Preparation method of composite yarn with flash effect

A yarn and mercerizing technology, which is applied in the field of composite yarn preparation, can solve the problems of dull yarn, dull fabric, poor three-dimensional effect, etc., achieve less scratchy feeling, better flash effect, and improve evenness and hairiness Effect

Active Publication Date: 2018-02-02
浙江中鼎纺织股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, whether it is pure spinning yarn or blended (mixed fiber) yarn, there are disadvantages such as dull yarn, poor three-dimensional effect, and the woven fabric is dull and not delicate, so it can no longer satisfy people's beauty-loving nature and fashion pursuit.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of composite yarn with flash effect
  • Preparation method of composite yarn with flash effect
  • Preparation method of composite yarn with flash effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The method for preparing a composite yarn with glittering effect described in this embodiment is as follows:

[0018] The first step is the selection of raw materials: 88% 90S mercerized Australian wool and 12% 46D gold and silver wire;

[0019] The second step is the preparation of pure wool roving: 88% of 90S mercerized Australian wool is prepared by loose wool dyeing → he wool → carding → drawing → roving (semi-worsted process route) to prepare a pure weight of 3.5g / 10m Wool roving; in the process of knitting, water, crude oil DH-601 and antistatic agent DK-103 are mixed into a mixed solution and sprayed on 90S mercerized wool at a spray rate of 35g / min, and then at room temperature Leave for 24 hours, and the amount of water accounts for 6% of the total amount of 90S mercerized Australian wool, the water temperature is controlled at 40℃, and the amount of hair oil DH-601 accounts for 1% of the total amount of 90S mercerized Australian wool. The antistatic agent DK- The ...

Embodiment 2

[0026] The method for preparing a composite yarn with glittering effect described in this embodiment is as follows:

[0027] The first step is the selection of raw materials: 84% 90S mercerized Australian wool and 16% 46D gold and silver wire;

[0028] The second step is the preparation of pure wool roving: 84% of 90S mercerized Australian wool is prepared by loose wool dyeing → blending → carding → drawing → roving (semi-worsted spinning process route) to prepare pure weight 3.5g / 10m Wool roving; in the process of knitting, water, crude oil DH-601 and antistatic agent DK-103 are mixed into a mixed solution and sprayed on the 90S mercerized Australian wool with a spray amount of 35g / min, and then at room temperature Leave for 24 hours, and the amount of water accounts for 6% of the total amount of 90S mercerized Australian wool, the water temperature is controlled at 40℃, and the amount of hair oil DH-601 accounts for 1% of the total amount of 90S mercerized Australian wool. The an...

Embodiment 3

[0035] The preparation method of a composite yarn with glittering effect described in this embodiment, the steps are as follows:

[0036] The first step is the selection of raw materials: 90% 90S mercerized Australian wool and 10% 46D gold and silver wire;

[0037] The second step is the preparation of pure wool roving: 90% of 90S mercerized Australian wool is prepared by loose wool dyeing → blending → carding → drawing → roving (semi-worsted process route) to prepare a pure weight of 3.5g / 10m Wool roving; in the process of knitting, water, crude oil DH-601 and antistatic agent DK-103 are mixed into a mixed solution and sprayed on the 90S mercerized Australian wool with a spray amount of 35g / min, and then at room temperature Leave for 24 hours, and the amount of water accounts for 6% of the total amount of 90S mercerized Australian wool, the water temperature is controlled at 40℃, and the amount of hair oil DH-601 accounts for 1% of the total amount of 90S mercerized Australian woo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of textile yarn, in particular to a preparation method of a composite yarn with a flash effect. The aim is to provide a preparation method of the compositeyarn with the flash effect, a gorgeous surface, a flashing luster and a strong sense of three-dimension. The preparation method comprises the first step of selection of raw materials, and the secondstep of preparation of pure wool roving; in the first step, the raw materials comprise 80-90% of 90S mercerized Australian wool and 8-20% of metallic yarn, and the total ratio of the 90S mercerized Australian wool and the metallic yarn is 100%; in the second step, the 80-90% of 90S mercerized Australian wool is prepared into the pure wool roving with a ration of 3.5 g per 10 m by means of flock dyeing, wool blending, cotton carding, drawing, and roving (semi worsted process route). The preparation method of the composite yarn with the flash effect utilizes the Siro-Phil technology to combine the metallic yarn with the mercerized Australian wool to make the yarn have better flash effect, the evenness and hairiness performance can be improved, the scratching sensation of the metallic yarn isreduced, and the yarn strength and the pilling performance of fabrics are improved.

Description

Technical field [0001] The invention relates to the technical field of textile yarns, in particular to a method for preparing composite yarns with glittering effects. Background technique [0002] Existing yarns can be divided into two categories according to the types of raw materials, pure spinning yarns and blended (blended fiber) yarns. The pure spinning yarns are composed of the same fiber, such as pure cotton yarn, wool yarn, viscose Glue fiber yarn, acrylic yarn, polyester yarn, nylon yarn, etc.; blended or twisted yarn is a yarn composed of two or more fibers, such as polyester / cotton blended yarn, wool / polyester Blended yarn, wool / acrylic blended yarn, polyester / viscose / acrylic blended yarn, silk / cotton twisted yarn, etc. However, whether it is pure spun yarn or blended (mixed fiber) yarn, the yarn has the defects of dullness, poor three-dimensionality, and the woven fabric is dull and not delicate, so it can no longer satisfy people's beauty-loving nature and pursuit o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/34
CPCD02G3/04D02G3/346D10B2101/20D10B2211/02
Inventor 朱跃文朱良勇沈明忠陈东升许力陆其兴
Owner 浙江中鼎纺织股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap