High nickel ternary lithium ion battery anode slurry and preparation method thereof
A lithium-ion battery and positive electrode slurry technology, which is applied to battery electrodes, secondary batteries, circuits, etc., can solve the problems of increasing the difficulty of homogenization, achieve the effects of reducing pulping time, reducing usage, and improving dispersion force
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0040] The preparation method of an embodiment of the high nickel ternary lithium ion battery positive electrode slurry of the present invention may include the following steps:
[0041] S1. Weigh the raw materials in parts by weight: 89.5-97.9 parts of high nickel ternary positive electrode powder, 1-5 parts of conductive agent, 1-5 parts of binder, 0.1%-0.5% by weight of all solid powders The mixed additives and the right amount of solvent. If the above-mentioned solid raw materials are stored abnormally, they can be baked first, cooled and then pulped.
[0042] S2. The binder and mixed additives in the raw materials are added to the solvent, stirred evenly and defoamed in vacuum to prepare a glue solution. Control the temperature of the glue liquid at 25-50℃.
[0043] Further, step S2 may include:
[0044] S2.1. Add any one of the binder and the mixed additive (dispersion type additive or acid buffer type additive) to the solvent, and then add the other after mixing uniformly. A...
Example Embodiment
[0056] Example 1
[0057] Take 97 parts of high-nickel ternary positive electrode powder, 1.3 parts of conductive agent, 1.4 parts of binder, and 0.3 parts of mixed additives. In the mixed additives, the dosage ratio of disperse type additives and acid buffer type additives is 1:2; It is polyvinylidene fluoride, the solvent is N-methylpyrrolidone, 25 parts. According to the preparation method of the present invention, the above-mentioned raw materials are made into a high-nickel ternary lithium ion battery positive electrode slurry. During the whole process, the temperature of the glue and the slurry is controlled to be 25-50 ℃, and the viscosity of the final slurry is 5600 mPa.s. The solid content of the slurry is 80%. Among them, the glue preparation time is 2.5h, and the total homogenization time is 5.0h.
Example Embodiment
[0058] Example 2
[0059] Take 96.8 parts of high-nickel ternary positive electrode powder, 1.3 parts of conductive agent, 1.4 parts of binder, and 0.5 part of mixed additives. In the mixed additives, the dosage ratio of dispersive additives and acid buffer type additives is 2:1; It is polyvinylidene fluoride, the solvent is N-methylpyrrolidone, 23.5 parts. According to the preparation method of the present invention, the above-mentioned raw materials are made into a high nickel ternary lithium ion battery positive electrode slurry. During the whole process, the temperature of the glue and the slurry is controlled to be 25-50°C, and the viscosity of the final slurry is 6300mPa.s. The solid content of the slurry is 81%. Among them, the glue preparation time is 2.5h, and the total homogenization time is 5.0h.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap