Large-gauge magnesium alloy long and flat ingot semicontinuous casting device

A magnesium alloy, large-scale technology, applied in the field of magnesium alloy casting, can solve problems such as hot cracking and cold cracking, and achieve the effects of reducing temperature gradient, reducing cracking tendency, and improving heat soaking effect.

Active Publication Date: 2018-10-12
NORTHEASTERN UNIV
View PDF14 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition to the above-mentioned problems, large-scale ingots, especially for magnesium alloy ingots with a rectangular cross-section (including flat ingots or square ingots) with a symmetrical structure, due to the cooling rate and cooling sequence in the circumferential and width directions during the casting process Casting stress and strain caused by different factors often lead to hot cracking during solidification or cold cracking after solidification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large-gauge magnesium alloy long and flat ingot semicontinuous casting device
  • Large-gauge magnesium alloy long and flat ingot semicontinuous casting device
  • Large-gauge magnesium alloy long and flat ingot semicontinuous casting device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The structure of the semi-continuous casting device for long slabs of large-size magnesium alloys is as follows: figure 1 As shown, it includes a diverter plate, a crystallizer and a dummy head 6; the crystallizer includes a mold inner sleeve 26, an electromagnetic coil 5, a cold water tank 31 and an oil cover plate 24, and a gas protection nozzle 3 is arranged above the oil cover plate 24 , the crystallizer inner sleeve 26 is provided outside, the electromagnetic coil 5 is located between a cold water tank 31 and the crystallizer inner sleeve 26; the top of the crystallizer inner sleeve 26 is a shunt plate, and the lower part of the crystallizer inner sleeve 26 is a dummy head 6;

[0050] The diverter plate is a single diverter plate 1, such as figure 2 As shown, a height adjustment device is arranged above the diverter plate, and the height adjustment device is composed of a height adjustment screw fixing base 14, a height adjustment screw 13 and a diverter plate sup...

Embodiment 2

[0065] Device structure is the same as embodiment 1, and difference is:

[0066] The diverter plate is split type diverter plate 2, the structure is as follows image 3 As shown, the split type diverter plate 2 is fixedly connected together by two square grooves 10 through a fixed support base plate 11, and the tops of each square groove 10 are fixedly connected together by connecting rods. The part of the corner is provided with a rectangular shunt opening 8, and a circular shunt hole 7 is arranged on the side wall of the square groove 10; several small holes are arranged on the side wall adjacent to one square groove and the other square groove;

[0067] The method is the same as in Example 1; the obtained magnesium alloy large-size ingot product has no cracks.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a large-gauge magnesium alloy long and flat ingot semicontinuous casting device. The large-gauge magnesium alloy long and flat ingot semicontinuous casting device comprises a distribution disk, a crystallizer and a dummy bar head. A height adjustment device is arranged above the distribution disk. The distribution disk is a monomer type distribution disk or a split type distribution disk. The monomer type distribution disk is of an integral structure formed by a rectangular side wall and a trapezoid bottom groove. One rectangular distribution port is arranged in each corner of the side wall. The split type distribution disk is formed by a plurality of rectangular grooves through a fixing supporting base plate in a fixedly connected manner, and is provided with rectangular distribution ports in the corners. A third cold water tank is arranged below a first cold water tank. The interior of a square groove above the dummy bar head is of a stepped two-layer groove type structure. A cavity is formed inside a base of the dummy bar head. The large-gauge magnesium alloy long and flat ingot semicontinuous casting device can be used for producing and preparing magnesium alloy flat ingots of various dimensions and specifications and with stable quality, and the tearing tendency of the ingots is effectively reduced.

Description

technical field [0001] The invention belongs to the technical field of magnesium alloy casting, and in particular relates to a semi-continuous casting device for a long flat ingot of a large-scale magnesium alloy. Background technique [0002] The semi-continuous casting process, also known as direct chilling, is a process in which the molten metal is continuously and stably solidified into an ingot through a crystallizer. The crystallizer is mainly composed of the inner cooling water tank spray hole and so on. The melt is in contact with the inner wall of the crystallizer to achieve primary cooling, and after exiting the crystallizer, the secondary cooling water is sprayed to the surface of the ingot at a certain angle through the water spray hole to achieve chilling. With the continuous improvement of industrial performance requirements for large-scale deformed structural materials, it is particularly important to produce large-scale high-quality cast slabs as high-perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/14B22D11/08B22D11/103B22D11/124
CPCB22D11/083B22D11/103B22D11/124B22D11/14
Inventor 乐启炽侯建廖启宇贾永辉宝磊王彤
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com