A kind of functional ceramic powder material and its preparation method and application

A technology of powder materials and functional ceramics, used in capacitors, electrical components, etc., can solve the problems of complex process and difficult control, and achieve the effect of broad application prospects, high dielectric constant, and good pressure-sensitive nonlinearity.

Active Publication Date: 2020-08-18
赣州艺佳兴陶瓷有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is relatively complicated and difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of functional ceramic powder material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A functional ceramic powder material, consisting of the following components by weight: CaCO 3 20 parts, CuO 20 parts, Al 2 o 3 10 parts, Fe 2 o 3 15 parts, NiO 5 parts, Ti 3 C 2 20 servings.

[0021] This embodiment also provides a preparation method of a functional ceramic powder material, the specific steps are as follows:

[0022] Step 1, weigh the following components by weight: CaCO 3 20 parts, CuO 20 parts, Al 2 o 3 10 parts, Fe 2 o 3 15 parts, 5 parts of NiO, spare;

[0023] Step 2, the above-mentioned CaCO 3 , CuO, Al 2 o 3 , Fe 2 o 3 , NiO, Ti 3 C 2 Grinding to a particle size of 0.06 μm yields CaCO 3 Powder, CuO powder, Al 2 o 3 Powder, Fe 2 o 3 Powder, NiO powder;

[0024] Step 3. Take Ti 3 AlC 2 Put it into a plastic reaction container, slowly add a sufficient amount of hydrofluoric acid with a mass fraction of 40%, shake it for 10 minutes while adding, and react in a water bath at 60°C for 10 hours to obtain a reaction soluti...

Embodiment 2

[0029]A functional ceramic powder material, consisting of the following components by weight: CaCO 3 40 parts, CuO 35 parts, Al 2 o 3 20 parts, Fe 2 o 3 20 parts, NiO 10 parts, Ti 3 C 2 30 servings.

[0030] This embodiment also provides a preparation method of a functional ceramic powder material, the specific steps are as follows:

[0031] Step 1, weigh the following components by weight: CaCO 3 40 parts, CuO 35 parts, Al 2 o 3 20 parts, Fe 2 o 3 20 parts, 10 parts of NiO, spare;

[0032] Step 2, the above-mentioned CaCO 3 , CuO, Al 2 o 3 , Fe 2 o 3 , NiO, Ti 3 C 2 Grinding to a particle size of 0.08 μm yields CaCO 3 Powder, CuO powder, Al 2 o 3 Powder, Fe 2 o 3 Powder, NiO powder;

[0033] Step 3. Take Ti 3 AlC 2 Put it into a plastic reaction container, slowly add a sufficient amount of hydrofluoric acid with a mass fraction of 40%, shake it for 20 minutes while adding, and react in a water bath at 60°C for 20 hours to obtain a reaction solut...

Embodiment 3

[0038] A functional ceramic powder material, consisting of the following components by weight: CaCO 3 30 parts, CuO 30 parts, Al 2 o 3 15 parts, Fe 2 o 3 17 parts, NiO 8 parts, Ti 3 C 2 25 servings.

[0039] This embodiment also provides a preparation method of a functional ceramic powder material, the specific steps are as follows:

[0040] Step 1, weigh the following components by weight: CaCO 3 30 parts, CuO 30 parts, Al 2 o 3 15 parts, Fe 2 o 3 17 parts, 8 parts of NiO, spare;

[0041] Step 2, the above-mentioned CaCO 3 , CuO, Al 2 o 3 , Fe 2 o 3 , NiO, Ti 3 C 2 Grinding to a particle size of 0.07 μm yields CaCO 3 Powder, CuO powder, Al 2 o 3 Powder, Fe 2 o 3 Powder, NiO powder;

[0042] Step 3. Take Ti 3 AlC 2 Put it into a plastic reaction container, slowly add a sufficient amount of hydrofluoric acid with a mass fraction of 40%, shake it for 15 minutes while adding, and react in a water bath at 60°C for 15 hours to obtain a reaction solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a functional ceramic powder material, a preparation method and an application. The functional ceramic powder material comprises components in parts by weight as follows: 20-40parts of CaCO3, 20-35 parts of CuO, 10-20 parts of Al2O3, 15-20 parts of Fe2O3, 5-10 parts of NiO and 20-30 parts of Ti3C2. Compared with the prior art, the method has the characteristics that operation is simple, conditions are easy to control and large-scale industrial production is easy, after a ceramic pressure-sensitive capacitor is prepared from the functional ceramic powder material, a porous structure of 2D Ti3C2 is filled with CaCO3, CuO, Al2O3, Fe2O3 and NiO, and the capacitor has dual functions of pressure sensitivity and capacitance, can realize double effects of over-voltage protection and noise removal by filtering, and has good electromagnetic compatibility; the functional ceramic powder material has higher functional ceramic powder material, good frequency stability and good pressure-sensitive nonlinearity and has broad application prospect.

Description

technical field [0001] The invention relates to the field of inorganic non-metallic ceramic materials, in particular to a functional ceramic powder material and its preparation method and application. Background technique [0002] Varistor ceramic refers to a semiconductor ceramic material that has nonlinear volt-ampere characteristics at a certain temperature and within a certain voltage range, and its resistance decreases sharply with the increase of voltage. According to this volt-ampere characteristic, this semiconductor ceramic material can be used to make a non-linear resistor, that is, a piezoresistor. If the varistor also has a significant capacitive effect, it is called a varistor-capacitance dual-function element. When used, it is equivalent to a parallel combination of a varistor and a capacitor, which can protect against overvoltage. It has good electromagnetic compatibility and is undoubtedly more effective in ensuring the normal operation of the circuit. With...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/01C04B35/45C04B35/56C04B35/626C04B35/622H01G17/00
Inventor 赵伟
Owner 赣州艺佳兴陶瓷有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com