continue to stir until fully mixed evenly to obtain a coating treatment liquid;

[0038] 3) Put the nickel-chromium alloy main body into the coating treatment solution for immersion, take it out and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nickel-chromium flat wire for electrical heating elements. The nickel-chromium flat wire comprises a nickel-chromium alloy body which is subjected to coating treatment, and coating treatment comprises the following steps that 1, 1-2 parts by weight of urotropine, 2.4 parts by weight of amino trimethylene phosphonic acid, 2.5 parts by weight of hexyldecanol and 0.7 part of lauryl trimethy ammonium chloride are put into 40 parts by weight of deionized water in sequence, and the materials are stirred to be uniform; 2, 5.6 parts by weight of polyvinyl alcohol, 8.5 parts by weight of ethyl acrylate, 1.3 parts by weight of igepon T and 0.7 part by weight of hexamethylenetetramine are added in sequence, stirring continues to be conducted till the materials are fully mixed to be uniform, and a coating treatment fluid is obtained; 3, the nickel-chromium alloy body is placed in the coating treatment fluid to be soaked and then taken out to be dried. According to the nickel-chromium flat wire for the electrical heating elements, the surface of the nickel-chromium is coated with a protective film, the performance is good, and the surface smoothness is good.

Description

technical field [0001] The invention relates to a nickel-chromium flat wire for an electric heating element. Background technique [0002] The nickel-chromium flat wire used for the existing electric heating element needs to be improved in terms of abrasion resistance, oxidation resistance, corrosion resistance, rust prevention, and weather resistance of the nickel-chromium alloy main body, and the surface finish is not satisfactory. Contents of the invention [0003] The object of the present invention is to provide a nickel-chromium flat wire for an electric heating element, the nickel-chromium alloy main body is coated with a film, and the surface of the nickel-chromium alloy main body is covered with a protective film, which has excellent abrasion resistance, oxidation resistance, corrosion resistance, and corrosion resistance. Rust, weather resistance, and good surface finish. [0004] In order to achieve the above object, the technical solution of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/07C23C22/73
CPCC23C22/07C23C22/73
Inventor 陈俊达
Owner CHANGSHU MEILI ALLOY MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap