Method for preparing cutting-resistant mine tire tread rubber

A tire tread, cutting-resistant technology, applied to special tires, tire parts, transportation and packaging, etc., can solve the problems of low tire service life, tire rubber collapse, etc.

Inactive Publication Date: 2018-07-10
中国化工集团曙光橡胶工业研究设计院有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And due to the particularity of the use environment, the road surface is complex, such as uneven potholes, there are many sharp foreign objects such as ore and gravel, and the tires are impacted by uneven force and cut by different degrees of sharp foreign objects during driving, causing the tires to be damaged during use. The rubber material is cut during the process, and the tire rubber is used to collapse and fall off, and the service life of the tire is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for preparing a cut-resistant mine tire tread rubber, the mass ratio of the raw material components of the surface rubber is: 20 parts of natural raw rubber, 50 parts of styrene-butadiene rubber, 30 parts of oil-extended styrene-butadiene rubber, 5 parts of zinc oxide 2 parts of anti-tear resin, 4 parts of coumarone, 8 parts of white carbon black, 55 parts of carbon black, 1.6 parts of sulfur, 1.1 parts of accelerator MBS, 0.15 parts of accelerator CBS. Mix evenly in the rubber machine, and mix in two stages in the internal mixer.

[0020] The mechanical properties of the prepared tire tread compounds are shown in Table 1.

Embodiment 2

[0022] A method for preparing cut-resistant mine tire tread rubber, the mass ratio of the raw material components of the surface rubber is: 20 parts of natural raw rubber, 55 parts of styrene-butadiene rubber, 25 parts of oil-extended styrene-butadiene rubber, 5 parts of zinc oxide 4 parts of anti-tear resin, 4 parts of coumarone, 10 parts of white carbon black, 60 parts of carbon black, 1.8 parts of sulfur, 1.2 parts of accelerator MBS, 0.2 parts of accelerator CBS. Mix evenly in the rubber mixer, and mix in two stages in the internal mixer.

[0023] Table 1 shows the mechanical properties of the prepared tire tread compound with excellent cutting resistance.

Embodiment 3

[0025] A method for preparing a cut-resistant mine tire tread rubber, the mass ratio of the raw material components of the surface rubber is: 20 parts of natural raw rubber, 60 parts of styrene-butadiene rubber, 20 parts of oil-extended styrene-butadiene rubber, 5 parts of zinc oxide 6 parts of tear-resistant resin, 4 parts of coumarone, 12 parts of white carbon black, 65 parts of carbon black, 2.0 parts of sulfur, 1.5 parts of accelerator MBS, 0.25 parts of accelerator CBS. Mix evenly in the rubber mixer, and mix in two stages in the internal mixer.

[0026] Table 1 shows the mechanical properties of the prepared tire tread compound with excellent cutting resistance.

[0027] Table 1: Mechanical Properties of Compounds

[0028] project

[0029] As can be seen from Table 1, the elongation at break of the sizing material obtained by the method of the embodiment is higher, which is beneficial to improving the compatibility of the sizing material and other foreign matt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing cutting-resistant mine tire tread rubber, and is characterized in that the tread rubber comprises the raw material components by mass: 10-20 parts of natural rubber, 50-60 parts of styrene butadiene rubber, 20-40 parts of oil-extended styrene-butadiene rubber, 1-6 parts of a tearing resistant agent, 5-15 parts of white carbon black, 3-5 parts of a protection system, 5-10 parts of an active agent, 50-65 parts of a reinforcing agent, 5-15 parts of a plasticizer, 1.5-2.5 parts of a vulcanizing agent and 0.5-1.5 parts of a promoter; the raw materialsof the tread rubber are mixed with an internal mixer to prepare the product. The rubber material prepared by the method has the characteristics of resistance to cutting and good containment to a roadsurface, and can avoid the problem that chunking and block falling of rubber after cutting in the use process of a tire.

Description

technical field [0001] The invention relates to a compound formula for a mine tire, in particular to a method for preparing a cut-resistant mine tire tread compound. Background technique [0002] The tires of mine trucks are large, and the tires are under a large load. And due to the particularity of the use environment, the road surface is complex, such as uneven potholes, there are many sharp foreign objects such as ore and gravel, and the tires are impacted by uneven force and cut by different degrees of sharp foreign objects during driving, causing the tires to be damaged during use. During the process, the rubber material is cut, and the tire rubber is used to collapse and fall off, resulting in a low service life of the tire. The rubber compound with excellent cutting resistance can make the tire tolerant to uneven road surfaces. The rubber compound has good toughness and is not easy to be cut and damaged to form blocks. [0003] Styrene-butadiene rubber is a polysty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/06C08L7/00C08K13/02C08K3/36C08K3/22C08K5/09C08K3/04C08K3/06B60C1/00
CPCC08L9/06B60C1/0016C08K2003/2296C08L2205/025C08L2205/035C08L7/00C08K13/02C08K3/36C08K3/22C08K5/09C08K3/04C08K3/06
Inventor 黄春耀张居印李艳云
Owner 中国化工集团曙光橡胶工业研究设计院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products