Flame-resistant waterproof lignin-modified asphalt roll and production method thereof

A technology for modifying asphalt and waterproofing membranes, applied in chemical instruments and methods, layered products, building insulation materials, etc., can solve problems such as safety accidents, and achieve enhanced interfacial bonding force, improved interfacial bonding strength, and excellent flame retardancy. performance effect

Inactive Publication Date: 2018-06-01
GUANGXI WUXUAN JINPAI WATERPROOF MATERIAL SCI & TECH CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the modified asphalt coil is a flammable material, and reports of safety accidents caused by the fire of the coil are often reported in the newspapers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-resistant waterproof lignin-modified asphalt roll and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A flame-retardant lignin-modified asphalt waterproof membrane, the waterproof membrane is a five-layer structure, from top to bottom: the upper surface isolation layer, the upper flame-retardant modified asphalt layer, the base layer, the lower resistance flame retardant modified asphalt layer and lower surface isolation layer; the upper flame retardant modified asphalt layer and the lower flame retardant modified asphalt layer are made of flame retardant modified asphalt, and the flame retardant modified asphalt The asphalt is made of the following raw materials in parts by weight: 40 parts of phenolized lignin; 20 parts of SBS modifier; 50 parts of 90# petroleum asphalt; 5 parts of γ-aminopropyltriethoxysilane; 5 parts of calcium carbonate; 5 parts of polyoxyethylene polyoxypropanolamine ether; 6 parts of citric acid; 6 parts of fumed silica; 1.6 parts of dimethyl methylphosphonate; 3.2 parts of microencapsulated red phosphorus; acetylcitric acid 3 parts of trihexyl e...

Embodiment 2

[0043]A flame-retardant lignin-modified asphalt waterproof membrane, the waterproof membrane is a five-layer structure, from top to bottom: the upper surface isolation layer, the upper flame-retardant modified asphalt layer, the base layer, the lower resistance flame retardant modified asphalt layer and lower surface isolation layer; the upper flame retardant modified asphalt layer and the lower flame retardant modified asphalt layer are made of flame retardant modified asphalt, and the flame retardant modified asphalt The asphalt is made from the following raw materials in parts by weight: 45 parts of phenolized lignin; 23 parts of SBS modifier; 55 parts of 90# petroleum asphalt; 2 parts of diethylenetriaminopropyltrimethoxysilane; γ- 3 parts of ethylenediaminotriethoxysilane; 3 parts of tri-tert-butoxyvinylsilane; 7 parts of modified nano-calcium carbonate; 7 parts of polyoxyethylene polyoxypropanolamine ether; 8 parts of citric acid; 8 parts of silicon oxide; 1.7 parts of d...

Embodiment 3

[0053] A flame-retardant lignin-modified asphalt waterproof membrane, the waterproof membrane is a five-layer structure, from top to bottom: the upper surface isolation layer, the upper flame-retardant modified asphalt layer, the base layer, the lower resistance flame retardant modified asphalt layer and lower surface isolation layer; the upper flame retardant modified asphalt layer and the lower flame retardant modified asphalt layer are made of flame retardant modified asphalt, and the flame retardant modified asphalt The asphalt is made from the following raw materials in parts by weight: 50 parts of phenolized lignin; 25 parts of SBS modifier; 60 parts of 90# petroleum asphalt; 3 parts of γ-methacryloxypropyltrimethoxysilane; 3 parts of γ-ureidopropyl triethoxysilane; 4 parts of (3-aminopropyl) triethoxysilane; 8 parts of modified nano-calcium carbonate; 8 parts of polyoxyethylene polyoxypropanolamine ether; lemon 9 parts of fumed silica; 2.4 parts of dimethyl methylphosph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to a flame-resistant waterproof lignin-modified asphalt roll. The flame-resistant waterproof lignin-modified asphalt roll is of a five-layer structure which comprises, from top to bottom, a top isolating layer, an upper flame-resistant modified asphalt layer, a padding layer, a lower flame-resistant modified asphalt layer and a bottom isolating layer, wherein the The upper and lower flame-resistant modified asphalt layers are prepared from flame-resistant modified asphalt. The flame-resistant modified asphalt is prepared from the following raw materials by weight: 40 to 50 parts of phenolated lignin, 20 to 25 parts of a SBS modifier, 50 to 60 parts of petroleum asphalt No. 90, 5 to 10 parts of a silane coupling agent, 5 to 8 parts of modified nanometer calcium carbonate, 5 to 8 parts of polyoxyethylene polyoxypropylene ether, 6 to 9 parts of citric acid, 6 to 9 parts of fumed silica, 4.8 to 7.2 parts of a flame-resistant mixture and 3 to 5 parts of trihexyl o-acetylcitrate. The flame-resistant waterproof lignin-modified asphalt roll prepared in the invention is greatly improved in tearing strength, bonding performance, water resistance, ageing resistance, hightemperature resistance, saline-alkaline tolerance and the like.

Description

technical field [0001] The invention relates to a polymer waterproof coiled material, in particular to a flame-retardant lignin-modified asphalt waterproof coiled material and a production method thereof, belonging to the field of waterproof chemical materials. Background technique [0002] Petroleum asphalt has good adhesion, aging resistance and waterproof ability, and has been widely used as road construction, waterproof and sealing materials for a long time. It is one of the most widely used materials in waterproof and anti-seepage projects at home and abroad because of its advantages of easy availability of raw materials and low price when used in waterproofing projects. [0003] Conserving resources and protecting the environment are the basic national policies of our country. Lignin is the second largest natural organic compound after cellulose in nature. The pulp and paper industry worldwide produces about 50 million tons of industrial lignin per year. The dischar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/02B32B27/06B32B27/36B32B13/14B32B13/12B32B17/02B32B17/06B32B27/32C08L95/00C08L97/00C08L71/02C08K13/06C08K3/26C08K3/36C08K5/11
CPCB32B5/022B32B5/02B32B13/12B32B13/14B32B17/06B32B27/06B32B27/32B32B27/36B32B2262/0276B32B2262/101B32B2307/306B32B2307/3065B32B2307/552B32B2307/558B32B2307/5825B32B2307/7145C08K2003/265C08K2201/011C08L95/00C08L97/00C08L71/02C08K13/06C08K3/26C08K3/36C08K5/11
Inventor 刘拥军刘永刚郑新国郑爱彬候尚春
Owner GUANGXI WUXUAN JINPAI WATERPROOF MATERIAL SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap