Internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and production method thereof

A waterproofing membrane, compound butyl technology, applied in rubber layered products, chemical instruments and methods, synthetic resin layered products, etc., can solve the problem of poor handling of the details of the waterproof layer, and achieve excellent viscosity-increasing properties. , Improve the composite quality, improve the effect of aging resistance

Active Publication Date: 2018-08-24
解飞
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] An object of the present invention is to provide a kind of internally reinforced composite butyl self-adhesive ethylene-propylene rubber waterproofing membrane, which is used to solve the existing EPDM waterproofing membrane. The problem that the coiled material can not handle the detailed nodes of the waterproof layer, especially the treatment and maintenance of the joints of tile roofs and metal roofs; Coil production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and production method thereof
  • Internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and production method thereof
  • Internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] refer to figure 1 , this internally reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof membrane is composed of a surface layer 1, a reinforcement layer 2, a base layer 3, a self-adhesive layer 4, and an anti-adhesive layer 5. The base layer 3 is compounded on both sides of the reinforcement layer 2 to form the base layer, the surface layer 1 and the base layer 3 are both ethylene-propylene rubber layers, the reinforcement layer 2 is metal punched mesh or fiber mesh cloth, and the self-adhesive layer 4 is butyl self-adhesive rubber layer or butyl hot melt adhesive, the anti-adhesive layer 5 is a PE isolation film; the metal punching screen is 2×4mm metal punching screen.

[0053] The components of surface layer 1 and base layer 3 are: 100 parts of binary ethylene propylene rubber; 80 parts of reinforcing agent; 40 parts of filler; 25 parts of plasticizer; 1.5 parts of active agent; 6 parts of tackifier 0.8 parts of accelerator; 1 part of vulca...

Embodiment 2

[0082] refer to figure 2 , this internally reinforced composite butyl self-adhesive ethylene propylene rubber waterproof membrane is composed of surface layer 1, reinforcement layer 2, self-adhesive layer 4, and anti-adhesive layer 5. The surface layer 1 is compounded on the reinforcement layer 2 constitutes the base layer, the surface layer 1 is an ethylene-propylene rubber layer, the reinforcement layer 2 is a metal punched mesh or fiber mesh cloth, and the self-adhesive layer 4 is a butyl self-adhesive rubber layer or butyl hot-melt adhesive, anti-adhesive Layer 5 is a PE isolation film; the metal punched and expanded mesh is 3×6mm metal punched and expanded mesh.

[0083] The components of surface layer 1 in parts by mass are: 100 parts of binary ethylene propylene rubber; 95 parts of reinforcing agent; 15 parts of filler; 20 parts of plasticizer; 1.7 parts of active agent; 8 parts of tackifier; 0.6 parts of curing agent; 1.2 parts of vulcanizing agent; 1.1 parts of anti...

Embodiment 3

[0112] This internally reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof membrane is composed of surface layer 1, reinforcement layer 2, base layer 3, self-adhesive layer 4, and anti-adhesive layer 5. The surface layer 1, base layer 3 is compounded on both sides of the reinforcement layer 2 to form the base layer, the surface layer 1 and the base layer 3 are both ethylene-propylene rubber layers, the reinforcement layer 2 is metal punched mesh or fiber mesh cloth, and the self-adhesive layer 4 is a butyl self-adhesive rubber layer Or butyl hot-melt adhesive, the anti-adhesive layer 5 is a PE isolation film; the metal punching screen is 3×6mm metal punching screen.

[0113] The components of surface layer 1 and base layer 3 are: 100 parts of EPDM rubber; 100 parts of reinforcing agent; 25 parts of filler; 26 parts of plasticizer; 1.8 parts of active agent; 7 parts of tackifier parts; accelerator 0.6 parts; vulcanizing agent 1.2 parts; anti-aging agen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and a production method thereof. The internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material is formed by sequentially and mutually overlapping and compounding a basic layer, a self-adhesive layer and a sticking prevention layer; the basic layer is prepared by compounding a surface layer and a foundation layer on two sides of a reinforcement layer or compounding the surface layer above the reinforcement layer; thesurface layer and the foundation layer are both ethylene-propylene rubber layers; the reinforcement layer is an expanded metal net or fiber grid cloth; the self-adhesive layer is a butyl self-adhesiverubber layer or a butyl hot melt adhesive; the sticking prevention layer is a PE isolating membrane. According to the internally-reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material disclosed by the invention, node parts of thin parts are permanently sealed to a maximum extent, so that a waterproofing effect of an overall waterproof layer is greatly improved and the durability life of the overall waterproof layer is greatly prolonged, and the problem that the node parts of the thin parts of the waterproof layer cannot be handled well by adopting an existing ethylene-propylene-diene monomer rubber waterproof coiled material is solved.

Description

1. Technical field [0001] The invention relates to the field of building waterproof materials, in particular to an internally reinforced composite butyl self-adhesive ethylene-propylene rubber waterproof coiled material and a production method thereof. 2. Background technology [0002] At present, the single-layer waterproof material used on building roofs should have the best comprehensive performance in the relatively mature and internationally recognized EPDM waterproof membrane, but the non-polar structure of EPDM also leads to its Self-adhesive and mutual adhesion are poor. During the construction of the coiled material, for the joints such as the yin and yang corners, due to the influence of construction and its own factors such as the plasticity of the coiled material and the cohesive force of the material, the coiled material is not easy to fix and stick to these parts, especially It is used in some areas with large temperature differences and roof materials with lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L33/02C08K5/14B29C69/02B29C35/02B29C47/92B29C43/58E04D5/10B32B25/16B32B25/18B32B7/12B32B25/10B32B25/04B32B25/08B32B27/32B32B27/06B32B15/02B32B15/06B32B3/12B32B33/00B29C48/92
CPCB29C35/02B29C43/58B29C2043/5816B32B3/12B32B7/12B32B15/02B32B15/06B32B25/04B32B25/08B32B25/10B32B25/16B32B25/18B32B27/06B32B27/32B32B33/00B32B2307/54B32B2307/73B32B2419/00B29C48/0011B29C48/08B29C48/92B29C2948/92704B29C2948/92876B29C2948/92885B29C2948/92904C08L23/16E04D5/10C08L33/02C08K5/14
Inventor 解飞解忠深解忠财
Owner 解飞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com