Composite matting masterbatch for BOPA film and preparation technology thereof

A matting masterbatch and composite technology, which is applied in the field of preparation technology of composite matting masterbatch for BOPA film, can solve the problem of inability to take into account the smooth performance and optical performance of the film, and achieve product diversification, cost saving, and high efficiency. Environmentally friendly effects

Inactive Publication Date: 2018-04-03
SHANTOU BEST SCI & TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the shortcomings that the conventional matting masterbatch cannot take into account the smoothness and optical properties of the film, and provide a composite matting masterbatch for BOPA film and its preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A composite matting masterbatch for BOPA films, comprising the following components and parts by weight:

[0042] Polyamide 85

[0043] Composite matting agent 10

[0044] Composite coupling agent 4

[0045] Compound antioxidant 1;

[0046] Described composite type matting agent is made up of following components and weight ratio:

[0047] Poly-4-methyl-1-pentene 5

[0048] Polycarbonate 5;

[0049] Described compound coupling agent is made up of following component and weight ratio:

[0050] Coupling agent A151 3

[0051] Coupling agent A172 1;

[0052] Described composite antioxidant is made up of following component and weight ratio:

[0053] Primary antioxidant 1076 1

[0054] Secondary antioxidant 264 0.

[0055] The following steps: Add the carrier polyamide through the main feeding port of the extruder using an electronic precision weight loss scale, fully heat and melt, and poly 4-methyl-1-pentene, polycarbonate fiber, coupling agent A151, Coupling ag...

Embodiment 2

[0057] A composite matting masterbatch for BOPA films, comprising the following components and parts by weight:

[0058] Polyamide 82

[0059] Composite matting agent 13

[0060] Composite coupling agent 3.5

[0061] Composite antioxidant 1.5;

[0062] Described composite type matting agent is made up of following components and weight ratio:

[0063] Poly-4-methyl-1-pentene 7

[0064] Polycarbonate 6;

[0065] Described compound coupling agent is made up of following component and weight ratio:

[0066] Coupling agent A151 2.3

[0067] Coupling agent A172 1.2;

[0068] Described composite antioxidant is made up of following component and weight ratio:

[0069] Primary antioxidant 1076 1.8

[0070] Secondary antioxidant 264 0.7.

[0071] The following steps: Add the carrier polyamide through the main feeding port of the extruder using an electronic precision weight loss scale, fully heat and melt, poly 4-methyl-1-pentene, polycarbonate fiber, coupling agent A151, Coup...

Embodiment 3

[0073] A composite matting masterbatch for BOPA films, comprising the following components and parts by weight:

[0074] Polyamide 80

[0075] Composite matting agent 15

[0076] Composite coupling agent 3

[0077] Compound antioxidant 2;

[0078] Described composite type matting agent is made up of following components and weight ratio:

[0079] Poly-4-methyl-1-pentene 8

[0080] Polycarbonate 7;

[0081] Described compound coupling agent is made up of following component and weight ratio:

[0082] Coupling agent A151 2

[0083] Coupling agent A172 1;

[0084] Described composite antioxidant is made up of following component and weight ratio:

[0085] Primary antioxidant 1076 1

[0086] Secondary Antioxidant 264 1.

[0087] The following steps: Add the carrier polyamide through the main feeding port of the extruder using an electronic precision weight loss scale, fully heat and melt, poly 4-methyl-1-pentene, polycarbonate fiber, coupling agent A151, Coupling agent ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hazeaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite matting masterbatch for BOPA film, the masterbatch is mainly used for BOPA film. In the present invention, a variety of matting agents are preferred, and a composite formula is adopted to design a composite matting masterbatch. It combines the advantages of various matting agents and is used in BOPA film, which has both the optical properties and matting effect of the film, and avoids the disadvantages of using a single matting agent. The technology belongs to the field of functional polymer materials.

Description

technical field [0001] The invention relates to the field of functional polymer materials, in particular to a preparation process of a composite matting masterbatch for BOPA films. Background technique [0002] BOPA is the English abbreviation of Biaxially oriented polyamide (nylon) film. Biaxially oriented polyamide (nylon) film (BOPA) is an important material for the production of various composite packaging materials. It has become the third largest after BOPP and BOPET films. Packaging material, biaxially oriented nylon film referred to as BOPA film, its main raw material is polycaprolactam, referred to as nylon 6 or PA6, this raw material is melt-extruded and cast on special equipment, and then longitudinally and transversely (or At the same time) stretching to make a film, that is, biaxially oriented nylon film. Outstanding tensile strength and puncture resistance, excellent high barrier properties to gases and odors, chemical resistance to grease and carbon oxides, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L69/00C08L23/20C08K5/5425C08K5/134C08K5/13C08J3/22
CPCC08L77/00C08J3/226C08J2377/00C08J2423/20C08J2469/00C08K2201/014C08L2203/16C08L2205/03C08L2205/16C08L69/00C08L23/20C08K5/5425C08K5/1345C08K5/13
Inventor 杨波王锦江刘小珊李素英
Owner SHANTOU BEST SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com