No-drape and volatilization-resistance hot-dip galvanization aluminum Ca-Al-Cr zinc aluminum alloy

A ca-al-cr, hot-dip galvanizing technology, applied in the field of alloys, can solve problems such as inability to improve product quality, poor control of aluminum concentration, particles on the surface of the coating, and achieve good comprehensive protection performance, excellent resistance to volatilization and corrosion. Oxidation resistance, low cost effect

Inactive Publication Date: 2018-08-24
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But so far, the aluminum concentration in hot-dip galvanized aluminum alloy is not well controlled, not only can not improve product quality, but will cause particles on the surface of the coating, and even defects such as missing plating, especially in batch hot-dip production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A Ca-Al-Cr zinc-aluminum alloy that uses non-wrinkle, anti-volatile, hot-dip galvanized aluminum at 320-340 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca:0.2wt.%, Na:0.1wt.%, Sc:0.2wt.%, Ni:1.2wt.%, Al:30.0wt.%, Cr:0.4wt .%, the balance is zinc. Alloy preparation method: Add the above-mentioned raw materials into an induction furnace protected by argon gas, and use a silicon carbide crucible; add the above-mentioned raw materials into an atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating Form the alloy solution at 500-600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 500-600 degrees for 10 minutes, then cast it into the same level equipment as the hot top for semi-continuous casting into the required For round ingots, the ingot moving speed is 5-8m / min. The cast ingot can be used as hot-dip galvanizing raw material for t...

Embodiment 2

[0021] A Ca-Al-Cr zinc-aluminum alloy that uses non-wrinkle, anti-volatile, hot-dip galvanized aluminum at 320-340 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 0.4wt.%, Na: 0.2wt.%, Sc: 0.3wt.%, Ni: 1.6wt.%, Al: 36.0wt.%, Cr: 0.8wt .%, the balance is zinc. Alloy preparation method: Add the above-mentioned raw materials into an induction furnace protected by argon gas, and use a silicon carbide crucible; add the above-mentioned raw materials into an atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating Form the alloy solution at 500-600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 500-600 degrees for 10 minutes, then cast it into the same level equipment as the hot top for semi-continuous casting into the required For round ingots, the ingot moving speed is 5-8m / min. The cast ingot can be used as hot-dip galvanizing raw material...

Embodiment 3

[0024] A Ca-Al-Cr zinc-aluminum alloy that uses non-wrinkle, anti-volatile, hot-dip galvanized aluminum at 320-340 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca:0.3wt.%, Na:0.2wt.%, Sc:0.2wt.%, Ni:1.5wt.%, Al:34.0wt.%, Cr:0.6wt .%, the balance is zinc. Alloy preparation method: Add the above-mentioned raw materials into an induction furnace protected by argon gas, and use a silicon carbide crucible; add the above-mentioned raw materials into an atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heating Form the alloy solution at 500-600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 500-600 degrees for 10 minutes, then cast it into the same level equipment as the hot top for semi-continuous casting into the required For round ingots, the ingot moving speed is 5-8m / min. The cast ingot can be used as hot-dip galvanizing raw material for t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a no-drape and volatilization-resistance hot-dip galvanization aluminum Ca-Al-Cr zinc aluminum alloy and a machining process thereof. The alloy comprises the following components in percentage by weight: 0.2-0.4 wt.% of Ca, 0.1-0.2 wt.% of Na, 0.2-0.3 wt.% of Sc, 1.2-1.6 wt.% of Ni, 30.0-36.0 wt.% of Al, 0.4-0.8 wt.% of Cr, and the balance of zinc. The material can be usedfor hot-dip galvanization of steel plates at 320-340 DEG C, and achieves better corrosion resistance compared with traditional pure zinc hot dipping. The material can be applied to hot-dip galvanization protection of steel for an ocean platform, and can be widely applied to more hot-dip galvanization along with widening of more engineering application fields.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a zinc alloy. Background technique [0002] The potential of zinc is negative than that of iron. When electrochemical corrosion occurs, zinc can be used as a sacrificial anode for cathodic protection of steel. Hot-dip galvanizing can significantly improve the atmospheric corrosion resistance of steel, and the galvanized layer can provide physical barrier protection for steel and isolate steel from corrosive media. The hot-dip galvanizing process is simple, and the steel is immersed in a molten zinc or zinc alloy bath continuously or in batches to obtain a hot-dip galvanized layer. Hot-dip galvanizing has the following characteristics: (1) Thick coating can be obtained, and the corrosion resistance is good. (2) The coating has good adhesion, and can be properly processed after plating, such as forming, welding and painting. [0003] In recent years, people have tried to apply ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C18/04C22C1/02C23C2/06
CPCC22C18/04C22C1/02C23C2/06
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD