Tensile-resistant and anti-breakage film material and preparation method thereof

A film material and anti-fracture technology, applied in the field of stretch-resistant and anti-fracture film materials and their preparation, can solve problems such as waste, bag rupture, etc., and achieve improved tensile strength and elongation at break, good application, and excellent tensile strength The effect of elongation

Inactive Publication Date: 2018-04-06
鲁忠华
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As plastic film is more and more widely used, people choose to use bags made of plastic film to hold items, and sometimes the items are too heavy to cause the bag to break, causing unnecessary waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A stretch-resistant and fracture-resistant film material, comprising the following raw materials in parts by weight: 50 parts of polyethylene, 3 parts of diethylenetriamine, 5 parts of methyl oleate, 4 parts of methyl benzoylformate, dimethylol 7 parts of urea, 4 parts of butyl orthosilicate, 11 parts of suberic acid, and 3 parts of methyl dihydrojasmonate.

[0020] A preparation method of a stretch-resistant and fracture-resistant film material, the preparation steps are: (1) mixing dimethylolurea and diethylenetriamine with deionized water twice its total mass to prepare dimethylolurea and the mixed solution A of diethylenetriamine; methyl oleate and methyl benzoylformate are mixed with 60% ethanol with 5 times of its total mass to prepare the mixed solution B of methyl oleate and methyl benzoylformate ; (2) Mix polyethylene with mixed solution A and mixed solution B, heat to 130°C and seal and stir at this temperature for 2 hours, the stirring speed is 250r / min; (3) ...

Embodiment 2

[0022] A stretch-resistant and fracture-resistant film material, comprising the following raw materials in parts by weight: 100 parts of polyethylene, 8 parts of diethylenetriamine, 11 parts of methyl oleate, 9 parts of methyl benzoylformate, dimethylol 15 parts of urea, 8 parts of butyl orthosilicate, 20 parts of suberic acid, and 7 parts of methyl dihydrojasmonate.

[0023] A preparation method of a stretch-resistant and fracture-resistant film material, the preparation steps are: (1) mixing dimethylolurea and diethylenetriamine with deionized water three times its total mass to prepare dimethylolurea and the mixed solution A of diethylenetriamine; methyl oleate and methyl benzoylformate are mixed with 80% ethanol of 8 times its total mass to prepare the mixed solution B of methyl oleate and methyl benzoylformate ; (2) Mix polyethylene with mixed solution A and mixed solution B, heat to 145°C and seal and stir at this temperature for 3 hours, the stirring speed is 400r / min; ...

Embodiment 3

[0025] A stretch-resistant and fracture-resistant film material, comprising the following raw materials in parts by weight: 75 parts of polyethylene, 6 parts of diethylenetriamine, 8 parts of methyl oleate, 7 parts of methyl benzoylformate, dimethylol 10 parts of base urea, 6 parts of butyl orthosilicate, 15 parts of suberic acid, and 5 parts of methyl dihydrojasmonate.

[0026] A preparation method of a tensile and fracture-resistant film material, the preparation steps are: (1) mixing dimethylolurea and diethylenetriamine with 2.5 times the total mass of deionized water to prepare dimethylolurea and the mixed solution A of diethylenetriamine; methyl oleate and methyl benzoylformate are mixed with 72% ethanol of 7 times its total mass to obtain the mixed solution B of methyl oleate and methyl benzoylformate ; (2) Mix polyethylene with mixed solution A and mixed solution B, heat to 135°C and seal and stir at this temperature for 2.6h, the stirring speed is 300r / min; (3) Then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tensile-resistant and anti-breakage film material. The film material is prepared from raw materials in parts by weight as follows: 50-100 parts of polyethylene, 3-8 parts ofdiethylenetriamine, 5-11 parts of methyl oleate, 4-9 parts of methyl benzoylformate, 7-15 parts of dimethylolurea, 4-8 parts of tetrabutyl orthosilicate, 11-20 parts of octanedioic acid and 3-7 partsof methyl dihydrojasmonate. The tensile-resistant and anti-breakage film material has greatly improved tensile strength and elongation at break, has excellent tensile strength at the low temperature,has the wide use range and can be better applied to food and medicine fields.

Description

technical field [0001] The invention relates to a film material, in particular to a stretch-resistant and fracture-resistant film material and a preparation method thereof. Background technique [0002] Plastic film can be used in food packaging, electrical product packaging, daily necessities packaging, clothing packaging and so on. As plastic film is more and more widely used, people choose to use bags made of plastic film to hold items, and sometimes the items are too heavy to cause the bag to rupture, causing unnecessary waste. Therefore, the present invention provides a film material with good stretch resistance and fracture resistance and a preparation method thereof. Contents of the invention [0003] The object of the present invention is to provide a stretch-resistant and fracture-resistant film material and its preparation method, so as to solve the problems raised in the above-mentioned background technology. [0004] To achieve the above object, the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K5/00C08K5/17C08K5/101C08K5/21C08K5/5415C08K5/092C08J5/18
Inventor 鲁忠华王金国
Owner 鲁忠华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap