Preparation method of high-strength medium-manganese steel plate

A manganese steel plate, high-strength technology, applied in the field of preparation of high-strength medium-manganese steel plate, can solve the problems of stamping and forming of automobile plates, surface wrinkles of steel parts, no macro work hardening, etc.

Active Publication Date: 2018-09-18
江苏育材堂车身技术有限公司
View PDF5 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large number of literature studies have shown that after reverse phase transformation annealing of severely cold-rolled medium-manganese steel, equiaxed ferrite and austenite structures are formed, and Lüders band deformation is easy to occur during the deformation process, without macroscopic work hardening, and Causes surface wrinkles of steel parts, which cannot meet the requirements of stamping and forming of automobile sheets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-strength medium-manganese steel plate
  • Preparation method of high-strength medium-manganese steel plate
  • Preparation method of high-strength medium-manganese steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] (1) Smelting and forging: 1# steel is smelted in a vacuum induction furnace, and its composition is shown in Table 1. The obtained molten steel is cast and forged to obtain a billet of 60mm×60mm×300mm.

[0065] (2) Hot rolling: heat the cast slab to 1150°C for 3 hours, start rolling at 1000°C, go through 7 passes of hot rolling, and finish at 800°C, with a total cumulative reduction of 96%, single pass The reduction ratio was 30%. Air-cool to room temperature after hot-rolling, and the thickness of the hot-rolled sheet is 2.5mm. Such as figure 1 As shown, the hot-rolled microstructure is dominated by lath martensite.

[0066] (3) Primary annealing: put the hot-rolled sheet into a box furnace at 620°C for 10 hours to simulate bell annealing, and air-cool to room temperature. figure 2 It is the SEM image of 1# steel annealed at 620°C for 10h and the surface scan image of the corresponding Mn element; the structure is lath ferrite and austenite, and there is cementite ...

Embodiment 2

[0073] (1) Smelting and forging: 2# steel was smelted in a vacuum induction furnace. The composition is shown in Table 1. The obtained molten steel was cast and forged to obtain a billet of 60mm×60mm×300mm.

[0074] (2) Hot rolling: heat the cast slab to 1200°C for 2 hours, start rolling at 1050°C, after 6 passes of hot rolling, finish rolling at 820°C, the total cumulative reduction is 96%, single pass The reduction ratio was 30%. Air cooling to 600°C after hot rolling, then furnace cooling, simulated coiling, the thickness of the hot rolled sheet is 2.4mm.

[0075] (3) Primary annealing: put the hot-rolled sheet into a box furnace at 650°C for 24 hours to simulate bell annealing, and air-cool to room temperature.

[0076] (4) Cold rolling: the above-mentioned annealed steel plate is cold-rolled, and the total cold-rolling reduction is 0% (no cold-rolling), 10%, and 15% respectively to obtain a cold-rolled plate. The cold-rolling reduction of the comparison process The amou...

Embodiment 3

[0082] (1) Smelting and forging: 3# steel was smelted in a vacuum induction furnace. The composition is shown in Table 1. The obtained molten steel was cast and forged to obtain a billet of 60mm×60mm×300mm.

[0083] (2) Hot rolling: heat the cast slab to 1250°C for 4 hours, start rolling at 1050°C, after 7 passes of hot rolling, finish at 780°C, total cumulative reduction is 95%, single pass The reduction ratio was 30%. Air-cool to room temperature after hot-rolling, and the thickness of the hot-rolled sheet is 3.1mm.

[0084] (3) Primary annealing: put the hot-rolled sheet into a box furnace at 600°C for 36 hours, simulate bell annealing, and air-cool to room temperature.

[0085](4) Cold rolling: the above-mentioned annealed steel plate is cold-rolled, and the total cold-rolling reduction is respectively 0% (no cold-rolling), 10%, and 18%, to obtain a cold-rolled plate, and the cold-rolling reduction of the comparison process The amounts are 40% and 50%.

[0086] (5) Seco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a high-strength medium-manganese steel plate, and belongs to the technical field of steel plates with high strength and toughness. The preparation method comprises the following steps that 1), smelting is carried out according the proportion of the components in the high-strength medium-manganese steel plate, and continuous casting or die casting iscarried out, then forging is carried out to obtain a blank; 2), heating and heat preservation are carried out on the blank, and the blank is air-cooled to the room temperature after subjected to multi-pass hot rolling so as to obtain a hot-rolled plate or a hot-rolled coiled plate; 3), the hot-rolled plate or the hot-rolled coiled plate is heated, undergoes heat preservation and then is cooled toobtain a primary annealing steel plate, and the primary annealing steel plate undergoes a step 4) or directly undergoes a step 5); 4), the primary annealing steel plate is cold-rolled to obtain a cold-rolled plate; and 5), the cold-rolled plate or the primary annealing steel plate is heated, undergoes heat preservation and is cooled to the room temperature to obtain the high-strength medium-manganese steel plate, wherein the yield strength of the high-strength medium-manganese steel plate is 450-1000 MPa, the tensile strength of the high-strength medium-manganese steel plate is 800-1500 MPa, the elongation percentage of the high-strength medium-manganese steel plate is 18%-60%, no Luders bands are generated during the uniaxial tension process, and the yield elongation rate of the high-strength medium-manganese steel plate is less than or equal to 1%. The preparation method has the advantage that high strength and elongation of the steel plate can be guaranteed, the steel plate can be yielded continuously in the deformation process, and the Luders bands and deformation can be prevented from being generated so as to facilitate cold stamping forming of the steel plates.

Description

technical field [0001] The invention belongs to the technical field of high-strength and tough steel plates, and in particular provides a preparation method of high-strength medium-manganese steel plates. Background technique [0002] High strength and toughness have always been the goal of the development of steel materials. The use of high-strength and toughness materials can improve the safety of parts, and can reduce the amount of materials used on the premise of ensuring safety, and realize the weight reduction of parts. All automobile manufacturers are working hard Realize vehicle weight reduction. With the rapid development of my country's automobile industry, the problems of energy consumption and environmental pollution have become increasingly prominent. Although the application of new energy in automobiles has slowed down the problem of environmental pollution, it has put forward higher requirements for the lightweight of automobiles. Iron and steel materials are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D8/02C22C38/58C22C38/38C22C38/04C22C38/34C22C38/02C22C38/06C22C38/12C22C38/14C22C38/16C22C38/08C22C38/32C22C38/54C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50
CPCC21D8/0226C21D8/0236C21D8/0263C21D8/0273C21D2211/001C21D2211/005C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/32C22C38/34C22C38/38C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C22C38/54C22C38/58
Inventor 易红亮杨达朋杜鹏举吴迪
Owner 江苏育材堂车身技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products