Viscose fiber containing radix isatidis extract and preparation method of viscose fiber

A technology of isatidis extract and viscose fiber, applied in the field of viscose fiber, can solve the problems of loss, loss of isatidis microcapsules, easy loss of isatidis microcapsules, etc., and achieve the effects of avoiding loss, short residence time and good mechanical properties

Active Publication Date: 2017-07-07
青岛邦特生态纺织科技有限公司
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (2) If coated with microcapsules, the Radix isatidis microcapsules are also easy to lose
[0010] In the spinning process, when the blended solution of viscose spinning stock solution and isatis root microcapsules is sprayed into the coagulation bath, the first fiber begins to form, and then covers the added microcapsules, but the v

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Viscose fiber containing radix isatidis extract and preparation method of viscose fiber
  • Viscose fiber containing radix isatidis extract and preparation method of viscose fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Embodiment 1 A kind of preparation method of viscose fiber containing Radix isatidis extract

[0058] Include the following steps:

[0059] (1) Preparation of isatidis microcapsules

[0060] A. Preparation of Radix Radix Emulsion

[0061] Add the Radix isatidis extract into the mixing container, add emulsifier, initiator and distilled water, control the temperature of the mixing container to 40°C, stir at 1800r / min, and stir for 0.5 hours to form a stable Radix isatidis emulsion;

[0062] Wherein the mass ratio of isatidis extract, emulsifier, initiator and distilled water is 100:5:1.8:350;

[0063] The emulsifier is Tween-20; the initiator is benzoyl peroxide.

[0064] , Preparation of melamine-formaldehyde resin capsule wall material prepolymer

[0065] Put 37% formaldehyde solution into the reaction kettle, stir, adjust the pH value to 7.8, add melamine according to the ratio of 37% formaldehyde solution: melamine at a ratio of 4:1, raise the temperature to 65°C,...

Embodiment 2

[0103] Embodiment 2 A preparation method of viscose fiber containing Radix isatidis extract, comprising the following steps:

[0104] (1) Preparation of isatidis microcapsules

[0105] A. Preparation of Radix Radix Emulsion

[0106] Add the Radix isatidis extract into the mixing container, add emulsifier, initiator and distilled water, control the temperature of the mixing container to 45°C, stir at 2000r / min, and stir for 0.7 hours to form a stable Radix isatidis emulsion;

[0107] Wherein the mass ratio of Radix isatidis extract, emulsifier, initiator and distilled water is 100: 7: 2.0: 370;

[0108] The emulsifier is Tween-20; the initiator is benzoyl peroxide.

[0109] , Preparation of melamine-formaldehyde resin capsule wall material prepolymer

[0110] Put 37% formaldehyde solution into the reaction kettle, stir, adjust the pH value to 8.0, add melamine according to the ratio of 37% formaldehyde solution:melamine is 4:1, raise the temperature to 70°C, and stir the rea...

Embodiment 3

[0150] Embodiment 3 The selection of microcapsule wall material

[0151] Adopt the preparation method of isatidis viscose fiber described in Example 1, only change the category of the capsule wall material in the preparation of Radix isatidis microcapsules in step (1), adopt the capsule wall material described in the following table 1 to prepare viscose fiber respectively , measure the viscose fiber prepared by each group, after washing 50 times, the loss rate of Radix isatidis on the surface of the fiber.

[0152] The selection of table 1 microcapsule wall material

[0153]

[0154] The above-mentioned urea-formaldehyde resin, polystyrene, polyisocyanate, gum arabic, and polycarbonate are all purchased finished products from the market, and the melamine-formaldehyde resin capsule wall material prepolymer is the melamine-formaldehyde resin capsule wall prepared by the preparation method described in Example 1. Material prepolymer.

[0155] As can be seen from the results ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Dry breaking strengthaaaaaaaaaa
Wet breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides viscose fiber containing a radix isatidis extract. According to the viscose fiber, the content of radix isatidis microcapsules is 9.1%-9.79%, the dry fracture strength of the fiber is 2.70cN/dtex-2.75cN/dtex, the wet fracture strength of the fiber is 1.70cN/dtex-1.75cN/dtex, the elongation at break of the fiber is 22%-23%, the antibacterial rate of the fiber to staphylococcus aureus is 99.0%-99.8%, the antibacterial rate of the fiber to Candida albicans is 96.6-98.8%, the antibacterial rate of the fiber to typhoid bacillus is 97.2%-99.1%, and the fiber has very strong effects of inhibiting and killing influenza A virus and influenza B virus. The invention further provides a preparation method of the viscose fiber containing the radix isatidis extract. The preparation method comprises a step of modifying the radix isatidis microcapsules. According to the preparation method, the loss of the radix isatidis microcapsules in the preparation process of the fiber is reduced, the dismantling backwashing rate of a coagulating bath filter is reduced, and the distribution uniformity of the radix isatidis microcapsules in the fiber is increased.

Description

technical field [0001] The invention relates to a viscose fiber, in particular to a viscose fiber containing Radix isatidis extract and a preparation method thereof, belonging to the technical field of textiles. Background technique [0002] The development of functional fibers is a symbol of the progress of modern fiber science. The development of functional fibers, differential fibers and high-performance fibers has created favorable conditions for the technological innovation of the traditional textile industry and the transformation to high-tech industries, and has contributed to the improvement of human living standards. Functional fiber refers to a new type of fiber that has some special function in addition to the physical and mechanical properties of ordinary fibers. [0003] Radix isatidis is an excellent Chinese herbal medicine, which has antibacterial, anti-virus, anti-tumor, and immune-enhancing functions; the extract of Radix isatidis is added to viscose fibe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F2/10D01F1/10C08G12/32
CPCD01F2/10C08G12/32D01F2/08D01F1/103B01J13/14Y02A50/30
Inventor 山传雷
Owner 青岛邦特生态纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap