Preparation method of perovskite micron-ring array
A technology of perovskite and perovskite precursors, applied in the direction of lead halide, etc., can solve the problems of high cost, complex equipment, and difficult operation process, and achieve fast response, simple equipment, and low operation process difficulty.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] All inorganic CsPbBr with an inner diameter of 2.5um 3 Preparation of perovskite micro ring array
[0029] 1) The glass substrate is sequentially used with a volume ratio of 3:1 H 2 SO 4 / H 2 O 2 Ultrasonic cleaning with mixed solution, acetone, isopropanol, ethanol and deionized water; then dried with nitrogen and placed in an oven to dry for later use. Drop the polystyrene microsphere suspension on the cleaned glass substrate at 80rpm After the water has evaporated, the colloidal monolayer template is obtained by spin-coating at a speed of 90°C. The particle size of the polystyrene microspheres is 8um, and the solid content of the emulsion of the polystyrene microspheres in the polystyrene microsphere suspension is 5.0wt%;
[0030] 2) Combine 1mmolCsBr and 1mmolPbBr 2 Dissolve in 10mL dimethyl sulfoxide to obtain a precursor solution of perovskite;
[0031] 3) Spin-coating the perovskite precursor solution on the colloidal single-layer template at a spin-co...
Example Embodiment
[0034] Example 2
[0035] All inorganic CsPbBr with an inner diameter of 6um 3 The preparation method of perovskite micro ring array includes the following steps:
[0036] 1) The glass substrate is sequentially used with a volume ratio of 7:3 H 2 SO 4 / H 2 O 2 The mixed solution, acetone, isopropanol, ethanol and deionized water are ultrasonically cleaned; then dried with nitrogen and placed in an oven to dry for later use. Drop the suspension of polystyrene microspheres on the cleaned glass substrate, spin-coated at a speed of 60 rpm, after the water has evaporated, place it on a heating table at 100°C for 20 hours or 110°C for 1 hour, and naturally cool to room temperature to obtain A colloidal single-layer template, in which the particle size of the polystyrene microspheres is 10um, and the solid content of the emulsion of the polystyrene microspheres in the polystyrene microsphere suspension is 2.5wt%;
[0037] 2) Combine 0.8mmolCsBr and 1mmolPbBr 2 Dissolve in 10mL dimethyl sul...
Example Embodiment
[0040] Example 3
[0041] All inorganic CsPb(Cl 0.3 Br 0.7 ) 3 Preparation of perovskite micro ring array
[0042] 1) Use H with a volume ratio of 8:3 for the glass substrate in turn 2 SO 4 / H 2 O 2 The mixed solution, acetone, isopropanol, ethanol and deionized water are ultrasonically cleaned; then dried with nitrogen and placed in an oven to dry for later use. Drop the suspension of polystyrene microspheres on the cleaned glass substrate, spin-coated at a speed of 80 rpm, after the water has evaporated, place it on a heating table and heat it at 110°C for 1 hour and then naturally cool to room temperature to obtain a colloidal monolayer template; The particle size of the polystyrene microspheres is 9um, and the emulsion solid content of the polystyrene microspheres in the polystyrene microsphere suspension is 3.5wt%;
[0043] 2) Add 1mmolCsBr, 0.7mmolPbBr 2 And 0.3mmolPbCl 2 After mixing, dissolve in 10mL dimethyl sulfoxide to obtain a Cl ion-containing perovskite precursor solut...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap