Imitated bowlder artificial flagstone

An artificial stone slab and imitation jade technology, applied in the field of slate, can solve the problems of dirt penetrating into the board, artificial boards with fine holes, and insufficient smoothness, etc., and achieve the effects of bright colors, weight issues, and reduced production costs

Inactive Publication Date: 2017-11-14
南通戈雅石业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its disadvantage is that the formula is unreasonable, the surface of the produced wood-based panel will have fine holes, and the smoothness is not enough
Therefore, dirt will penetrate into the board during use, which is prone to bacterial growth and is not easy to clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The imitation jade artificial stone slab of the present invention is made of the following components according to the weight ratio:

[0026] 60 parts of aluminum hydroxide;

[0027] 20 parts of compound powder;

[0028] 71 parts of water reducing agent;

[0029] Accelerator 1 part;

[0030] Potassium peroxide ethyl ketone 0.2 part;

[0031] 28 parts of unsaturated resin;

[0032] Ash gravel 24 parts;

[0033] Pigment paste 0.1 part;

[0034] Alloy powder 0.1 part;

[0035] 20 parts of glass fiber;

[0036] 36 parts of loess lime powder;

[0037] 0.35 part of auxiliary agent.

[0038] The auxiliary agent is a mixture of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate, and the weight ratio of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate is 4:1.

Embodiment 2

[0040] The imitation jade artificial stone slab of the present invention is made of the following components according to the weight ratio:

[0041] 80 parts of aluminum hydroxide;

[0042] 25 parts of compound powder;

[0043] 82 parts of water reducing agent;

[0044] Accelerator 3 parts;

[0045] Potassium peroxide ethyl ketone 0.3 part;

[0046] 32 parts of unsaturated resin;

[0047] Ash grit 45 parts;

[0048] 0.3 parts of pigment paste;

[0049] 0.8 parts of alloy powder;

[0050] 40 parts of glass fiber;

[0051] 50 parts of loess lime powder;

[0052] 0.5 part of auxiliary agent.

[0053] The auxiliary agent is a mixture of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate, and the weight ratio of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate is 4:1.

Embodiment 3

[0055] The imitation jade artificial stone slab of the present invention is made of the following components according to the weight ratio:

[0056] 70 parts of aluminum hydroxide;

[0057] 23 parts of compound powder;

[0058] 77 parts of water reducing agent;

[0059] Accelerator 2 parts;

[0060] Potassium peroxide ethyl ketone 0.25 part;

[0061] 30 parts of unsaturated resin;

[0062] Ash gravel 32 parts;

[0063] 0.2 parts of pigment paste;

[0064] Alloy powder 0.5 part;

[0065] 30 parts of glass fiber;

[0066] 43 parts of loess lime powder;

[0067] 0.42 parts of auxiliary agent.

[0068] The auxiliary agent is a mixture of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate, and the weight ratio of silane coupling agent and tert-butyl peroxy-2-ethylhexanoate is 4:1.

[0069] The stone formula of the present invention is made of high polymer composite materials for imitation jade mosaic, and is made by modern production technology. It is environmen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a jade-like artificial stone slab, which is made of the following components according to the proportion by weight: 60-80 parts of aluminum hydroxide; 20-25 parts of composite powder; 71-82 parts of water reducer; 1-3 parts of accelerator 0.2-0.3 parts of potassium peroxide ethyl ketone; 28-32 parts of unsaturated resin; 24-45 parts of gray gravel; 0.1-0.3 parts of pigment paste; 0.1-0.8 parts of alloy powder; Powder 36-50 parts; auxiliary agent 0.35-0.5 parts. The advantages of the present invention are: the stone formula of the present invention, the imitation jade mosaic is made of polymer composite materials, and is made by modern production technology. It is environmentally friendly, non-toxic, and non-radiative. It is a new generation of environmentally friendly building materials. Diverse, colorful, crystal clear, can be produced according to various requirements of customers, flexible and changeable, convenient for decoration and matching, and create a colorful living space.

Description

technical field [0001] The invention relates to the field of stone slabs, in particular to an imitation jade artificial stone slab. Background technique [0002] There are two main types of natural stone: marble and granite. Generally speaking, those with texture are called "marble"; those with spots are called "granite". In a narrow sense, marble refers to the stone produced in Dali, Yunnan. In fact, there are not many stones from Dali in all parts of the country. The two can also be distinguished from geological concepts. Granite is igneous rock, also called acid crystalline plutonic rock. It is the most widely distributed rock in igneous rock. It is composed of feldspar, quartz and mica, and the rock is hard and dense. Its composition is mainly silicon dioxide, accounting for about 65% to 75%. The so-called igneous rock is the rock formed by the condensation and crystallization of underground magma or lava from volcanoes. The content of silica in igneous rocks, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B111/54C04B111/82
CPCC04B26/18C04B2111/542C04B2111/82
Inventor 沈建美
Owner 南通戈雅石业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com