Ceramic contact pin shell structure and manufacturing method thereof

A manufacturing method and shell technology, which is applied in semiconductor/solid-state device manufacturing, electrical components, electrical solid-state devices, etc., can solve problems such as inability to assemble and weld, solder cannot be filled, welding holes, etc., and achieve the effect of improving airtight reliability

Active Publication Date: 2018-04-20
NO 55 INST CHINA ELECTRONIC SCI & TECHNOLOGYGROUP CO LTD
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the gap is too narrow, the lead pins cannot be inserted smoothly, so that assembly and welding cannot be performed; if the gap is too wide, the solder cannot be filled, resulting in soldering holes
And a slight fluctuation in the size of the gap will also cause the amount of solder to be unable to be precisely controlled, resulting in airtightness problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic contact pin shell structure and manufacturing method thereof
  • Ceramic contact pin shell structure and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0040] Manufacturing the ceramic pin shell structure includes the following steps:

[0041] 1) Using tape casting equipment at a drying temperature of 120°C to obtain a sheet of raw porcelain tape with a thickness of 0.34mm and a length and width of 210mm;

[0042] 2) Take 4 layers of 0.34 thick aluminum nitride raw porcelain tape, and use a mechanical punching machine to open the holes required for the lead pin;

[0043] 3) Use a printing machine and a screen screen to coat the top surface and the bottom surface with tungsten paste to obtain the metallized area required for the welding end seal of the ceramic part and the Kovar sealing ring and the metal required for welding with the Kovar frame chemical area, to dry;

[0044] 4) After drying, use the stencil screen and printing machine to open holes for the tungsten paste on the outermost layer of the porcelain tape to realize the metallization of the inner wall, and obtain the metallization area of ​​the guide pin and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic contact pin shell structure and a manufacturing method thereof. According to the shell structure, a ceramic part and a metal guiding needle are subjected to a combination mode of end sealing and shaft sealing; the manufacturing method comprises the following steps of 1) obtaining aluminium oxide raw ceramic bands through curtain coating; 2) forming holes in each layer of the aluminium oxide raw ceramic bands; 3) performing printing on the outermost layer and the bottom layer of the ceramic bands to obtain metallization needed by ceramic part and shell framework welding; 4) performing hole suspension on the holes in the ceramic band on the outermost layer; 5) obtaining single processed ceramic parts; 6) adopting chemical nickel plating; 7) manufacturing a semi-finished product shell; and 8) manufacturing a finished product packaging shell. The ceramic contact pin shell structure and the manufacturing method thereof have the advantage as follows: the airtight reliability of high-reliability power electronic packaging shell can be improved effectively; and in addition, batch production preparation of the product can be ensured for a large-scale production process.

Description

technical field [0001] The invention relates to a ceramic pin housing structure and a manufacturing method thereof, which is aimed at the structure and manufacturing method of a packaging housing for power electronics, and belongs to the technical field of ceramic packaging. Background technique [0002] Ceramic pin housings are widely used in high-reliability packaging of power electronic devices, such as typical To254 and To256 series packaging. There are generally two types of sealing forms for the pins of this type of packaging shell, one is end sealing and the other is shaft sealing. Both sealing forms have a certain proportion of airtightness problems in the production process. [0003] For the end seal structure, the surface bonding is formed by welding the surface of the welding ring and the porcelain part, and the gap between the lead pin and the welding ring is filled with silver-copper solder to form a sealing structure of the welding ring, porcelain part and lead...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01L23/04H01L23/08H01L21/48
CPCH01L21/4803H01L21/4807H01L23/04H01L23/08
Inventor陈寰贝陈宇宁周昊
OwnerNO 55 INST CHINA ELECTRONIC SCI & TECHNOLOGYGROUP CO LTD