Flame-retardant anti-static PVC (Polyvinyl Chloride) tube and preparation method thereof

A PVC pipe, flame retardant and antistatic technology, applied in the field of flame retardant and antistatic PVC pipe and its preparation, can solve problems such as exudation, and achieve good flame retardant performance and antistatic performance.

Inactive Publication Date: 2017-07-14
ANHUI GUODENG PIPE IND TECH CO LTD
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PVC-U pipe has strong corrosion resistance, easy bonding, low price, and hard texture. However, due to the leakage of PVC-U monomer and additives, it is only suitable for water supply systems whose delivery temperature does not exceed 45°C.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A flame-retardant antistatic PVC pipe, calculated in parts by weight, comprising the following raw materials:

[0023] 86 parts of polyvinyl chloride resin, 14 parts of calcium carbonate with a particle size of 600 mesh, 3 parts of German SMS3183, 5 parts of impact modifier, 1.5 parts of polyethylene wax, 2 parts of inorganic flame retardant and 4 parts of antistatic agent; antistatic agent The percentage content of each component is 25% of calcined kaolin, 35% of conductive carbon black and 40% of titanium dioxide, and the inorganic flame retardant is composed of brucite powder and sepiolite. Impact modifiers are methyl methacrylate, ethyl acrylate, butyl acrylate and styrene copolymers.

[0024] The preparation method comprises the following steps:

[0025] 1) Add calcium carbonate with a particle size of 600 mesh and an inorganic flame retardant into polyvinyl chloride resin and mix at high speed for 4 minutes;

[0026] 2) Then add the impact modifier, German SMS31...

Embodiment 2

[0029] A flame-retardant antistatic PVC pipe, calculated in parts by weight, comprising the following raw materials:

[0030] 80 parts of polyvinyl chloride resin, 10 parts of calcium carbonate with a particle size of 300 mesh, 4 parts of Green Industry CZ6100B, 3 parts of impact modifier, 0.5 parts of paraffin wax, 1 part of inorganic flame retardant and 2 parts of antistatic agent; antistatic agent The percentage content of each component is 30% of calcined kaolin, 40% of conductive carbon black and 30% of titanium dioxide, and the inorganic flame retardant is composed of brucite powder and sepiolite. Impact modifiers are methyl methacrylate, ethyl acrylate, butyl acrylate and styrene copolymers.

[0031] The preparation method comprises the following steps:

[0032] 1) Add calcium carbonate with a particle size of 300 meshes and an inorganic flame retardant into polyvinyl chloride resin and mix at high speed for 2 minutes;

[0033] 2) Then add the impact modifier, Green I...

Embodiment 3

[0036] A flame-retardant antistatic PVC pipe, calculated in parts by weight, comprising the following raw materials:

[0037] 90 parts of polyvinyl chloride resin, 20 parts of calcium carbonate with a particle size of 700 mesh, 2 parts of German SMS3182, 6 parts of impact modifier, 2 parts of oxidized polyethylene wax, 3 parts of inorganic flame retardant and 6 parts of antistatic agent; antistatic The percentage content of each component in the agent is 20% of calcined kaolin, 40% of conductive carbon black and 40% of titanium dioxide, and the inorganic flame retardant is composed of brucite powder and sepiolite. Impact modifiers are methyl methacrylate, ethyl acrylate, butyl acrylate and styrene copolymers.

[0038] The preparation method comprises the following steps:

[0039] 1) Add calcium carbonate with a particle size of 700 mesh and an inorganic flame retardant into polyvinyl chloride resin and mix at high speed for 5 minutes;

[0040] 2) Then add the impact modifier...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant anti-static PVC (Polyvinyl Chloride) tube and a preparation method thereof. The flame-retardant anti-static PVC tube comprises the following raw materials: a polyvinyl chloride resin, a filling agent, a stabilizer, an impact modifier, a lubricant, an inorganic flame retardant and an anti-static agent, wherein the anti-static agent consists of calcined kaolin, conductive carbon black and titanium dioxide; and the inorganic flame retardant consists of brucite powder and sepiolite. The preparation method comprises the following steps: 1) mixing the filling agent, the inorganic flame retardant and the polyvinyl chloride resin for 2-5 minutes at a high speed; and 2) further adding the impact modifier, the stabilizer, the lubricant and the anti-static agent into the mixture of the step 1), mixing for 10-15 minutes at 100-110 DEG C, after uniform mixing, transferring into a cooling stirring, stirring for 3-5 minutes at 40-50 DEG C at a slow speed, and finally performing extrusion by using a conical two-screw extruder at 180-190 DEG C, thereby obtaining the tube. The tube is good in flame retardancy and anti-static property, and can be applied to fields such as marsh gases and coal.

Description

technical field [0001] The technical field of PVC pipes of the present invention particularly relates to a flame-retardant and antistatic PVC pipe and a preparation method thereof. Background technique [0002] PVC (full name Polyvinylchlorid) is polyvinyl chloride, and other ingredients are added to enhance its heat resistance, toughness, ductility, etc. The top layer of this surface film is lacquer, the main component in the middle is polyvinyl chloride, and the bottom layer is back-coated adhesive. It is a well-loved, popular and widely used synthetic material in the world today. It is the second most used synthetic material worldwide. According to statistics, in 1995 alone, the production of PVC in Europe was about 5 million tons, while its consumption was 5.3 million tons. In Germany, PVC production and consumption average 1.4 million tons. [0003] PVC pipe (PVC-U pipe) rigid polyvinyl chloride pipe is made of polyvinyl chloride resin, stabilizer, lubricant, etc., ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L33/12C08K13/06C08K3/34C08K7/10C08K3/04C08K3/22C08K3/26
CPCC08K2201/003C08K2201/017C08L27/06C08L2201/02C08L2201/04C08L2203/18C08L2205/03C08L33/12C08K13/06C08K3/346C08K7/10C08K2003/222C08K3/04C08K2003/2241C08K2003/265
Inventor 李娟李伟利张正梅
Owner ANHUI GUODENG PIPE IND TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap