A kind of manufacturing method of silicon-containing aluminum alloy welding wire for aerospace

A silicon-aluminum alloy, manufacturing method technology, applied in manufacturing tools, welding/cutting media/materials, welding equipment, etc., can solve the problems of poor internal structure, easy occurrence of pores, slag inclusion and cracks, etc., and achieve uniform structure and structure. Uniform and fine, the effect of eliminating intragranular segregation

Active Publication Date: 2019-10-11
NORTHEAST LIGHT ALLOY CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem that the existing silicon-aluminum alloy welding wire has a poor internal structure, which leads to easy occurrence of pores, slag inclusions and cracks during welding, and provides a method for manufacturing an aerospace-use silicon-containing aluminum alloy welding wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of silicon-containing aluminum alloy welding wire for aerospace

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0016] Specific implementation mode 1: This implementation mode is a manufacturing method of silicon-containing aluminum alloy welding wire for aerospace, which is specifically completed according to the following steps:

[0017] 1. Melting: According to the mass fraction of Si in the silicon-containing aluminum alloy welding wire is 3.0%-4.0%, the mass fraction of Cu is 1.5%-2.8%, the mass fraction of Cr is 0.001%-0.08%, and the mass fraction of V is 0.05%~0.20%, the mass fraction of Be is 0.0001%~0.0015%, the mass fraction of Ti is 0.08%~0.18%, the mass fraction of Zr is 0.08%~0.28%, the mass fraction of impurities is ≤0.1%, and the balance is Al weighs low magnesium aluminum alloy ingots, copper ingots, silicon aluminum alloys, chromium aluminum alloys, vanadium aluminum alloys, zirconium aluminum alloys, beryllium aluminum alloys and titanium aluminum alloys, and low magnesium aluminum alloy ingots, copper ingots, silicon aluminum alloys, Chromium-aluminum alloy, vanadium-...

specific Embodiment approach 2

[0027] Specific embodiment two: the difference between this embodiment and specific embodiment one is: in step one, the mass fraction of Si in the silicon-containing aluminum alloy welding wire is 3.5%, the mass fraction of Cu is 2.05%, and the mass fraction of Cr is 0.02%, the mass fraction of V is 0.10%, the mass fraction of Be is 0.0006%, the mass fraction of Ti is 0.11%, the mass fraction of Zr is 0.13%, and the balance is Al. Weigh low-magnesium aluminum alloy ingots, copper ingots, Silicon-aluminum alloys, chrome-aluminum alloys, vanadium-aluminum alloys, zirconium-aluminum alloys, beryllium-aluminum alloys, and titanium-aluminum alloys. Others are the same as the first embodiment.

specific Embodiment approach 3

[0028] Embodiment 3: This embodiment differs from Embodiment 1 or Embodiment 2 in that: in step 1, melt at a temperature of 740° C. for 5.5 hours to obtain a silicon-containing aluminum alloy melt. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method for a silicon-contained aluminum alloy welding wire rod for spaceflight, and relates to a manufacturing method for a welding wire rod. The manufacturingmethod aims to solve the problem that gas holes, slag inclusion and cracks easily occur in the welding process due to the fact that an existing silicon-aluminum alloy welding wire is poor in internalstructure. The manufacturing method comprises the steps of 1, carrying out smelting,2, carrying out casting, 3, carrying out saw cutting, 4, carrying out turning on an oxidation skin, 5, carrying outpreheating; 6, carrying out extruding; 7, carrying out annealing; 8, carrying out primary stretching; 9, carrying out intermediate annealing; and 10, carrying out second stretching so as to obtain thesilicon-contained aluminum alloy welding wire rod for spaceflight. The silicon-contained aluminum alloy welding wire rod manufacture through the manufacturing method has the advantages of being uniform in structure and free of coarse grains. The manufacturing method is mainly used for preparing the silicon-contained aluminum alloy welding wire rod for spaceflight.

Description

technical field [0001] The invention relates to a method for manufacturing welding wire. Background technique [0002] Aluminum alloy has the characteristics of high specific strength, good manufacturing process and low cost, and is the preferred structural material for aerospace products. Carrier rocket storage tanks, satellite storage tanks, tactical missile shells, etc. are welded with aluminum alloy. Aluminum alloy welding wire is a necessary filler material for aluminum alloy welding, and it is one of the factors that determine the quality of welds, and plays an important role in the welding production of aerospace aluminum alloys. The silicon-aluminum alloy welding wire belongs to a type of aluminum alloy welding wire and is widely used in the aerospace field. However, the existing silicon-aluminum alloy welding wire has a poor internal structure, which leads to problems such as pores, slag inclusions and cracks during welding. . Contents of the invention [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C1/03B23K35/28C22F1/043
Inventor 高宝亭高新宇王海彬殷云霞贾宁杨晓禹刘世雷郑天航付金来姜鹏
Owner NORTHEAST LIGHT ALLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com