Lip moistening moisture retention lip glaze formula and preparation method thereof

A lip glaze and formula technology, which is applied in the directions of pharmaceutical formulas, cosmetic preparations, dressing preparations, etc., can solve the problems of removing makeup, unable to cover lip lines, affecting facial makeup, etc., and achieves improvement of plumpness and moisture. And the effect of good color rendering ability and high color saturation

Inactive Publication Date: 2018-01-16
广州尚薇化妆品有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional lip gloss is applied on the lips after the production is completed, which cannot moisturize and moisturize for a long time, and after the lip gloss contacts with external objects...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] A formula and preparation method of a moisturizing lip glaze, comprising the following raw materials and weight fractions: 5-10 parts by mass of distearyl dimethyl ammonium hectorite; 10-15 parts by mass of propylene carbonate; 10-15 parts by mass of propylene carbonate; 3 to 5 parts by mass; 5 to 8 parts by mass of jojoba seed oil; 8 to 15 parts by mass of isotridecyl isononanoate; 5 to 10 parts by mass of coloring material; cyclopentasiloxane 10-20 parts by mass; trimethylsiloxysilicate 15-20 parts by mass; polypropylsilsesquioxane 5-10 parts by mass; microspheres 5-10 parts by mass; silicone resin 10-15 parts by mass; 10-15 parts by mass of isohexyl palmitate; 1-2 parts by mass of water and 2-5 parts by mass of silica.

[0016] The formula and preparation method of a lip moisturizing lip gloss include the following raw materials and weight fractions: 10 parts by mass of disteardimethylammonium hectorite; 10 parts by mass of propylene carbonate; 5 parts by mass of pol...

Embodiment 1

[0025] A formula and preparation method of a moisturizing lip glaze, comprising the following raw materials and weight fractions: 5-10 parts by mass of distearyl dimethyl ammonium hectorite; 10-15 parts by mass of propylene carbonate; 10-15 parts by mass of propylene carbonate; 3 to 5 parts by mass; 5 to 8 parts by mass of jojoba seed oil; 8 to 15 parts by mass of isotridecyl isononanoate; 5 to 10 parts by mass of coloring material; cyclopentasiloxane 10-20 parts by mass; trimethylsiloxysilicate 15-20 parts by mass; polypropylsilsesquioxane 5-10 parts by mass; microspheres 5-10 parts by mass; silicone resin 10-15 parts by mass; 10-15 parts by mass of isohexyl palmitate; 1-2 parts by mass of water and 2-5 parts by mass of silica.

[0026] The manufacturing process steps are as follows:

[0027] a. Weigh the above-mentioned raw materials according to parts by weight, and prepare disposable biscuit bags, olive oil and lip gloss tubes in addition;

[0028] b. First mix distearyl...

Embodiment 2

[0033] A formula and a preparation method of lip moisturizing lip glaze, comprising the following raw materials and their weight fractions: 10 parts by mass of disteardimethylammonium hectorite; 10 parts by mass of propylene carbonate; 5 parts by mass of polyisobutylene; Jojoba seed oil is 10 parts by mass; isotridecanyl isononanoate is 15 parts by mass; colorant is 10 parts by mass; cyclopentasiloxane is 20 parts by mass; Ester is 20 parts by mass; Polypropylsilsesquioxane is 10 parts by mass; Microsphere is 10 parts by mass; Silicone resin is 15 parts by mass; Isohexyl palmitate is 15 parts by mass; Water is 1 part by mass and Silica is 5 parts by mass.

[0034] The manufacturing process steps are as follows:

[0035] a. Weigh the above-mentioned raw materials according to parts by weight, and prepare disposable biscuit bags, olive oil and lip gloss tubes in addition;

[0036] b. First mix distearyl dimethyl ammonium hectorite, propylene carbonate, polyisobutylene, jojoba ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lip moistening moisture retention lip glaze formula and a preparation method thereof. The lip glaze formula comprises the following raw material in parts by weight: 5 to 10 parts of disteardimonium hectorite, 10 to 15 parts of propylene carbonate, 3 to 5 parts of polyisobutylene, 5 to 8 parts of jojoba seed oil, 8 to 15 parts of isotridecyl isononanoate, 5 to 10 parts ofpigment, 10 to 20 parts of cyclopentasiloxane, 15 to 20 parts of trimethyl siloxysilicate, 5 to 10 parts of polypropyl silsesquioxane, 5 to 10 parts of microsphere, 10 to 15 parts of organic silicon resin, 10 to 15 parts of isohexyl palmitate, 1 to 2 parts of water, and 2 to 5 parts of silica. The lip glaze has a good moistening and color developing performance, can keep the water of lips for a long time, and is not easy to remove.

Description

technical field [0001] The invention relates to the technical field of lip glaze preparation, in particular to a formulation of lip moisturizing lip glaze and a preparation method thereof. Background technique [0002] Lip glaze is a kind of lip makeup item. Using lip glaze can achieve the effect that lipstick and lip gloss cannot show. Before the appearance of lip gloss, makeup artists would add transparent lip gloss on the surface of red lipstick to create a bright and plump lip makeup effect. Lip gloss combines the saturated color of lipstick and the glossy texture of lip gloss into one, and it can be easily achieved with just one swipe of lip gloss. [0003] The traditional lip gloss is applied on the lips after the production is completed, which cannot moisturize and moisturize for a long time, and after the lip gloss contacts with external objects, it will adhere to the object, which is easy to cause makeup to come off, and when the traditional lip gloss is used It c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/92A61K8/58A61K8/81A61K8/37A61K8/25A61Q1/04A61Q19/00
Inventor 李冬敏
Owner 广州尚薇化妆品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap