A seed coating agent for reducing arsenic absorption by crops and its preparation method
A crop and iron oxide technology is applied in the field of seed coating agent for reducing the absorption of arsenic by crops and the preparation of seed coating agent for reducing the absorption of arsenic by crops. Difficulty of application
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0077] Embodiment 1: the preparation of seed coating agent of the present invention
[0078] The implementation steps of this embodiment are as follows:
[0079] A. Preparation of iron oxide-CaCl 2 suspension
[0080] in grams of FeCl 3 ·6H 2 The ratio of O to distilled water in milliliters is 50:500, FeCl 3 ·6H 2 O dissolved in distilled water followed by FeCl in grams 3 ·6H 2 The ratio of O to the calcium hydroxide aqueous solution in milliliters is 54:330, add 1.0 moles of calcium hydroxide aqueous solution, mix well, and obtain the pH value of the solution using a concentration of 0.5N sulfuric acid or sodium hydroxide aqueous solution to adjust to 7.5, stir, Stand still to get iron oxide-CaCl 2 suspension. The method described in this manual is used to analyze and determine that the iron oxide is ferrihydrite;
[0081] B, preparation Trichoderma aculeatus chlamydospore powder
[0082] I. Preparation of arsenic-containing solid medium
[0083] 100 parts by weight...
Embodiment 2
[0090] Embodiment 2: the preparation of seed coating agent of the present invention
[0091] The implementation steps of this embodiment are as follows:
[0092] A. Preparation of iron oxide-CaCl 2 suspension
[0093] in grams of FeCl 3 ·6H 2 The ratio of O to distilled water in milliliters is 58:500, FeCl 3 ·6H 2 O dissolved in distilled water followed by FeCl in grams 3 ·6H 2 The ratio of O to the calcium hydroxide aqueous solution in milliliters is 50:330, add 0.8 moles of calcium hydroxide aqueous solution, mix uniformly, obtain the pH value of the solution and use the concentration of 1.0N sulfuric acid or sodium hydroxide aqueous solution to adjust to 7.0, stir, Stand still to get iron oxide-CaCl 2 suspension. The method described in this manual is used to analyze and determine that the iron oxide is ferrihydrite;
[0094] B, preparation Trichoderma aculeatus chlamydospore powder
[0095] I. Preparation of arsenic-containing solid medium
[0096] 95 parts by ...
Embodiment 3
[0103] Embodiment 3: the preparation of seed coating agent of the present invention
[0104] The implementation steps of this embodiment are as follows:
[0105] A. Preparation of iron oxide-CaCl 2 suspension
[0106] in grams of FeCl 3 ·6H 2 The ratio of O to distilled water in milliliters is 54:500, FeCl 3 ·6H 2 O dissolved in distilled water followed by FeCl in grams 3 ·6H 2 The ratio of O to the calcium hydroxide aqueous solution in milliliters is 58:330, add 1.2 moles of calcium hydroxide aqueous solution, mix uniformly, obtain the pH value of the solution and adjust to 8.0 with sulfuric acid or sodium hydroxide aqueous solution with a concentration of 2.0N, stir, Stand still to get iron oxide-CaCl 2 suspension. The method described in this manual is used to analyze and determine that the iron oxide is ferrihydrite;
[0107] B, preparation Trichoderma aculeatus chlamydospore powder
[0108] I. Preparation of arsenic-containing solid medium
[0109] 105 parts b...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap