Hydrogen sulfide corrosion resistant hardened and tempered high-strength steel plate for offshore drilling platform and producing method for hydrogen sulfide corrosion resistant hardened and tempered high-strength steel plate

A steel plate production method and hydrogen sulfide resistance technology, applied in the field of metallurgy, can solve problems that restrict the development of national economic construction, etc., and achieve the effects of excellent hydrogen sulfide corrosion resistance, excellent impact toughness, and reduced sulfur content

Active Publication Date: 2017-03-22
WUYANG IRON & STEEL
3 Cites 8 Cited by

AI-Extracted Technical Summary

Problems solved by technology

For a long time, due to the lack of necessary production equipment and technical support, and because there is no domestic mature experience in the production of hydrogen sulfide corrosion-resistant quenched ...
View more

Abstract

The invention discloses a hydrogen sulfide corrosion resistant hardened and tempered high-strength steel plate for an offshore drilling platform. The steel plate consists of the following chemical components in percentage by weight: 0.13%-0.15% of C, 0.15%-0.35% of Si, 1.10%-1.30% of Mn, 1.20%-1.25% of Ni, less than or equal to 0.012% of P, less than or equal to 0.003% of S, 0.020%-0.050% of Al, 0.020%-0.030% of Nb, 0.030%-0.040% of V, 0.015%-0.02% of Ti, 1.00%-1.10% of Cr, 0.40%-0.50% of Mo, 0.0005%-0.0015% of B, less than or equal to 0.25% of Cu, and the balance Fe and inevitable impurities. A production method comprises the processes of heating, rolling and thermal treatment. The steel plate produced by the production method has the characteristics of being uniform in component and internally compact, has a good structure, good comprehensive properties, good hydrogen sulfide corrosion resistance and good welding performance, and the performances of the steel plate completely meet operating requirements of the hydrogen sulfide corrosion resistant hardened and tempered high-strength steel plate for the offshore drilling platform.

Technology Topic

Steel platesCorrosion resistant +5

Examples

  • Experimental program(4)

Example Embodiment

[0034] Example 1
[0035] The hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel plate for offshore drilling platform adopts the following composition ratio and production process. Composition ratio (wt): C: 0.15%, Si: 0.24%, Mn: 1.16%, Ni: 1.20%, P: 0.010%, S: 0.003%, Al: 0.035%, Nb: 0.023%, V: 0.035 %, Ti: 0.018%, Cr: 1.05%, Mo: 0.45%, B: 0.0005%, Cu: 0.12%, the balance is Fe and unavoidable impurities. The thickness is 85mm.
[0036] Production process: (1) Smelting process: The molten steel is first smelted in the primary smelting furnace and then sent to the LF refining furnace for refining. Increased slag volume and multiple flows of slag are used to facilitate the removal of P. The vacuum of the ladle VD furnace is 1580℃. During the refining process, 4kg/t molten steel for aluminum wire and 5.5m/t molten steel for Si-Ca wire are fed into the molten steel during the refining process, the vacuum degree is 66 Pa during vacuum treatment, and the vacuum holding time is 25 minutes.
[0037] (2) Continuous casting process: the superheat is 13℃, the drawing speed is 0.95m/min, and the continuous casting is obtained.
[0038] (3) Heating process: the continuous casting slab is heated in a continuous heating furnace, the maximum heating temperature is 1240℃, the soaking temperature is 1200℃, and the total heating time is 11min/mm.
[0039] (4) Rolling process: the rolling temperature of the first stage is 1050℃, the pass reduction rate is 10%, the final rolling temperature is 920℃, and the cumulative reduction rate is 40%; the thickness of the open steel is 150mm, and the second stage The start rolling temperature is 880℃, the final rolling temperature is 820℃, the cumulative reduction rate is 45%, and the single pass reduction rate is 12%.
[0040] (5) Heat treatment: adopt quenching + tempering process, quenching cooling medium is water, quenching temperature is 900℃, heat preservation coefficient 2.1min/mm, roll speed 4m/mim, water cooling accelerated cooling, tempering temperature is 650℃, heat preservation Time 5.5min/mm.
[0041] The mechanical properties and hydrogen sulfide corrosion resistance of the hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel sheet for offshore drilling platforms obtained in this example: yield strength 780MPa, tensile strength 840MPa, -40°C transverse impact energy average 150J, hardness 285HB/295HB/305HB , HIC (hydrogen sulfide corrosion resistance) test results are CLR: 0.05%, CTR: 0.01%, CSR: 0.003%.

Example Embodiment

[0042] Example 2
[0043] The hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel plate for offshore drilling platform adopts the following composition ratio and production process. Composition ratio (wt): C: 0.14%, Si: 0.26%, Mn: 1.09%, Ni: 1.21%, P: 0.008%, S: 0.002%, Al: 0.038%, Nb: 0.025%, V: 0.033 %, Ti: 0.015%, Cr: 1.08%, Mo: 0.48%, B: 0.0009%, Cu: 0.10%, the balance is Fe and unavoidable impurities. The thickness is 60mm.
[0044] Production process: (1) Smelting process: the molten steel is first smelted in the primary smelting furnace, and then sent to the LF refining furnace for refining. Increased slag volume and multiple slag flow are used to facilitate the removal of P. The vacuum of the ladle VD furnace is 1590℃. During the refining process, 4kg/t molten steel for aluminum wire and 5m/t molten steel for Si-Ca wire are fed into the molten steel during the refining process. The vacuum degree is 68Pa during vacuum treatment and the vacuum retention time is 23min.
[0045] (2) Continuous casting process: the superheat is 13℃, the drawing speed is 1.00m/min, and the continuous casting is obtained.
[0046] (3) Heating process: the continuous casting billet is heated in a continuous heating furnace, the maximum heating temperature is 1240℃, the soaking temperature is 1220℃, and the total heating time is 11min/mm.
[0047] (4) Rolling process: the rolling temperature of the first stage is 1050℃, the pass reduction rate is 10%, the final rolling temperature is 920℃, and the cumulative reduction rate is 40%; the thickness of the open steel is 120mm, and the second stage The start rolling temperature is 870℃, the final rolling temperature is 810℃, the cumulative reduction rate is 45%, and the single pass reduction rate is 12%.
[0048] (5) Heat treatment: adopt quenching + tempering process, quenching cooling medium is water, quenching temperature is 900℃, heat preservation coefficient 2.0min/mm, roll speed 4m/mim, water cooling accelerated cooling, tempering temperature is 660℃, heat preservation Time 5.5min/mm.
[0049] The mechanical properties and hydrogen sulfide corrosion resistance of the hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel plate for offshore drilling platforms obtained in this example: yield strength 790MPa, tensile strength 840MPa, -40°C transverse impact energy average 200J, hardness 290HB/300HB/305HB , HIC (hydrogen sulfide corrosion resistance) test results are CLR: 0%, CTR: 0%, CSR: 0%.

Example Embodiment

[0050] Example 3
[0051] The hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel plate for offshore drilling platform adopts the following composition ratio and production process. Composition ratio (wt): C: 0.13%, Si: 0.15%, Mn: 1.30%, Ni: 1.25%, P: 0.012%, S: 0.001%, Al: 0.020%, Nb: 0.020%, V: 0.030 %, Ti: 0.02%, Cr: 1.00%, Mo: 0.50%, B: 0.0015%, Cu: 0.20%, the balance is Fe and unavoidable impurities. The thickness is 85mm.
[0052] Production process: (1) Smelting process: the molten steel is first smelted in the primary smelting furnace, and then sent to the LF refining furnace for refining. Increased slag volume and multiple slag flow are used to facilitate the removal of P. When the ladle temperature is 1600℃, the vacuum of the ladle VD furnace During the refining process, 3kg/t molten steel for aluminum wire and 6m/t molten steel for Si-Ca wire are fed into the molten steel during the refining process, the vacuum degree is 70Pa during vacuum treatment, and the vacuum holding time is 15min.
[0053] (2) Continuous casting process: the superheat is 20℃, the drawing speed is 1.05m/min, and the continuous casting is obtained by continuous casting.
[0054] (3) Heating process: the continuous casting slab is heated in a continuous heating furnace, the maximum heating temperature is 1220℃, the soaking temperature is 1210℃, and the total heating time is 12min/mm.
[0055] (4) Rolling process: the rolling temperature of the first stage is 1100℃, the pass reduction is 30%, the final rolling temperature is 920℃, and the cumulative reduction is 50%; the thickness of the open steel is 145mm, the second stage The start rolling temperature is 850℃, the final rolling temperature is 800℃, the cumulative reduction rate is 30%, and the single pass reduction rate is 10%.
[0056] (5) Heat treatment: adopt quenching + tempering process, quenching cooling medium is water, quenching temperature is 910℃, heat preservation coefficient 2.3min/mm, roll speed 7m/mim, water cooling accelerated cooling, tempering temperature is 670℃, heat preservation The time is 4.5min/mm.
[0057] The mechanical properties and hydrogen sulfide corrosion resistance of the hydrogen sulfide corrosion-resistant quenched and tempered high-strength steel sheet for offshore drilling platforms obtained in this example: yield strength 790MPa, tensile strength 855MPa, -40°C transverse impact energy average 210J, hardness 300HB/295HB/300HB , HIC (hydrogen sulfide corrosion resistance) test results are CLR: 0%, CTR: 0%, CSR: 0%.

PUM

PropertyMeasurementUnit
Yield strength780.0mPa
Tensile strength840.0mPa
Lateral impact energy150.0J

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.

Similar technology patents

Far-infrared thermal therapy sand bed

ActiveCN106333840ASimple structurewell organized
Owner:深圳市英之创科技有限公司

High-strength die-casting aluminum alloy and processing technology thereof

InactiveCN114574719Awell organizedImprove mechanical properties and corrosion resistance
Owner:海安宏宇合金材料有限公司

Method for describing space entity object based on relations

InactiveCN103309947Awell organized
Owner:HANGZHOU DIANZI UNIV

Automatic strip tidying machine

InactiveCN103431079AWell organizedgood quality tea
Owner:安徽绿源机械科技股份有限公司

Classification and recommendation of technical efficacy words

  • Excellent overall performance
  • well organized

Method for preparing rare-earth-tungsten electrode material

InactiveCN103045886AHigh densitywell organized
Owner:DALIAN UNIV OF TECH

Large heat input energy welding high-strength EH36 steel plate and making method thereof

ActiveCN109161671AGood mechanical propertieswell organized
Owner:JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD

Microencapsulated DHA micro-algal oil containing antioxidant peptides and preparation method thereof

InactiveCN106617074AStrong antioxidant activitywell organized
Owner:NORTHEAST AGRICULTURAL UNIVERSITY

Multifunctional desk with books and goods capable of being collected intelligently

ActiveCN104000392Aachieve layeringwell-organized
Owner:CHANGCHUN UNIV OF SCI & TECH

Pickled chicken paw soak solution

InactiveCN103478669Awell organized
Owner:HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka