Polycarbonate resin composition and optical molded article

A polycarbonate resin and composition technology, applied in optics, optical components, light guides, etc., can solve the problems of reduced light transmittance, unable to fully meet the requirements of light guide plate materials, etc., and achieve high utilization value, thermal stability and weather resistance. Excellent properties and excellent light transmittance

Active Publication Date: 2017-12-01
SUMIKA POLYCARBONATE LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the polycarbonate resin compositions disclosed in Patent Documents 3 to 6 do not fully satisfy recent demands as materials for light guide plates (particularly light transmission even when molding at high temperature for thin-wall molding). rate will not be reduced etc.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarbonate resin composition and optical molded article
  • Polycarbonate resin composition and optical molded article
  • Polycarbonate resin composition and optical molded article

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～17 and comparative example 1～6

[0131] The above-mentioned raw materials are dropped into the drum according to the ratio shown in Table 1 and Table 2. After dry mixing for 10 minutes, use a twin-screw extruder (manufactured by Nippon Steel Works, TEX30α) to melt at the melting temperature Melt-kneading was carried out at 220° C. to obtain pellets of a polycarbonate resin composition. It should be noted that the particles obtained in Examples and Comparative Examples are approximately elliptical columns, the average length of each aggregate formed by 100 particles is about 5.1 mm to about 5.4 mm, and the average major diameter of the cross-sectional ellipse is about 4.1 mm. to about 4.3 mm, and the average value of the minor diameter is about 2.2 mm to about 2.3 mm.

[0132] Using the obtained pellets, each test piece for evaluation was prepared according to the following method, and used for evaluation. The results are shown in Table 1 and Table 2.

[0133] (Measuring method of melt viscosity)

[0134] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a polycarbonate resin composition. The polycarbonate resin composition is obtained by blending, with respect to 100 pts.wt. of a polycarbonate resin (A), 0.005 to 3.0 pts.wt. of a melting viscosity modifier (B) and 0.005 to 1.0 pt.wt. of a phosphorous ester compound (C), and has a ratio eta 1 / eta 2 of melting viscosity of the polycarbonate resin composition eta 1 to melting viscosity eta 2 of the polycarbonate resin (A) satisfying 0.45<= eta 1 / eta 2<=0.95, where eta is melting viscosity at a measurement temperature of 220 DEG C and shearing rate of 10 sec.

Description

[0001] This application is a divisional application of application number: 201680007204.5, PCT application number: PCT / JP2016 / 001711, filing date: March 24, 2016, and title of invention "Polycarbonate resin composition and molded article for optics" . technical field [0002] The present invention relates to a polycarbonate resin composition and an optical molded article. Background technique [0003] Conventionally, polycarbonate resins have been used in molded products such as light guide plates, various lenses, and signs because of their excellent impact resistance, heat resistance, and transparency. [0004] For example, Patent Document 1 discloses an aromatic polycarbonate resin for a light guide plate in which a stabilizer and a release agent are mixed with an aromatic polycarbonate resin in which the ratio of the weight-average molecular weight to the number-average molecular weight is specified within a specific range. combination. [0005] Patent Document 2 disclo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L71/02C08K5/526C08K5/527G02B1/04
CPCC08K2201/014C08L69/00C08L2201/08C08L2201/10G02B1/04C08L71/02C08K5/526C08K5/527C08K5/524G02B6/0065
Inventor 榊阳一郎
Owner SUMIKA POLYCARBONATE LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com