Infrared high-emission coating and preparation method thereof

An emission coating and infrared technology, applied in coating and other directions, can solve the problems of coating peeling, partial variation and decomposition of filler, low thermal emission ratio, etc., and achieve the effects of ensuring cleanliness, improving stability, and accelerating heat dissipation efficiency

Active Publication Date: 2017-12-12
RICHU DONGFANG SOLAR ENERGY
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the thermal emissivity ratio of high-efficiency coatings is usually below 0.9. At the same time, as the temperature increases, the coating is prone to peeling off, chalking, and discoloration. Variation decomposition leads to the attenuation of the thermal emission ratio of the coating, which seriously affects the use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example

[0057] 1) Weigh 15-20% of silicone modified resin and 5-10% of fluorocarbon resin to mix and stir evenly;

[0058] 2) Weighing 15-25% of butyl acetate and 35-45% of xylene are mixed and stirred evenly;

[0059] 3) Mix the uniformly mixed resin and solvent in 1) and 2) and stir evenly for use;

[0060] 4) Weigh 8~15% of the nano-composite oxide FeTiOx and 2~5% of at least one oxide of Mg, Ni, Co, Gu, Si and mix them thoroughly, and put them into a high-temperature furnace, and control the heating temperature at 700~ 900°C, calcined for 2~3 hours for hybridization treatment;

[0061] 5) Preliminarily grinding the calcined nano-composite oxides in 4) for later use;

[0062] 6) Mix and stir the products obtained in 3) and 5) according to 7~8:3~2;

[0063] 7) According to the ratio of 0.1~0.2: 0.1~0.3: 0.3~0.5: 0.3~0.5, weigh the delustering agent, anti-settling agent, dispersant, and leveling agent respectively;

[0064] 8) Add the matting agent, anti-sedimentation agent, disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
emissivityaaaaaaaaaa
Login to View More

Abstract

The invention provides an infrared high-emission coating and a preparation method thereof and belongs to a functional coating film. The coating comprises a component A and a component B, wherein the component A is used as a main coating and contains a filler, a film forming matter and additives; the ilmenite type nano-composite oxide subjected to high-temperature calcinations hybridization treatment is used as the filler; the film forming matter includes one or two of organic silicon modified resin and fluorocarbon resin, a solvent n-butyl acetate and dimethylbenzene; the additives include a delustering agent, an anti-flooding agent, a dispersing agent and a flatting agent; a carbimide lipid curing agent is used as the component B. In a use process, the component A and the component B are uniformly mixed at the ratio of 9:(0.5-1); the coating can be utilized to quicken the heat dissipating efficiency of the object surface; the cleanness of the coating surface is guaranteed and the heat emission ratio of the coating is stabilized at the value more than or equal to 0.92 for a long time.

Description

technical field [0001] The invention relates to a functional coating film layer, in particular to an infrared high-emitting coating and a preparation method thereof. Background technique [0002] At present, the thermal emissivity ratio of high-efficiency coatings is usually below 0.9. At the same time, as the temperature increases, the coating is prone to peeling off, chalking, and discoloration. The variation decomposition leads to the attenuation of the thermal emissivity ratio of the coating, which seriously affects the use effect. Contents of the invention [0003] The technical problem to be solved in the present invention is to address the deficiencies of the prior art, and propose a high-infrared high-emitting coating that maintains a long-term stable thermal emission specific energy, and a preparation method thereof. [0004] The technical problem to be solved in the present invention is achieved through the following technical solutions, a high-infrared emission...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D127/12C09D7/12
CPCC08K2201/011C09D183/04C08L27/12C08K9/00C08K3/22
Inventor 焦青太魏加杰胡张顺
Owner RICHU DONGFANG SOLAR ENERGY
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com