Soaking-salt sintered magnesium aluminate spinel brick for RH furnace and production method of soaking-salt sintered magnesium aluminate spinel brick for RH furnace

A magnesia-alumina spinel brick and a production method technology, applied in the field of refractory materials, can solve problems such as slag erosion in a RH vacuum refining furnace, and achieve the effects of lowering temperature, lowering porosity, and lowering costs

Inactive Publication Date: 2017-07-25
海城利尔麦格西塔材料有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a magnesia-alumina spinel brick for RH furnace and its production method to improve the porosity of the magnesia-alumina spinel brick, thereby solving the problem of slag erosion in the RH vacuum refining furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soaking-salt sintered magnesium aluminate spinel brick for RH furnace and production method of soaking-salt sintered magnesium aluminate spinel brick for RH furnace
  • Soaking-salt sintered magnesium aluminate spinel brick for RH furnace and production method of soaking-salt sintered magnesium aluminate spinel brick for RH furnace
  • Soaking-salt sintered magnesium aluminate spinel brick for RH furnace and production method of soaking-salt sintered magnesium aluminate spinel brick for RH furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with embodiment the present invention is further described:

[0017] The following examples describe the present invention in detail. These examples are only to describe the best embodiment of the present invention, and do not limit the scope of the present invention.

[0018] Embodiment 1-3 is provided below, and the formula of firing magnesia-aluminum spinel bricks with immersion salt in RH furnace is as shown in table 1:

[0019] Table 1 Example 1-3 uses magnesia carbon residual brick as the formula for making gunning material as main raw material

[0020]

[0021] In the above formula, the 97 high-purity magnesia, 97 fused magnesia, fused magnesia-aluminum spinel and calcined Al 2 o 3 All are commercially available raw materials. It is required that the magnesia content of the magnesia is high, and the alumina content in the fused magnesia-aluminum spinel is greater than 65%.

[0022] The main raw material indicators are shown in Table 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a soaking-salt sintered magnesium aluminate spinel brick for an RH furnace. Physicochemical indexes of the soaking-salt sintered magnesium aluminate spinel brick are as follows: MgO is larger than or equal to 86 percent, Al2O3 is larger than or equal to 10 percent, SiO2 is smaller than or equal to 0.74 percent, the compressive strength is larger than or equal to 108.4MPa, the apparent porosity is smaller than or equal to 13.0, the volume density is larger than or equal to 3.03g / cm<3>, and the water cooling and thermal shock stability at the temperature of 1100 DEG C is larger than or equal to 13. The soaking-salt sintered magnesium aluminate spinel brick is prepared from the following raw materials in parts by weight: 20-35 parts of 200-mesh 97 high-purity magnesia, 15-25 parts of 0-1mm 97 high-purity magnesia, 10-15 parts of 1-3mm 97 high-purity magnesia, 10-15 parts of 0-1mm 97 fused magnesia, 10-15 parts of 1-3mm 97 fused magnesia, 10-15 parts of 1-3mm 97 fused magnesium aluminate spinel, 3-5 parts of calcined Al2O3 micropowder and 3-5 parts of a binder paper pulp. After being sintered, the soaking-salt sintered magnesium aluminate spinel brick for the RH furnace is subjected to vacuum soaking-salt with an industrial salt solution, so that the porosity of the magnesium aluminate spinel brick is improved, and the problem of slag corrosion of an RH vacuum refining furnace is solved.

Description

technical field [0001] The invention relates to the field of refractory materials, in particular to a magnesia-aluminum spinel brick used for RH furnaces and a production method thereof. Background technique [0002] RH furnace is the main out-of-furnace refining equipment for producing high-quality steel. With the development of the steel industry and the expansion of living needs, the demand for high value-added products continues to increase, and the production load of the RH vacuum refining furnace has been increasing. Due to the continuous improvement of equipment functions, the performance of refractory materials has also been improved. high demands. The refractory material of RH vacuum refining furnace is required to have excellent resistance to molten steel and molten steel due to the severe erosion of high-temperature molten steel, the melting erosion of slag and molten steel, and the intense thermal shock damage process of intermittent treatment of molten steel. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/043C04B35/626
CPCC04B35/043C04B35/62605C04B2235/3217C04B2235/3222C04B2235/444C04B2235/77C04B2235/96
Inventor 赵东辉王新杰张义先尹斌金钊王健骁
Owner 海城利尔麦格西塔材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com