Natural inorganic anti-aging additive as well as preparation method and application thereof

An anti-aging and additive technology, applied in coatings and other directions, can solve problems such as low survival rate, difficult governance, low efficiency, etc., and achieve the effect of simple production process, small equipment investment and low cost

Active Publication Date: 2018-10-09
IDEAL NEW MATERIAL TECH HONGKONG LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, desert control depends on planting plants, which has low survival rate, high cost and low efficiency
At present, although some exciting scientific research results have been achieved in desert control, desert control is still a worldwide problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Natural inorganic anti-aging additive as well as preparation method and application thereof
  • Natural inorganic anti-aging additive as well as preparation method and application thereof
  • Natural inorganic anti-aging additive as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A natural inorganic anti-aging additive, comprising the following raw materials in parts by weight:

[0029] 84 parts of sandy soil, 10 parts of nano-zinc oxide (50nm), 4.9 parts of nano-titanium dioxide (anatase nano-scale titanium dioxide 35nm), 0.1 part of nano-silver and 1 part of nano-airgel (silicon airgel);

[0030] Wherein, in addition to the above-mentioned raw materials, it is not ruled out to add some other functional raw materials in order to obtain a certain function.

[0031] The preparation method of the natural inorganic anti-aging additive, the preparation method is specifically:

[0032] (1) Crush: Crush the desert sand into 3000 meshes;

[0033] (2) Stirring: Pour the desert sand, nano-zinc oxide, nano-titanium dioxide, nano-silver oxide, and nano-airgel into a stirring tank in proportion, and stir for 30 minutes;

[0034] (3) Baking: put the material stirred in step (2) into a baking oven and bake at 750° C. for 30 minutes to prepare the natural in...

Embodiment 2

[0037] A natural inorganic anti-aging additive, comprising the following raw materials in parts by weight:

[0038] 75 parts of desert soil, 15 parts of nano-zinc oxide (20nm), 8 parts of nano-titanium dioxide (rutile nano-scale titanium dioxide 15nm), 0.3 parts of nano-silver and 1.7 parts of nano-airgel (organic aerogel);

[0039] Wherein, in addition to the above-mentioned raw materials, it is not ruled out to add some other functional raw materials in order to obtain a certain function.

[0040] The preparation method of the natural inorganic anti-aging additive, the preparation method is specifically:

[0041] (1) Crush: Crush the desert sand into 2500 meshes;

[0042] (2) Stirring: Pour the desert sand, nano-zinc oxide, nano-titanium dioxide, nano-silver oxide, and nano-airgel into a stirring tank in proportion, and stir for 25 minutes;

[0043] (3) Baking: put the material stirred in step (2) into a baking oven and bake at 700° C. for 40 minutes to prepare the natural...

Embodiment 3

[0045] A natural inorganic anti-aging additive, comprising the following raw materials in parts by weight:

[0046] 90 parts of saline-alkali soil, 5 parts of nano-zinc oxide (100nm), 3 parts of nano-titanium dioxide (1 part of rutile nano-sized titanium dioxide 50nm, 2 parts of anatase nano-sized titanium dioxide 50nm), 0.05 part of nano-silver and nano-airgel (carbon airgel) 1.95 parts;

[0047] Wherein, in addition to the above-mentioned raw materials, it is not ruled out to add some other functional raw materials in order to obtain a certain function.

[0048] The preparation method of the natural inorganic anti-aging additive, the preparation method is specifically:

[0049] (1) Crush: Crush the desert sand into 3500 meshes;

[0050] (2) Stirring: Pour the desert sand, nano-zinc oxide, nano-titanium dioxide, nano-silver oxide, and nano-airgel into a stirring tank in proportion, and stir for 35 minutes;

[0051] (3) Baking: put the material stirred in step (2) into a ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of novel materials, and particularly relates to a natural inorganic anti-aging additive as well as a preparation method and application thereof. Desert sand, nanometer zinc oxide, nanometer titanium dioxide, nanometer silver and nanometer aerogel are mixed and baked to prepare the anti-aging additive. The preparation method is simple and feasible and issuitable for industrial production. In addition, the preparation method breaks through the traditional idea of governing the desert by various methods; the desert sand in various environments is crushed and is used as raw materials to be directly used; a great amount of desert sand can be consumed; meanwhile, the inherent natural harmony of the ecological environment is protected.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a natural inorganic anti-aging additive and its preparation method and application. Background technique [0002] The desert is one of the most tenacious natural enemies of human beings. With the wind blowing, the desert sand will desertify the existing land. Land desertification will not only drastically reduce the land that we can effectively use, but also lead to land degradation, soil structure damage, and soil nutrient loss. At the same time, it will cause blockage of rivers, reservoirs, and canals, causing damage to railway roadbeds, bridges, and culverts. Desertification will also cause sand and dust weather, which will affect the normal take-off and landing of aircraft, damage communications, transmission lines, and facilities. The resulting disaster threat Residents are safe. According to monitoring, my country's urban air pollutants are mainly tiny pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K13/04C08K3/36C08K3/34C08K3/22C08K3/08C08K7/26C08K7/22C08K7/24C09D7/61
CPCC09D7/70C08K3/08C08K3/22C08K3/346C08K3/36C08K7/22C08K7/24C08K7/26C08K13/04C09D7/61C08K2201/003C08K2201/011C08K2003/2296C08K2003/0806C08K2003/2241C09D7/67
Inventor 何新桥
Owner IDEAL NEW MATERIAL TECH HONGKONG LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More