Surface electroplating processing technology for automobile safety belt buckle
A processing technology, seat belt technology, applied in the field of surface electroplating processing technology of automobile seat belt buckle, to achieve the effect of high promotion value, good comprehensive use characteristics, and enhanced corrosion resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] A surface electroplating process for a car seat belt buckle, comprising the steps of:
[0027] (1) Buckle cleaning treatment:
[0028] First use sandpaper to polish the surface of the buckle to be processed, blow off the surface debris with compressed air after completion, then immerse it in acetone solution for surface degreasing treatment, and finally take it out and rinse it with deionized water for later use ;
[0029] (2) Surface activation treatment:
[0030] Put the buckle treated in step (1) into a hydrochloric acid solution with a mass fraction of 5% and soak it for activation for 2 minutes, then take it out, rinse it with deionized water once, and set it aside;
[0031] (3) Electroplating nickel plating treatment:
[0032] Immerse the buckle treated in step (2) into the nickel plating solution for surface nickel plating treatment, and control the average current density to 2.5A / dm 2 After 11 minutes of electroplating treatment, the buckle can be taken out;...
Embodiment 2
[0044] A surface electroplating process for a car seat belt buckle, comprising the steps of:
[0045] (1) Buckle cleaning treatment:
[0046] First use sandpaper to polish the surface of the buckle to be processed, and then blow off the debris on the surface with compressed air, then immerse it in acetone solution for surface degreasing treatment, and finally take it out and rinse it with deionized water for later use ;
[0047] (2) Surface activation treatment:
[0048] Put the buckle processed in step (1) into a hydrochloric acid solution with a mass fraction of 6% for 2.5 minutes of activation treatment, take it out, rinse it with deionized water once, and set it aside;
[0049] (3) Electroplating nickel plating treatment:
[0050] Immerse the buckle after step (2) into the nickel plating solution for surface nickel plating, and control the average current density to 2.8A / dm 2After 12 minutes of electroplating treatment, the buckle can be taken out; the components and t...
Embodiment 3
[0062] A surface electroplating process for a car seat belt buckle, comprising the steps of:
[0063] (1) Buckle cleaning treatment:
[0064] First use sandpaper to polish the surface of the buckle to be processed, blow off the surface debris with compressed air after completion, then immerse it in acetone solution for surface degreasing treatment, and finally take it out and rinse it with deionized water for later use ;
[0065] (2) Surface activation treatment:
[0066] Put the buckle treated in step (1) into a hydrochloric acid solution with a mass fraction of 7% for 3 minutes, take it out, rinse it with deionized water, and set it aside;
[0067] (3) Electroplating nickel plating treatment:
[0068] Immerse the buckle treated in step (2) into the nickel plating solution for surface nickel plating treatment, and control the average current density to 3A / dm 2 After 13 minutes of electroplating treatment, the buckle can be taken out; the components and their corresponding...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
quality score | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap