Composite board, as well as production process and equipment thereof

A technology of composite sheet and production process, which is applied in the direction of layered products, chemical instruments and methods, lamination devices, etc. The effect of firmness

Active Publication Date: 2018-01-12
红岛实业(英德)有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The defect of the former is that the mass is large, and the defect of the latter is that the compartment is easy to separate from the metal plate, especially after cutting, this characteristic is more obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite board, as well as production process and equipment thereof
  • Composite board, as well as production process and equipment thereof
  • Composite board, as well as production process and equipment thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] see figure 1 , 2 And 3, a kind of composite sheet material, comprises two-layer metal plate 1 up and down, and metal plate 1 is preferably stainless steel thin plate or aluminum thin plate, is provided with interlayer board 2 between described two-layer metal board 1, described interlayer board 2 A plurality of frustum-shaped hollow protrusions 3 with open lower surfaces and closed upper surfaces are provided on the upper surface, and a plastic compound for laminating the interlayer board 2 and the metal board 1 is provided between the sandwich board 2 and the metal board 1. Layer 4.

[0031] In this embodiment, the structure of the sandwich panel 2 is changed, and it is set as a sandwich panel 2 with a plurality of frustum-shaped hollow protrusions 3 in conjunction with a plastic composite layer 4 to achieve a close fit between the sandwich panel 2 and the metal plate 1 , its weight is lighter, and compared with the traditional wave-shaped metal interlayer, it will n...

Embodiment 2

[0037] like Figure 4 , a kind of production device that is used to produce the composite sheet material as described in embodiment 1, comprises the continuous rolling equipment 10 that is used to output sandwich panel semi-finished product and is used for the upper and lower two-layer metal plate 1 and sandwich panel 2 and A compound mechanism 20 for compounding two layers of plastic composite layers 4;

[0038] The continuous rolling equipment 10 includes an extrusion roller 101 and a support roller 102, the surface of the extrusion roller 101 is provided with a plurality of spherical extrusion parts 103, and the surface of the support roller 102 is an elastic surface 104; Between the pressure roller and the support roller 102 is a gap for passing the smooth metal plate 1;

[0039] Two composite rollers 201 arranged up and down in the composite mechanism 20, one side of the composite rollers 201 are respectively provided with a plate output unit 202 for outputting the metal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of composite boards, and discloses a composite board, which comprises upper and lower layers of metal plates, wherein a sandwich plate with a plurality of hollow protruding parts is arranged between the two layers of metal plates, and plastic composite layers for attaching the sandwich plate to the metal plates are arranged between the sandwich plate and the metal plates. The composite board is light in weight and strong in strength, and has a good bonding effect between a sandwich and the metal plates on the surfaces after cutting. In addition, the inventionalso provides a production process and equipment for producing the composite board.

Description

technical field [0001] The invention relates to the field of composite plate processing equipment, in particular to a composite plate and its production process and equipment. Background technique [0002] It is a commonly used technology in this field to set up an interlayer between two layers of metal sheets. There are two kinds of commonly used composite metal sheets. The first one is to set a plastic layer between the upper and lower layers of metal sheets, which is used to improve strength and heat insulation. Another is to set a corrugated metal spacer between two layers of metal plates, which is also used for strength and heat insulation. [0003] The defect of the former is that the mass is large, and the defect of the latter is that the interlayer is easy to separate from the metal plate, especially after cutting, this characteristic is more obvious. Contents of the invention [0004] The object of the present invention is to provide a composite plate with light ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B3/30B32B15/08B32B37/00B32B37/04B32B37/06
Inventor 姜荣行
Owner 红岛实业(英德)有限公司