A foaming material and a technology for a bumper, which is applied in the field of environmentally friendly flame-retardant polyurethane foaming material for the lower bumper and its preparation, can solve the problem of short escape time for personnel, difficulty in protecting the body and people, and unsatisfactory bumper strength. effects, etc.

Inactive Publication Date: 2017-12-15
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protect...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An environmentally friendly flame-retardant polyurethane foam material for bumper lower bars, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0020] Polyester 403: 25 parts;

[0021] Polyester 3360: 35 parts;

[0022] Glass fiber: 250 parts;

[0023] Polyether 4110: 12 parts;

[0024] Silicone oil: 2.5 parts;

[0025] Catalyst HP-2: 1.3 parts;

[0026] Catalyst A33: 1.5 parts;

[0027] Water: 3.6 parts;

[0028] Flame retardant TCEP: 36 parts.

[0029] Add the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 130r / min, and the stirring time is 4h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed at a ratio of 1:1.7 The mass ratio of the bumper can be mixed evenly to obtain the environmentally friendly flame-retardant polyurethane foam material for the bumper lower bar.

Embodiment 2

[0031] An environmentally friendly flame-retardant polyurethane foam material for bumper lower bars, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0032] Polyester 403: 26.5 parts;

[0033] Polyester 3360: 40 parts;

[0034] Glass fiber: 300 parts;

[0035] Polyether 4110: 15 parts;

[0036] Silicone oil: 2.75 parts;

[0037] Catalyst HP-2: 1.55 parts;

[0038] Catalyst A33: 1.7 parts;

[0039] Water: 3.75 parts;

[0040] Flame retardant TCEP: 37 parts.

[0041] Put the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 140r / min, and the stirring time is 4.5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed according to 1: The mass ratio of 1.7 is evenly mixed to obtain the environmentally friendly flame-retardant polyurethane foam material for the bumper lower bar.

Embodiment 3

[0043] An environmentally friendly flame-retardant polyurethane foam material for bumper lower bars, comprising the following preparation steps: firstly, a composite material is prepared in parts by mass:

[0044] Polyester 403: 28 parts;

[0045] Polyester 3360: 45 parts;

[0046] Glass fiber: 350 parts;

[0047] Polyether 4110: 18 parts;

[0048] Silicone oil: 3 parts;

[0049] Catalyst HP-2: 1.8 parts;

[0050] Catalyst A33: 1.9 parts;

[0051] Water: 3.9 parts;

[0052] Flame retardant TCEP: 38 parts.

[0053] Add the above materials into the reaction kettle for mixed reaction, wherein the silicone oil is silicone oil AK-158, the stirring speed is 150r / min, and the stirring time is 5h to obtain the combined material, and then the acetonitrile polyester and the combined material are mixed at a ratio of 1:1.7 The mass ratio of the bumper can be mixed evenly to obtain the environmentally friendly flame-retardant polyurethane foam material for the bumper lower bar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bumper lower bar environment-friendly flame-retardant polyurethane foam material and a preparation method. The bumper lower bar environment-friendly flame-retardant polyurethane foam material is composed of acetonitrile polyester and a composite material in a mass ratio of 1:1.7, and the composite material is composed of the following components by mass: 25-28 parts of polyester 403, 35-45 parts of polyester 3360, 250-350 parts of glass fiber, 12-18 parts of polyether 4110, 2.5-3 parts of silicone oil, 1.3-1.8 parts of a catalyst HP-2, 1.5-1.9 parts of a catalyst A33, 3.6-3.9 parts of water, and 36-38 parts of a flame retardant TCEP, wherein the silicone oil is silicone oil AK-158. The preparation method includes: adding the components of the composite material into a reaction kettle and carrying out mixing reaction under a stirring speed of 130-150r/min for 4-5h to obtain the composite material, then mixing acetonitrile polyester and the composite material in a mass ratio of 1:1.7 evenly, thus obtaining the bumper lower bar environment-friendly flame-retardant polyurethane foam material. With the materials and the method provided by the invention, the prepared bumper lower bar environment-friendly flame-retardant polyurethane foam material has the advantages of flame retardance and high temperature resistance, high flame-retardant properties, high strength, long service life and environmental protection.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant polyurethane foam material for a bumper lower bar and a preparation method thereof, belonging to the field of automobiles. Background technique [0002] At present, with the development of the automobile industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for auto parts have also increased significantly. As a part of safety precautions, people have stricter requirements for bumpers. High temperature resistance, high flame retardancy, high strength, light weight, long service life, and high environmental protection characteristics. The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protection for the body and people. Also, due to poor flame retardancy, the escape time of personnel is short, and there is a great potential safety hazard. . Theref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/48C08G18/61C08G18/42C08K7/14C08K5/521C08J9/12C08G101/00
CPCC08G18/4018C08G18/4202C08G18/4829C08G18/61C08G2101/00C08J9/125C08J2203/10C08J2375/06C08J2375/08C08K5/521C08K7/14C08G2110/0083
Inventor 朱章娣朱凌宇纪朝根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap