PVC synthetic leather for automotive interior

A technology for automotive interior and synthetic leather, applied in the field of leather, can solve the problems of poor anti-aging performance, can not be used as automotive interior material, poor wear resistance of PVC, achieve good wear resistance and scratch resistance, and improve anti-ultraviolet performance. , Improve the effect of anti-aging function

Active Publication Date: 2018-05-11
雄进塑料制品(东莞)有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary PVC leather, due to the characteristics of the product itself, has poor air permeability, is prone to mildew, and simultaneously breeds the growth of bacteria, and the PVC in the prior art has poor wear resistance and poor aging resistance, so it cannot be used as an automotive interior material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC synthetic leather for automotive interior
  • PVC synthetic leather for automotive interior
  • PVC synthetic leather for automotive interior

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] like figure 1 As shown in the figure, the present invention provides a kind of PVC synthetic leather for automobile interior, which is characterized in that: from bottom to top, the structure of the PVC synthetic leather sequentially includes a PVC base layer 1, a first adhesive layer 2, an antibacterial layer 3, a second adhesive layer The composite layer 4, the anti-ultraviolet layer 5, the third adhesive layer 6 and the wear-resistant layer 7, by weight, the antibacterial layer 3 includes the following components:

[0034] PVC resin 92.5%;

[0035] Chitosan 4%;

[0036] Nano silver antibacterial agent 3.5%;

[0037] The degree of deacetylation of chitosan is 90%, and the molecular weight of chitosan is 150,000.

[0038] By weight, the composition of nano-silver antibacterial agent is:

[0039] 42 nuclear alkyne silver cluster compound [Ag 42 {Eu(W 5 O 18 ) 2}( t BuC≡C) 28 Cl 4 ]OH xH 2 O 30%;

[0040] Silver-loaded zeolite 70%.

[0041] In parts by weig...

Embodiment 2

[0050] like figure 1 As shown in the figure, the present invention provides a kind of PVC synthetic leather for automobile interior, which is characterized in that: from bottom to top, the structure of the PVC synthetic leather sequentially includes a PVC base layer 1, a first adhesive layer 2, an antibacterial layer 3, a second adhesive layer The composite layer 4, the anti-ultraviolet layer 5, the third adhesive layer 6 and the wear-resistant layer 7, by weight, the antibacterial layer 3 includes the following components:

[0051] PVC resin 96.5%;

[0052] Chitosan 1%;

[0053] Nano silver antibacterial agent 2.5%;

[0054] The deacetylation degree of the chitosan is 92%, and the molecular weight of the chitosan is 180,000.

[0055]By weight, the composition of the nano-silver antibacterial agent is:

[0056] 42 nuclear alkyne silver cluster compound [Ag 42 {Eu(W 5 O 18 ) 2}( t BuC≡C) 28 Cl 4 ]OH xH 2 O 25%;

[0057] Silver-loaded zeolite 75%.

[0058] In parts...

Embodiment 3

[0068] like figure 1 As shown in the figure, the present invention provides a kind of PVC synthetic leather for automobile interior, which is characterized in that: from bottom to top, the structure of the PVC synthetic leather sequentially includes a PVC base layer 1, a first adhesive layer 2, an antibacterial layer 3, a second adhesive layer The composite layer 4, the anti-ultraviolet layer 5, the third adhesive layer 6 and the wear-resistant layer 7, by weight, the antibacterial layer 3 includes the following components:

[0069] PVC resin 98%;

[0070] Chitosan 1.5%;

[0071] Nano silver antibacterial agent 0.5%;

[0072] The deacetylation degree of the chitosan is 88%, and the molecular weight of the chitosan is 120,000.

[0073] By weight, the composition of the nano-silver antibacterial agent is:

[0074] 42 nuclear alkyne silver cluster compound [Ag 42 {Eu(W 5 O 18 ) 2}( t BuC≡C) 28 Cl 4 ]OH xH 2 O 35%;

[0075] Silver-loaded zeolite 65%.

[0076] In part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of leather and more specifically relates to PVC synthetic leather for automotive interior. The PVC synthetic leather comprises a PVC base layer, a first adhesion layer, an antibacterial layer, a second adhesion layer, an ultraviolet-proof layer, a third adhesion layer and a wear-resistant layer sequentially, wherein the antibacterial layer comprises thecomponents by weight as follows: 90%-98% of PVC resin, 0.1%-5% of chitosan and 0.1%-5% of a nano-silver antibacterial agent, the degree of deacetylation of the chitosan is 85%-95%, and the molecularweight of the chitosan is 0.1-0.2 million. Compared with the prior art, the PVC synthetic leather can have a good antibacterial effect by means of the antibacterial layer. Meanwhile, the ultraviolet-proof layer is arranged, so that the ultraviolet resistance of the synthetic leather can be improved, and the aging resistance of the synthetic leather can be improved; the PVC synthetic leather is endowed with good wear resistance and scratch resistance by means of the wear-resistant layer.

Description

technical field [0001] The invention belongs to the technical field of leather, and more particularly, the invention relates to a PVC synthetic leather for automobile interiors. Background technique [0002] With the development of synthetic leather technology, PVC synthetic leather has been used to replace natural leather in most areas of life due to its characteristics of various performance materials close to natural leather. Due to the development of various industries, the various requirements of customers for products are also getting higher and higher. Ordinary PVC leather, due to the characteristics of the product itself, has poor air permeability, is prone to mildew, and breeds bacterial growth at the same time, and the PVC in the prior art has poor wear resistance and anti-aging performance, so it cannot be used as a car interior material. [0003] In view of this, the present invention aims to provide a kind of PVC synthetic leather for automobile interior, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/06B32B27/18B32B27/30B32B7/12C08L27/06C08L5/08C08K9/12C08K3/08C08K5/132C08K3/36B60R13/02
Inventor 柯松
Owner 雄进塑料制品(东莞)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap