Amorphous anti-DC iron core and its heat treatment method

A heat treatment method and anti-DC technology, used in heat treatment furnaces, heat treatment equipment, magnetic core manufacturing, etc., can solve the problems of uneven temperature of ordinary annealing furnaces and low magnetic consistency of products, and achieve high magnetic consistency and high magnetic properties. Consistency and temperature uniformity

Active Publication Date: 2018-01-30
河南嵩岳清诚新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] A typical heat treatment method is to use a common annealing furnace to heat the iron core multiple times. However, since different iron cores in the same batch of iron cores have different positions in the annealing furnace, the temperature of different positions inside the common annealing furnace is different. Uniformity, for example, the temperature at the furnace door is lower than that at other locations, resulting in different magnetic properties of different iron cores in the same batch of amorphous anti-DC iron cores after annealing, and the product magnetic consistency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous anti-DC iron core and its heat treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0035] The core of the invention is to provide a heat treatment method for an amorphous anti-DC iron core, which can improve the magnetic consistency of the product. Another core of the present invention is to provide an amorphous anti-DC iron core, which has high magnetic consistency of the product.

[0036] Please refer to figure 1 , figure 1 It is a flowchart of a specific embodiment of the heat treatment method provided by the present invention.

[0037...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat treatment method of non-crystal anti-direct-current iron cores. The heat treatment method comprises the steps that iron cores are classified and put in plates according to set standard; a continuous annealing furnace is preheated; the annealing time and annealing temperature of the continuous annealing furnace are set according to the weight of the iron cores; the well put iron cores are put in the continuous annealing furnace, and the continuous annealing furnace keeps the annealing temperature for iron core annealing. In the heat treatment method of the non-crystal anti-direct-current iron cores, the iron cores are firstly classified, and then the annealing time and annealing temperature of the continuous annealing furnace are set according to different weights of iron cores so that the continuous annealing furnace can conduct targeted continuous annealing on the iron cores, the temperature in the continuous annealing furnace is uniform, and it can be ensured that the annealed non-crystal anti-direct-current iron cores have higher magnetism consistency. The invention further discloses the non-crystal anti-direct-current iron cores. The products have higher magnetism consistency.

Description

technical field [0001] The invention relates to the technical field of machining, in particular to a heat treatment method for an amorphous anti-DC iron core. In addition, the present invention also provides a product produced by the heat treatment method of the above-mentioned amorphous anti-DC iron core. Background technique [0002] Amorphous anti-DC iron core is usually made by cutting the strip to the required width, winding it into the required disc or ring, and then heat-treating it. The qualified products are then cured. The strip used as raw material is mostly iron-based alloy, usually called iron core. The heat treatment of the iron core will change the atomic arrangement order of the amorphous, so that it becomes a crystal, and becomes a constant magnetic permeability, which is used for DC resistance. [0003] A typical heat treatment method is to use an ordinary annealing furnace to heat the iron core multiple times. However, since different iron cores in the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/02C21D1/26C21D9/00
CPCC21D1/26C21D9/0062H01F41/0206
Inventor 董晓源孙利军许晓飞董晓磊李希涛冯建峰
Owner 河南嵩岳清诚新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products