Full spectrum LED phosphor composition and high color white light LED lamp

A technology of LED lamps and phosphors, applied in the field of lighting, can solve the problems of high color temperature, low color rendering index of phosphors or their combination, and not suitable for home lighting LEDs, etc., achieve good color rendering, improve work and study efficiency, The effect of protecting eyesight

Active Publication Date: 2017-04-26
HEBEI LIFU CHEM TECH
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a full-spectrum LED phosphor composition and a high-color-rendering white LED lamp to solve the problem that t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Full spectrum LED phosphor composition and high color white light LED lamp
  • Full spectrum LED phosphor composition and high color white light LED lamp
  • Full spectrum LED phosphor composition and high color white light LED lamp

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033]Blu-ray chip + full-spectrum phosphor composition: 2700K color temperature

[0034] A full-spectrum phosphor composition with a color temperature of 2700K, comprising the following components in mass percent: an improved green phosphor (Lu, Y) with an emission peak at 525nm under blue light excitation 3 (Al,Ga) 5 o 12 : Ce: 79.2%, red phosphor SrLiAl with emission peak at 650nm under blue light excitation 3 N 4 :Eu: 20.8%. The matching Blu-ray chip wavelength is: 450nm-452.5nm. The emission spectrum of the obtained product is shown in figure 2 shown.

Embodiment 2

[0036] Blu-ray chip + full-spectrum phosphor composition: 3000K color temperature

[0037] A full-spectrum phosphor composition with a color temperature of 3000K, comprising the following components in mass percent: an improved green phosphor (Lu, Y) with an emission peak at 515nm under blue light excitation 3 (Al,Ga) 5 o 12 : Ce: 78.0%, red phosphor SrLiAl with emission peak at 650nm under blue light excitation 3 N 4 :Eu: 22.0%. The matching Blu-ray chip wavelength is: 450nm-452.5nm.

Embodiment 3

[0039] Blu-ray chip + full-spectrum phosphor composition: 4000K color temperature

[0040] A full-spectrum phosphor composition with a color temperature of 4000K, comprising the following components in mass percent: an improved green phosphor (Lu, Y) with an emission peak at 520nm under blue light excitation 3 (Al,Ga) 5 o 12 : Ce: 81.3%, red phosphor SrLiAl with emission peak at 650nm under blue light excitation 3 N 4 :Eu: 18.7%. The matching Blu-ray chip wavelength is: 450nm-452.5nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a full spectrum LED phosphor composition and a high color white light LED lamp. The composition comprises 78% to 88% of green phosphor with the emission peak of 500 nm to 550 nm under blue light excitation and 12% to 22% of red phosphor with the emission peak of 625 nm to 670 nm under blue light excitation, the phosphor composition has a general color rendering index larger than 95 under CCT of about 2700K to 6000K has a full spectrum close to natural light, the package of 2700K to 6000K color temperature can be realized, the yield is high, and the phosphor composition can be widely applied to an occasion with a strict color discrimination requirement such as lighting, printing and dyeing, jewelry, and cosmetics.

Description

technical field [0001] The invention relates to the technical field of lighting, in particular to a full-spectrum LED fluorescent powder composition and a high-color-rendering white LED lamp. Background technique [0002] 15 standard color samples are stipulated internationally, and a wider CRI (R1-R15) can be calculated from their average value, but CRI is usually defined as the average value of 8 standard color samples (R1-R8), which is usually called As a general color rendering index, and abbreviated as Ra. In particular, the color rendering of R9 saturated red is very important for a certain range of applications. [0003] At present, the mainstream white light LED uses InGaN blue light chips to excite YAG:Ce 3+ Phosphor powder produces yellow light complementary to blue light, which is then mixed to achieve. However, since YAG:Ce 3+ In phosphors, the spectral energy of red light accounts for about 8-15% of the total spectral energy, which is much lower than the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L33/50C09K11/64F21V9/16
CPCC09K11/64F21V9/30H01L33/502Y02B20/00
Inventor 杨志平路亚娟蒋双双刘学千赵金鑫
Owner HEBEI LIFU CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap