High-wear-resistance composite board

A composite sheet, high wear-resistant technology, applied in the field of polymer composite materials, can solve the problems of poor wear resistance and short service life, and achieve the effect of improving structural strength

Inactive Publication Date: 2018-09-28
泰州市启航石油分析仪器有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] PVC composite board has the characteristics of corrosion resistance and light weight, but it has poor wear resistance and short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention will be further described below in conjunction with embodiment.

[0013] High wear-resistant composite plate, including polyvinyl chloride, stabilizer, processing modifier, plasticizer, lubricant, SiC nano powder, reinforcing agent, in this embodiment, the reinforcing agent is nano-scale CaCO 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-wear-resistance composite board. The high-wear-resistance composite board comprises polyvinyl chloride, stabilizers, processing modifiers, plasticizers, lubricants, SiCnanopowder and enhancers. The enhancers refer to nano-scale CaCO3. The high-wear-resistance composite board has the advantages of wear resistance and high structural strength.

Description

technical field [0001] The invention relates to a polymer composite material, in particular to a PVC composite plate. Background technique [0002] PVC composite board has the characteristics of corrosion resistance and light weight, but it has poor wear resistance and short service life. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention proposes a high wear-resistant composite plate that can significantly improve wear resistance. [0004] The present invention achieves technical goals through the following technical solutions. [0005] The high wear-resistant composite plate includes polyvinyl chloride, a stabilizer, a processing modifier, a plasticizer, and a lubricant; it is characterized in that it also includes SiC nano powder. [0006] A further improvement lies in: further comprising a reinforcing agent. [0007] A further improvement is: the reinforcing agent is nanoscale CaCO 3 . [0008] Compared with the prior art...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K3/34C08K3/26
CPCC08K3/34C08K3/26C08K2003/265C08K2201/011C08L27/06
Inventor 张冬平
Owner 泰州市启航石油分析仪器有限公司