High thixotropic transparent marble adhesive and preparation method thereof

A marble glue and transparent technology, which is applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of transparent marble glue such as thinning and flowing, and achieve a simple and healthy preparation method Threat mitigation, enhanced mechanical and thixotropic effects

Active Publication Date: 2018-02-09
江苏大力士云石护理材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the above defects or improvement needs of the prior art, the present invention provides a highly thixotropic transparent marble glue, thereby solving the problem that the existing transparent marble glue is thin or even flowing at medium and high temperatures (35-65°C). technical problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High thixotropic transparent marble adhesive and preparation method thereof
  • High thixotropic transparent marble adhesive and preparation method thereof
  • High thixotropic transparent marble adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～ Embodiment 10

[0040] The high thixotropic transparent marble glue of embodiment 1~10, specific composition is listed in table 1 (the content data of each component in the form is weight part):

[0041] Table 1 High thixotropic transparent marble glue components and process conditions

[0042]

[0043] Accurately weigh the formulation components of Examples 1 to 10 in Table 1, wherein the mesh size of micron-sized silica is between 400 mesh and 1000 mesh, and prepare each embodiment according to the process conditions in Table 1 (while performing ultrasonic dispersion). Example of high thixotropic transparent marble glue.

[0044] According to GB / T 2794-2013 "Determination of Viscosity of Adhesives", the high thixotropic transparent marble glue prepared above was adopted SNB-3 digital rotational viscometer (Shanghai Nirun Intelligent Technology Co., Ltd.), and the 4th grade was selected. The rotors were tested at 35°C, 45°C, 55°C and 65°C at the speeds of 6r / min and 60r / min respectively, t...

Embodiment 16

[0074] Example 16: Stir at high speed under a negative pressure of 0.08Mpa and a rotating speed of 1500r / min, and carry out ultrasonic dispersion at the same time, and the duration is 30 minutes;

Embodiment 17

[0075] Example 17: Stir at high speed under a negative pressure of 0.1 Mpa and 1500 r / min at a rotational speed, and at the same time carry out ultrasonic dispersion for 30 minutes.

[0076] As shown in Table 5, under the process conditions of 1500r / min high-speed stirring under normal pressure and 1500r / min high-speed stirring under normal pressure and 1500r / min high-speed stirring under normal pressure, and ultrasonic dispersion at the same time or under negative pressure 0.08Mpa Stir at a low speed of 800r / min, and carry out ultrasonic dispersion at the same time. The duration of 30 minutes cannot reach the process conditions described in the present invention. The negative pressure is 0.08Mpa or 0.1Mpa, and the rotating speed is under the negative pressure state of 1500r / min. The effect of ultrasonic dispersion can only make the high thixotropic transparent marble glue overcome the shortcomings of existing marble glue that is thin or even flowing at medium and high temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high thixotropic transparent marble adhesive which includes, by weight parts, 100 parts of pre-accelerated unsaturated polyester resin, 3-5 parts of liquid thixotropic agent,5-10 parts of powder thixotropic agent and 10-200 parts of filler. The liquid thixotropic agent includes one or more selected from a group consisting of glycerol, diethylene glycol and triethylene glycol. The powder thixotropic agent includes polyamide wax, precipitated silica and transparent talc. The high thixotropic transparent marble adhesive is prepared by a preparation method of performinghigh-speed stirring at a negative pressure state with a negative pressure of 0.08-0.1 MPa and a rotating speed of no smaller than 1500 r / min and performing ultrasonic dispersion. The preparation method is simple, the prepared marble adhesive is good in thixotropic property, and the problem of being too thin or flowing does not occur even if at medium and high temperatures (35-65 DEG C).

Description

technical field [0001] The invention relates to a marble glue and a preparation method thereof, more particularly, to a highly thixotropic transparent marble glue and a preparation method thereof. Background technique [0002] As a stone adhesive, marble glue has been widely used in the field of stone construction, and it is the most widely used in the field of bonding. This requires that the marble glue cannot be thinned or flowed so as not to contaminate the stone, that is, the thixotropy of the marble glue ( When the object is sheared, the consistency becomes smaller, and when the shearing is stopped, the consistency increases again) is better. [0003] At present, manufacturers often use thixotropic agents to solve such problems, such as hydrogenated castor oil and nano-scale powder thixotropic agents mentioned in the patent 201010201032.X "A Stone Jointing Adhesive". However, the marble glue produced by thixotropic agents in China is only suitable for indoors with low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J167/06C09J11/06C09J11/04C09J11/08
CPCC08K2201/003C08K2201/014C09J11/04C09J11/06C09J11/08C09J167/06C08L77/00C08K3/36C08K3/34C08K5/053C08K5/06
Inventor 杜昆文杜昆武邱国峰毛攀峰熊善高周哲邓宇昊胡兆勇王莉亚
Owner 江苏大力士云石护理材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com