Black-matrix-silver-spot oil-drop Jianzhan and preparation method thereof

A black background, oil drop technology, applied in clay products, other household appliances, applications, etc., can solve the problem of low yield, and achieve the effect of high yield, good decorative effect, and clear process flow

Active Publication Date: 2018-07-10
余秋华
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this regard, even modern means are difficult to handle, and the yield rate is also very low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black-matrix-silver-spot oil-drop Jianzhan and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The invention discloses a black-bottomed silver-spotted oil-drop built-in cup, which includes a green body and a glaze.

[0037] The green body includes the following components in parts by weight: 20 parts of kaolin, 70 parts of red clay, 10 parts of black soil, 6 parts of Jian'ou weathered stone, 1 part of ash and 1 part of glaze slurry;

[0038] The glaze includes the following components in parts by weight: 60 parts of hematite, 4 parts of Shuiji weathered stone, 4 parts of Jianou weathered stone, 12 parts of ash, 6 parts of albite, 2 parts of talc, and 6 parts of calcite , 2 parts of fluorite and 2 parts of Zijin soil;

[0039] The preparation method of the above-mentioned black-bottomed silver-spotted oil drop built-up lamp comprises the following steps:

[0040] (1) The glaze is weighed and mixed according to the formula, and the weight ratio of the material to water is 1:0.8. The glaze and water are put into a ball mill and ground for 7 hours, and then passed t...

Embodiment 2

[0046] Black background and silver spot oil drop Jianzhan, which includes body and glaze.

[0047] The green body includes the following components in parts by weight: 15 parts of kaolin, 68 parts of red clay, 12 parts of black soil, 5 parts of Jian'ou weathered stone, 0.5 part of ash and 0.8 part of glaze slurry;

[0048] The glaze includes the following components in parts by weight: 58 parts of hematite, 5 parts of Shuiji weathered stone, 5 parts of Jianou weathered stone, 7 parts of ash, 6 parts of albite, 2 parts of talc, and 7 parts of calcite , 1.5 parts of fluorite and 2 parts of purple gold soil;

[0049] The preparation method of the above-mentioned black-bottomed silver-spotted oil drop built-up lamp comprises the following steps:

[0050](1) The glaze is weighed and mixed according to the formula, and the weight ratio of the material to water is 1:0.9. The glaze and water are put into a ball mill and ground for 8 hours, and then passed through a 120-mesh sieve to ...

Embodiment 3

[0056] Black background and silver spot oil drop Jianzhan, which includes body and glaze.

[0057] The green body includes the following components in parts by weight: 25 parts of kaolin, 65 parts of red clay, 15 parts of black soil, 3 parts of Jian'ou weathered stone, 1.5 parts of ashes and 0.9 parts of glaze slurry;

[0058] The glaze includes the following components in parts by weight: 62 parts of hematite, 4 parts of Shuiji weathered stone, 4 parts of Jianou weathered stone, 10 parts of ash, 5 parts of albite, 3 parts of talc, and 5 parts of calcite , 3 parts of fluorite and 1 part of Zijin soil;

[0059] The preparation method of the above-mentioned black-bottomed silver-spotted oil drop built-up lamp is characterized in that it comprises the following steps:

[0060] (1) The glaze is weighed and mixed according to the formula, and the weight ratio of the material to water is 1:0.8. The glaze and water are put into a ball mill and ground for 6 hours, and then passed thr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a black-matrix-silver-spot oil-drop Jianzhan and a preparation method thereof. The Jianzhan comprises a blank body and a glaze material; the blank body comprises the followingcomponents in parts by weight: 15-25 parts of kaolin, 65-70 parts of red clay, 10-15 parts of black soil, 3-6 parts of Jianou weathered stone, 0.5-1.5 parts of ash and 0.8-1 part of a glaze slip; theglaze material comprises the following components in parts by weight: 58-62 parts of hematite ore, 4-5 parts of Shuiji weathered stone, 4-5 parts of Jianou weathered stone, 7-12 parts of ash, 5-6 parts of albite, 2-3 parts of talc, 5-7 parts of calcite, 1.5-3 parts of fluorite and 1-2 parts of Zinjin clay. The method provided by the invention adopts original ore and other natural materials to prepare the Jianzhan blank body and the glaze material, the blank body can withstand high-temperature firing and has no deformation and no foaming, and the fired Jianzhan has a black and bright glaze surface, at the same time, silver-gloss crystal spots are irregularly scattered on the glaze surface, the crystal spots like oil droplets and are glittering and translucent carving, and the black-matrix-silver-spot oil drops are formed and have a very good decorative effect and art aesthetic feeling.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to a black-bottomed silver-spotted oil-drop built-in cup and a preparation method thereof. Background technique [0002] Jianzhan is a wonderful art garden and a black porcelain chapter in the history of Chinese ceramics. During the Song and Yuan Dynasties, the black-glazed tea cups produced by Jianyang Jianyao in Fujian Province were famous all over the world for their magnificent glaze color changes, exquisite craftsmanship and excellent artistic level. [0003] The main types of Jianzhan are rabbit hair and oil drop. It is difficult to control the temperature of firing Jianzhan. If the temperature is too high, it will easily cause flow glaze to stick to the bottom; Yield rate of cups. The nature of the base glaze of the Jianzhan determines the difficulty of firing a beautifully patterned rabbit-haired bowl, and the difficulty of building a bowl with oil droplets is higher th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/135C04B33/13C04B33/04C04B33/24C03C8/00C04B41/87
CPCC03C8/00C04B33/04C04B33/13C04B33/135C04B33/24C04B41/009C04B41/5022C04B41/87C04B2235/5427C04B2235/656C04B2235/6567C04B2235/658C04B41/4535Y02P40/60
Inventor 余秋华
Owner 余秋华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com