Double-color makeup removal non-woven fabric and manufacturing technology thereof
A non-woven and makeup-removing technology, applied in textiles and papermaking, non-woven fabrics, layered products, etc., can solve the problem that single-layer cotton pads cannot be used in multiple functions, and achieve the effect of being convenient to carry.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0041] Select 1.0dtex×8mm yellow orange viscose fiber, disperse it with water, make it 2% concentration, and then dilute it to 3 / 10,000 concentration, dehydrate and form it through the inclined wire former, and become a fiber web with a dryness of 20% ①, Wet weight is 200g / m 2 . Then fiber mesh ① with a weight of 16g / m 2 The water-repellent PP spunbond fabric is superimposed and sent to the spunlace machine for combination, and 3-10 spunlaces are used for spunlace entanglement at a pressure of 1-10Mpa, so that the orange viscose fiber is embedded in the water-repellent PP spunbond fabric to make Composite non-woven fabric A. Then use 0.5dtex×3mm white viscose fiber, dilute and disperse it into a water mixture with a concentration of 2 / 10,000, dehydrate and form it on another set of inclined wire former, the dryness is 25%, and the wet weight is 150g / m 2 Lay it to the other side of the PP spunbond surface of the composite non-woven fabric A made earlier, and then use 3-8 spu...
Embodiment 2
[0043] Choose 1.7dtex×38mm natural color bamboo viscose fiber, and make it 40g / m 2 Colored fiber mesh ①. Choose 0.8dtex×35mm white viscose fiber, and make it 40g / m 2 White fiber mesh ②. Between the two layers of fiber net ① and ②, the grammage is 20g / m 2 The water-repellent hot-air non-woven fabric is used, and then one side is needle-punched with 3-8 passes, and then the other side is made with a certain strength composite non-woven fabric B after being needle-punched with 3-5 passes. Composite non-woven fabric B is coated with foam, one side of the natural color bamboo viscose fiber layer is coated with 5% natural plant cleansing essential oil, and the white fiber layer is coated with 5% lamb oil diluted and foamed, and the two sides are coated. The final composite non-woven fabric is dried with a dryer, so that the natural plant cleansing essential oil and lamb oil are dried and deposited on the respective fiber surfaces, and the gram weight is 110g / m 2 The makeup remov...
Embodiment 3
[0045] Choose 0.9dtex×38mm white viscose fiber, and make it into 40g / m by sorting machine 2 fiber mesh ②, laid on 15g / m 2 One side of the water-repellent hot-pressed non-woven fabric is entangled with spunlace with a water pressure of 3-8Mpa and the number of passes is 3-8. White viscose fibers are embedded in the water-repellent hot-pressed non-woven fabric to make Composite non-woven fabric A. Then use 2.0dtex×30mm bamboo pulp natural color fiber, open and air-laid to make 35g / m 2 The fiber web ① is sent to the other side of the water-repellent hot-pressed non-woven fabric of the composite non-woven fabric A through the conveying network. The natural color fiber of bamboo pulp is embedded in the water-repellent hot-pressed non-woven fabric to make a three-layer composite non-woven fabric B. The three-layer composite non-woven fabric B is dehydrated again, and the natural color bamboo fiber layer is coated with 5% natural orange essential oil, and the white viscose surface...
PUM
| Property | Measurement | Unit |
|---|---|---|
| length | aaaaa | aaaaa |
| length | aaaaa | aaaaa |